Metal oxide semiconductor device with localized laterally doped channel
Assignee: Advanced Micro Devices Inc
•
Filing: 1998-11-24
•
Granted: 2001-01-30
•
Expires: 2018-11-24
Abstract
Abstract Channel doping is implemented such that dopants remain localized under the gate without migrating under the source/drain juctions during processing, thereby avoiding performance degradation of the finished device. Embodiments include implanting impurities at an acute angle to form a lateral channel implant localized below the gate after activation of source/drain regions, and activating the lateral channel implant by a low-temperature RTA during subsequent metal silicide formation. The use of a low-temperature RTA for electrical activation of the lateral channel implant avoids impurity migration under the source/drain junctions, thereby lowering parasitic junction capacitance and enabling the manufacture of semiconductor devices exhibiting higher circuit speeds with improved threshold voltage control.
Inventors
- 👤 Zoran Krivokapic
- 👤 Ognjen Milic
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 13:51
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0223; H10D30/0227; H10D30/0212; H10D62/00; H10D62/10; H10D62/17; H10D62/213; H10D62/221; H10D62/235; H10D62/299; H10D62/307; H10D62/351; H10D62/357; H10D62/364; H10D62/371; H10P; H10P30/00; H10P30/20; H10P30/222
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
89 words
A method of manufacturing a semiconductor device, which method comprises: forming a polysilicon gate on a main surface of a semiconductor substrate; forming source/drain regions in the substrate having junctions with the substrate; heating to electrically activate the source/drain regions; ion implanting impurities at an acute angle into the substrate to form a lateral channel implant below the gate after the step of heating to electrically activate the source/drain regions; and heating to electrically activate the lateral channel implant without substantially diffusing the lateral channel implant under the junctions.
Claim 2
Independent Claim
89 words
A method of manufacturing a semiconductor device, which method comprises: forming a polysilicon gate on a main surface of a semiconductor substrate; forming source/drain regions in the substrate having junctions with the substrate; heating to electrically activate the source/drain regions; ion implanting impurities at an acute angle into the substrate to form a lateral channel implant below the gate after the step of heating to electrically activate the source/drain regions; and heating to electrically activate the lateral channel implant without substantially diffusing the lateral channel implant under the junctions.
Claim 3
Dependent Claim
25 words
The method according to claim 1 , comprising implanting impurities at an angle of about 32° to about 45° to form the lateral channel implant.
Claim 4
Dependent Claim
45 words
The method according to claim 2 , comprising implanting impurities at a dosage of about 5×10 12 atoms cm −2 to about 3×10 13 atom cm −2 and at an energy of about 30 keV to about 80 keV to form the lateral channel implant.
Claim 5
Dependent Claim
24 words
The method according to claim 3 , comprising implanting boron, BF 2 , indium, antimony, arsenic or phosphorus to form the lateral channel implant.
Claim 6
Dependent Claim
26 words
The method according to claim 1 , comprising heating to electrically activate the lateral channel implant at a temperature of no greater than about 800° C.
Claim 7
Dependent Claim
54 words
The method according to claim 1 , wherein the step of forming the polysilicon gate comprises: thermally growing a gate oxide on the main surface; depositing a blanket layer of polysilicon by LPCVD on the gate oxide; masking a portion of the polysilicon layer corresponding to the polysilicon gate; and etching the polysilicon layer.
Claim 8
Dependent Claim
88 words
The method according to claim 1 , wherein the step of forming the source/drain regions comprises: ion implanting impurities into the substrate to form an LDD implant; forming an oxide buffer layer on the main surface and on sidewalls of the gate; forming first protective spacers on the buffer layer on the sidewalls of the gate and extending onto the main surface; and ion implanting impurities into the substrate to form a source/drain implant; the method comprising removing the first protective spacers before forming the lateral channel implant.
Claim 9
Dependent Claim
44 words
The method according to claim 7 , comprising implanting impurities at a dosage of about 5×10 13 atoms cm −2 to about 2×10 14 atom cm −2 and at an energy of about 2 keV to about 5 keV to form the LDD implant.
Claim 10
Dependent Claim
20 words
The method according to claim 8 , comprising implanting BF 2 , arsenic or antimony to form the LDD implant.
Claim 11
Dependent Claim
35 words
The method according to claim 7 , wherein the step of forming an oxide buffer layer comprises thermally growing a layer of silicon dioxide to a thickness of about 30 Å to about 60 Å.
Claim 12
Dependent Claim
34 words
The method according to claim 7 , wherein the step of forming an oxide buffer layer comprises depositing a layer of silicon dioxide to a thickness of about 30 Å to about 60 Å.
Claim 13
Dependent Claim
47 words
The method according to claim 7 , wherein the step of forming the first protective spacers comprises: forming a layer of silicon nitride on the buffer layer by LPCVD to a thickness of about 300 Å to about 600 Å; and anisotropically etching the silicon nitride layer.
Claim 14
Dependent Claim
44 words
The method according to claim 7 , comprising implanting impurities at a dosage of about 2×10 15 atoms cm −2 to about 4×10 15 atom cm −2 and at an energy of about 2 keV to about 4 keV to form the source/drain implant.
Claim 15
Dependent Claim
23 words
The method according to claim 13 , comprising implanting boron, BF 2 , indium, antimony, arsenic or phosphorus to form the source/drain implant.
Claim 16
Dependent Claim
41 words
The method according to claim 1 , wherein the step of heating to electrically activate the source/drain regions includes rapid thermal annealing at a temperature of about 1020° C. to about 1050° C. for about 10 seconds to about 20 seconds.
Claim 17
Dependent Claim
97 words
The method according to claim 7 , further comprising: forming a layer of silicon dioxide on the buffer layer after forming the lateral channel implant; anisotropically etching the silicon dioxide layer to form second protective spacers on the sidewalls of the gate and extending onto the main surface, and to remove portions of the buffer layer on the main surface and the gate not covered by the second protective spacers; forming a metal layer on the main surface and the gate; and heating to form a metal silicide layer and to electrically activate the lateral channel implant.
Claim 18
Dependent Claim
56 words
The method according to claim 16 , wherein the step of heating to form a metal silicide layer comprises: heating at a first temperature to form a first-phase metal silicide layer; and heating at a second temperature to form a second-phase metal silicide layer having a resistivity lower than that of the first-phase metal silicide layer.
Claim 19
Dependent Claim
37 words
The method according to claim 17 , wherein the metal layer comprises cobalt or titanium, the first-phase metal silicide layer comprises CoSi or TiSi, and the second-phase metal silicide layer comprises CoSi 2 or TiSi 2 .
Claim 20
Dependent Claim
49 words
The method according to claim 18 , wherein the step of heating at the first temperature includes rapid thermal annealing at about 600° C. to about 650° C., and the step of heating at the second temperature includes rapid thermal annealing at about 700° C. to about 800° C.
References Cited (Backward Citations)
US4841346A
Cited
US5578510A
Cited
US5500379A
Cited
US5543337A
Cited
US5478763A
Cited
US6020231A
Cited
US5851886A
Cited
US5893740A
Cited
US5874329A
Cited
US6020244A
Cited
US6010952A
Cited
US6025232A
Cited
US6030875A
Cited
US6051860A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-01-30 | 2004-07-31 | 2005-01-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-01-30 | 2008-07-31 | 2009-01-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-01-30 | 2012-07-31 | 2013-01-30 | $7700.00 | Window Closed / Lapsed |