Two step thermal treatment procedure applied to polycide structures deposited using dichlorosilane as a reactant
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-05-15
•
Granted: 1999-07-13
•
Expires: 2018-05-15
Abstract
Abstract A process for fabricating a polycide SAC structure, for a MOSFET device, has been developed. This process features a polycide SAC structure, comprised of tungsten silicide on in situ doped polysilicon, using tungsten hexafluoride and dichlorosilane as reactants for deposition of tungsten silicide. A first thermal anneal treatment is performed prior to polycide patterning, supplying protection to exposed tungsten silicide sides, during the patterning procedure. A second thermal anneal treatment is performed after polycide patterning, and prior to a silicon oxide deposition, offering protection to the exposed top surface of tungsten silicide, during the silicon oxide deposition.
Inventors
- 👤 Kuo-Hsien Cheng
- 👤 Chi-Di An
- 👤 Wen Jan Lin
- 👤 Hung-Che Liao
- 👤 Jer-Yuan Sheu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:20
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/069; H10D; H10D64/00; H10D64/01; H10D64/013; H10D64/01302; H10D64/01304; H10D64/01306; H10D64/01308; H10D64/01312; H10D64/01332; H10D64/01336; H10D64/01338
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
140 words
A method of fabricating a polycide, self-aligned contact, (SAC), structure, for a MOSFET device, on a semiconductor substrate, comprising the steps of: providing a gate insulator layer on said semiconductor substrate; providing insulator capped, polycide gate structures on said gate insulator layer; providing insulator spacers on the sides of said polycide gate structures; providing source/drain regions, in regions of said semiconductor substrate, not covered by said insulator capped, polycide gate structures; depositing a first insulator layer; forming a self aligned contact, (SAC), opening in said first insulator layer, exposing a source/drain region, between polycide gate structures; depositing a polysilicon layer; depositing a metal silicide layer; performing a first thermal anneal treatment; patterning of said metal silicide layer, and of said polysilicon layer, to create said polycide SAC structure; performing a second thermal anneal treatment; and depositing a second insulator layer.
Claim 2
Independent Claim
140 words
A method of fabricating a polycide, self-aligned contact, (SAC), structure, for a MOSFET device, on a semiconductor substrate, comprising the steps of: providing a gate insulator layer on said semiconductor substrate; providing insulator capped, polycide gate structures on said gate insulator layer; providing insulator spacers on the sides of said polycide gate structures; providing source/drain regions, in regions of said semiconductor substrate, not covered by said insulator capped, polycide gate structures; depositing a first insulator layer; forming a self aligned contact, (SAC), opening in said first insulator layer, exposing a source/drain region, between polycide gate structures; depositing a polysilicon layer; depositing a metal silicide layer; performing a first thermal anneal treatment; patterning of said metal silicide layer, and of said polysilicon layer, to create said polycide SAC structure; performing a second thermal anneal treatment; and depositing a second insulator layer.
Claim 3
Dependent Claim
39 words
The method of claim 1, wherein said gate insulator layer is silicon dioxide, obtained via thermal oxidation, in an oxygen-steam ambient, at a temperature between about 850 to 1000° C., to a thickness between about 50 to 200 Angstroms.
Claim 4
Dependent Claim
59 words
The method of claim 1, wherein said polycide gate structures are comprised of an underlying in situ doped, polysilicon layer, deposited using LPCVD procedures, to a thickness between about 500 to 1500 Angstroms, and an overlying tungsten silicide layer, deposited using LPCVD procedures, to a thickness between about 800 to 1500 Angstroms, using tungsten hexafluoride and dichlorosilane, as reactants.
Claim 5
Dependent Claim
41 words
The method of claim 1, wherein said polycide gate structures are formed via an anisotropic RIE procedure, using CHF 3 as an etchant for the capping insulator layer, and using Cl 2 as an etchant for tungsten silicide and polysilicon layers.
Claim 6
Dependent Claim
28 words
The method of claim 1, wherein said first insulator layer is silicon oxide, deposited using LPCVD or PECVD procedures, to a thickness between about 800 to 2500 Angstroms.
Claim 7
Dependent Claim
27 words
The method of claim 1, wherein said SAC opening is formed in said first insulator layer, via an anisotropic RIE procedure, using CHF 3 as an etchant.
Claim 8
Dependent Claim
39 words
The method of claim 1, wherein said polysilicon layer is deposited using LPCVD procedures, to a thickness between about 200 to 1000 Angstroms, using dichlorosilane as a source, and doped in situ via the addition of arsine or phosphine.
Claim 9
Dependent Claim
33 words
The method of claim 1, wherein said metal silicide layer is tungsten silicide, deposited using LPCVD procedures, to a thickness between about 800 to 1500 Angstroms, using tungsten hexafluoride and dichlorosilane as reactants.
Claim 10
Dependent Claim
35 words
The method of claim 1, wherein said first thermal anneal treatment is performed using conventional furnace procedures, or using rapid thermal processing, at a temperature between about 700 to 850° C., in a nitrogen ambient.
Claim 11
Dependent Claim
33 words
The method of claim 1, wherein said polycide SAC structure is formed via an anisotropic RIE procedure, using Cl 2 as an etchant for said metal silicide layer, and for said polysilicon layer.
Claim 12
Dependent Claim
35 words
The method of claim 1, wherein said second thermal anneal treatment is performed using conventional furnace procedures, or using rapid thermal processing, at a temperature between about 700 to 850° C., in a nitrogen ambient.
Claim 13
Dependent Claim
33 words
The method of claim 1, wherein said second insulator layer is silicon oxide, deposited using LPCVD or PECVD procedures, at a temperature between about 300 to 750° C., using TEOS as a source.
Claim 14
Independent Claim
229 words
A method for forming a polycide self-aligned contact, (SAC), structure, for MOSFET devices, on a semiconductor substrate, using thermal anneal procedures to protect a dichlorosilane grown, tungsten silicide layer, during a polycide patterning, and during an overlying insulator deposition, comprising the steps of: providing a gate insulator layer on said semiconductor substrate; providing silicon oxide capped, polycide gate structures, with silicon oxide spacers on the sides of said silicon oxide capped, polycide gate structures, on said gate insulator layer; providing source/drain regions, in a region of said semiconductor substrate, not covered by said silicon oxide capped, polycide gate structures; depositing a first inter-polysilicon oxide, (IPO-1), layer; forming a self-aligned contact, (SAC), opening, in said IPO-1 layer, exposing a source/drain region, between silicon oxide capped, polycide gate structures; depositing an in situ doped polysilicon layer; depositing a tungsten silicide layer, on said in situ doped polysilicon layer, using dichlorosilane and tungsten hexafluoride as a source; performing a first thermal anneal treatment; patterning of said tungsten silicide layer, and of said in situ doped polysilicon layer, to form said polycide SAC structure, completely overlying said source/drain region, exposed in said SAC opening, and partially overlying a top portion of said silicon oxide capped, polycide gate structures, in areas where said polycide gate structures abut said SAC opening; performing a second thermal anneal treatment; and depositing a second inter-polysilicon oxide, (IPO-2), layer.
Claim 15
Independent Claim
229 words
A method for forming a polycide self-aligned contact, (SAC), structure, for MOSFET devices, on a semiconductor substrate, using thermal anneal procedures to protect a dichlorosilane grown, tungsten silicide layer, during a polycide patterning, and during an overlying insulator deposition, comprising the steps of: providing a gate insulator layer on said semiconductor substrate; providing silicon oxide capped, polycide gate structures, with silicon oxide spacers on the sides of said silicon oxide capped, polycide gate structures, on said gate insulator layer; providing source/drain regions, in a region of said semiconductor substrate, not covered by said silicon oxide capped, polycide gate structures; depositing a first inter-polysilicon oxide, (IPO-1), layer; forming a self-aligned contact, (SAC), opening, in said IPO-1 layer, exposing a source/drain region, between silicon oxide capped, polycide gate structures; depositing an in situ doped polysilicon layer; depositing a tungsten silicide layer, on said in situ doped polysilicon layer, using dichlorosilane and tungsten hexafluoride as a source; performing a first thermal anneal treatment; patterning of said tungsten silicide layer, and of said in situ doped polysilicon layer, to form said polycide SAC structure, completely overlying said source/drain region, exposed in said SAC opening, and partially overlying a top portion of said silicon oxide capped, polycide gate structures, in areas where said polycide gate structures abut said SAC opening; performing a second thermal anneal treatment; and depositing a second inter-polysilicon oxide, (IPO-2), layer.
Claim 16
Dependent Claim
34 words
The method of claim 13, wherein said IPO-1 layer, is a silicon oxide layer, deposited using LPCVD or PECVD procedures, to a thickness between about 800 to 2500 Angstroms, using TEOS as a source.
Claim 17
Dependent Claim
26 words
The method of claim 13, wherein said SAC opening is formed in said IPO-1 layer, via an anisotropic RIE procedure, using CHF 3 as an etchant.
Claim 18
Dependent Claim
39 words
The method of claim 13, wherein said in situ doped polysilicon layer is deposited using LPCVD procedures, to a thickness between about 200 to 1000 Angstroms, using dichlorosilane as a source, with the addition of either arsine or phosphine.
Claim 19
Dependent Claim
31 words
The method of claim 13, wherein said tungsten silicide layer is deposited using LPCVD procedures, to a thickness between about 800 to 1500 Angstroms, using tungsten hexafluoride and dichlorosilane as reactants.
Claim 20
Dependent Claim
36 words
The method of claim 13, wherein said first thermal anneal treatment is performed at a temperature between about 700 to 850° C., in a nitrogen ambient, using conventional furnace procedures, or using rapid thermal processing procedures.
Claim 21
Dependent Claim
36 words
The method of claim 13, wherein said polycide SAC structure is formed via an anisotropic RIE procedure, using Cl 2 as an etchant for said tungsten silicide layer, and for said in situ doped polysilicon layer.
Claim 22
Dependent Claim
36 words
The method of claim 13, wherein said second thermal anneal treatment is performed at a temperature between about 700 to 850° C., in a nitrogen ambient, using conventional furnace procedures, or using rapid thermal processing procedures.
Claim 23
Dependent Claim
43 words
The method of claim 13, wherein said IPO-2 layer, is a silicon oxide layer, deposited using LPCVD or PECVD procedures, at a temperature between about 300 to 750° C., to a thickness between about 800 to 2000 Angstroms, using TEOS as a source.
References Cited (Backward Citations)
US4833099A
Cited
US5075251A
Cited
US5541131A
Cited
US5182232A
Cited
US5231056A
Cited
US5393685A
Cited
US5552339A
Cited
US5691235A
Cited
US5624870A
Cited
US5550078A
Cited
US5633200A
Cited
US5706164A
Cited
US5763303A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-12 | 2003-01-11 | 2003-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-12 | 2007-01-11 | 2007-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-12 | 2011-01-11 | 2011-07-13 | $7700.00 | Window Closed / Lapsed |