Process for forming metal silicide contacts using amorphization of exposed silicon while minimizing device degradation

Claim 2

An improved process for implanting the exposed portions of a surface of a silicon substrate and the surface of a polysilicon gate electrode to amorphize such silicon to permit the subsequent formation of metal silicide having smaller grain size than metal silicide formed from non-amorphized silicon, the improvement comprising: a) orienting said silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 15° to about 60° with a line perpendicular to the plane of said surface of said substrate; and b) implanting said exposed portions of said surface of said silicon substrate and said polysilicon gate electrode surface with said implantation beam to amorphize said silicon surfaces while maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate.

Claim 3

The process of claim 1 wherein said exposed silicon surfaces are implanted with an ion capable of amorphizing said exposed silicon surfaces selected from the group of elements consisting of a Group III element, a Group IV element, a Group V element, and a Group VIII element.

Claim 4

The process of claim 1 wherein said exposed silicon surfaces are implanted with an ion selected from the group of elements consisting of gallium, indium, germanium, arsenic, antimony, argon, krypton, and xenon.

Claim 5

The process of claim 1 wherein said ions are implanted at a dosage level equivalent to an arsenic dosage ranging from about 1×10 14 atoms/cm 2 to about 3×10 14 atoms/cm 2 .

Claim 6

The process of claim 1 wherein said ions are implanted at an implant energy ranging from about 20 KeV to about 40 KeV.

Claim 7

The process of claim 1 wherein said tilt angle ranges from about 30° to about 60°.

Claim 8

The process of claim 1 wherein said tilt angle ranges from about 40° to about 50°.

Claim 9

The process of claim 1 wherein said tilt angle is about 45°.

Claim 10

The process of claim 1 wherein said implanting step further comprises rotating said silicon substrate through one or more 90° intervals while maintaining said angle between said axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate.

Claim 11

The process of claim 1 wherein said implanting step further comprises rotating said silicon substrate through four 90° intervals while maintaining said angle between said axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate.

Claim 12

An improved process for implanting exposed portions of the surface of a silicon substrate where source and drain regions of an MOS device have been formed and for implanting the surface of a polysilicon gate electrode of said MOS device to amorphize such exposed portions of said silicon substrate surface and said polysilicon gate electrode surface to permit the subsequent formation of metal silicide on said implanted surfaces having smaller grain size than metal silicide formed from non-amorphized silicon without increasing the leakage current of said MOS device, the improvement comprising: a) orienting said silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 30° to about 60° with a line perpendicular to the plane of the surface of said substrate; and b) implanting said exposed portions of said surface of said silicon substrate and said polysilicon gate electrode surface with said implantation beam to amorphize said exposed silicon surfaces while maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate; whereby implantation of said ions, from said implantation beam, into the gate oxide or the channel of said MOS device, is inhibited.

Claim 13

An improved process for implanting exposed portions of the surface of a silicon substrate where source and drain regions of an MOS device have been formed and for implanting the surface of a polysilicon gate electrode of said MOS device to amorphize such exposed portions of said silicon substrate surface and said polysilicon gate electrode surface to permit the subsequent formation of metal silicide on said implanted surfaces having smaller grain size than metal silicide formed from non-amorphized silicon without increasing the leakage current of said MOS device, the improvement comprising: a) orienting said silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 30° to about 60° with a line perpendicular to the plane of the surface of said substrate; and b) implanting said exposed portions of said surface of said silicon substrate and said polysilicon gate electrode surface with said implantation beam to amorphize said exposed silicon surfaces while maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate; whereby implantation of said ions, from said implantation beam, into the gate oxide or the channel of said MOS device, is inhibited.

Claim 14

The process of claim 11 wherein said exposed silicon surfaces are implanted with an ion capable of amorphizing said exposed silicon surfaces selected from the group of elements consisting of a Group III element, a Group IV element, a Group V element, and a Group VIII element.

Claim 15

The process of claim 11 wherein said exposed silicon surfaces are implanted with an ion selected from the group of elements consisting of gallium, indium, germanium, arsenic, antimony, argon, krypton, and xenon.

Claim 16

The process of claim 11 wherein said ions are implanted at a dosage level equivalent to an arsenic dosage ranging from about 1×10 14 atoms/cm 2 to about 3×10 14 atoms/cm 2 .

Claim 17

The process of claim 11 wherein said ions are implanted at an implant energy ranging from about 20 KeV to about 40 KeV.

Claim 18

The process of claim 11 wherein said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate ranges from about 30° to about 45°.

Claim 19

A silicon substrate having exposed portions of the surface thereof where source and drain regions of an MOS device have been formed and a polysilicon gate electrode with an upper surface thereon, said gate electrode formed on said substrate surface between said source and drain regions of said MOS device, said exposed surface of said silicon substrate and said exposed surface of said polysilicon gate electrode amorphized to permit the subsequent formation of metal silicide on said implanted surfaces having smaller grain size than metal silicide formed from non-amorphized silicon without increasing the leakage current of said MOS device, said amorphized surfaces formed by: a) orienting said silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 15° to about 60° with a line perpendicular to the plane of the surface of said substrate; and b) implanting said exposed portions of said surface of said silicon substrate and said polysilicon gate electrode surface with said implantation beam to amorphize said exposed silicon surfaces while maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate; whereby implantation of said ions, from said implantation beam, into the gate oxide or the channel of said MOS device, is inhibited.

Claim 20

A silicon substrate having exposed portions of the surface thereof where source and drain regions of an MOS device have been formed and a polysilicon gate electrode with an upper surface thereon, said gate electrode formed on said substrate surface between said source and drain regions of said MOS device, said exposed surface of said silicon substrate and said exposed surface of said polysilicon gate electrode amorphized to permit the subsequent formation of metal silicide on said implanted surfaces having smaller grain size than metal silicide formed from non-amorphized silicon without increasing the leakage current of said MOS device, said amorphized surfaces formed by: a) orienting said silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 15° to about 60° with a line perpendicular to the plane of the surface of said substrate; and b) implanting said exposed portions of said surface of said silicon substrate and said polysilicon gate electrode surface with said implantation beam to amorphize said exposed silicon surfaces while maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate; whereby implantation of said ions, from said implantation beam, into the gate oxide or the channel of said MOS device, is inhibited.

Claim 21

The process of claim 11 wherein said implanting step further comprises rotating said silicon substrate through one or more 90° intervals while maintaining said angle between said axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate.

Claim 22

The process of claim 11 wherein said implanting step further comprises rotating said silicon substrate through four 90° intervals while maintaining said angle between said axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate.

Claim 23

The process of claim 11 wherein said tilt angle ranges from about 40° to about 50°.

Claim 24

An improved process for implanting the surface of a polysilicon gate electrode of an MOS device to amorphize said polysilicon gate electrode surface to permit the subsequent formation of metal silicide on said implanted surfaces having a smaller grain size than metal silicide formed from non-amorphized silicon without increasing the leakage current of said MOS device, the improvement comprising: a) orienting a silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 30° to about 60° with a line perpendicular to the plane of the surface of said substrate; b) implanting said surface of said polysilicon gate electrode with a non-dopant ion, capable of amorphizing said polysilicon gate electrode, said non-dopant ion selected from the group of consisting of germanium, argon, krypton, and xenon; and c) maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate during said implantation; whereby implantation of said ions, from said implantation beam, into the gate oxide or the channel of said MOS device beneath said polysilicon gate electrode, is inhibited.

Claim 25

An improved process for implanting the surface of a polysilicon gate electrode of an MOS device to amorphize said polysilicon gate electrode surface to permit the subsequent formation of metal silicide on said implanted surfaces having a smaller grain size than metal silicide formed from non-amorphized silicon without increasing the leakage current of said MOS device, the improvement comprising: a) orienting a silicon substrate to an implantation beam so that the axis of said implantation beam defines an angle ranging from about 30° to about 60° with a line perpendicular to the plane of the surface of said substrate; b) implanting said surface of said polysilicon gate electrode with a non-dopant ion, capable of amorphizing said polysilicon gate electrode, said non-dopant ion selected from the group of consisting of germanium, argon, krypton, and xenon; and c) maintaining said tilt angle between the axis of said implantation beam and said line perpendicular to said plane of said surface of said silicon substrate during said implantation; whereby implantation of said ions, from said implantation beam, into the gate oxide or the channel of said MOS device beneath said polysilicon gate electrode, is inhibited.