Method of fabricating a ferrolelectric capacitor with a graded barrier layer structure
Assignee: Hanger Solutions LLC
•
Filing: 1997-11-20
•
Granted: 1999-07-13
•
Expires: 2017-11-20
Abstract
Abstract A method of fabricating an integrated circuit capacitor in which a first conductive plate, a layer of ferroelectric material, and a second conductive plate are deposited and formed in sequence. Thereafter a diffusion barrier material and an insulative material are deposited either (1) as layers of the diffusion barrier material and the insulative material with tensile and compressive stresses in the respective layers offsetting one another, (2) as a layered dielectric stack with alternating layers of the diffusion barrier material and the insulative material, or (3) as a graded diffusion barrier material varying from a binary oxide of Ta, Nb, or Zr at the surface of the ferroelectric material to SiO 2 at a distance above the surface of the ferroelectric material.
Inventors
- 👤 Peter S. Kirlin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:55
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/682; H10D1/692; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6938; H10P14/69398
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
95 words
A method of fabricating a capacitor, comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; d. depositing over the second conductive plate and a part of the ferroelectric material a diffusion barrier material with residual internal tensile stress in its structure; and e. depositing over the diffusion barrier material an insulative material with a residual internal compressive stress in its structure.
Claim 2
Independent Claim
95 words
A method of fabricating a capacitor, comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; d. depositing over the second conductive plate and a part of the ferroelectric material a diffusion barrier material with residual internal tensile stress in its structure; and e. depositing over the diffusion barrier material an insulative material with a residual internal compressive stress in its structure.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein: the ferroelectric material comprises a material selected from the group consisting of PbZrTiO 3 and SrBi 2 Ta 2 O 9 .
Claim 4
Dependent Claim
82 words
The method of claim 1 wherein: the diffusion barrier layer material comprises a material selected from the group consisting of TiO 2 , ZrO 2 , Ta 2 O 5 , Nb 2 O 5 , Zr 1-x Ti x O 2 , where x is a number in a range from zero to one, and Ta 5-y Si y O 10 , Nb 5-y Si y O 10 , where y is a number in a range from zero to five.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein: the diffusion barrier material is deposited by sputtering.
Claim 6
Dependent Claim
15 words
The method of claim 1 wherein: the diffusion barrier layer material is deposited by evaporation.
Claim 7
Dependent Claim
18 words
The method of claim 1 wherein: the diffusion barrier layer material is deposited by physical vapor deposition (PVD).
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein: the insulative layer material is SiO 2 deposited by chemical vapor deposition (CVD).
Claim 9
Dependent Claim
61 words
The method of claim 6 wherein: the insulative layer material comprises a material selected from the group consisting of materials including Si 3 N 4 , spin-on-glass, SiF x O 4-z , and an organic dielectric, where z is a number in a range from zero to four and the selected insulative layer material is spun onto the diffusion barrier layer.
Claim 10
Independent Claim
74 words
A method of fabricating a capacitor, comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; and d. depositing over the second conductive plate a layered dielectric stack with alternating layers of a diffusion barrier material and of an insulative material.
Claim 11
Independent Claim
74 words
A method of fabricating a capacitor, comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; and d. depositing over the second conductive plate a layered dielectric stack with alternating layers of a diffusion barrier material and of an insulative material.
Claim 12
Dependent Claim
61 words
The method of claim 9 wherein: stress in the layered dielectric stack is reduced in comparison to a corresponding capacitor structure lacking the layered dielectric stack, by selecting a desirable number of layers, thickness of layers, and/or deposition conditions, so that tensile stresses in the diffusion barrier material and compressive stresses in the insulative material are correspondingly cancelling of one another.
Claim 13
Dependent Claim
23 words
The method of claim 9 wherein: the insulative material of the layered dielectric stack is SiO 2 deposited by chemical vapor deposition (CVD).
Claim 14
Dependent Claim
63 words
The method of claim 9 wherein: the insulative material of the layered dielectric stack comprises a material selected from the group consisting of Si 3 N 4 , spin on glass, SiF z O 4-z , and an organic dielectric, where z is a number in a range from zero to four and the selected insulative material is spun onto the barrier layer.
Claim 15
Dependent Claim
54 words
The method of claim 9 wherein: the diffusion barrier material comprises a material selected from the group consisting of TiO 2 , ZrO 2 , Ta 2 O 5 , and Nb 2 O 5 and is deposited by a process selected from the group consisting of physical vapor deposition (PVD), sputtering, and evaporation.
Claim 16
Dependent Claim
58 words
The method of claim 13 wherein: the insulative material comprises a material selected from the group consisting of Si 3 N 4 , spin on glass, SiF z O 4-z , and an organic dielectric, where z is a number in a range from zero to four and the selected insulative material is spun onto the barrier layer.
Claim 17
Independent Claim
114 words
The method of fabricating a capacitor, the method comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; d. depositing a graded diffusion barrier material on the layer of ferroelectric material, the graded diffusion barrier material having a content defined by Ta 5-y Si y O 10 or Nb 5-y Si y O 10 and the number y varying from zero at the surface of the ferroelectric material to five at a desired distance above the surface of the ferroelectric material.
Claim 18
Independent Claim
114 words
The method of fabricating a capacitor, the method comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; d. depositing a graded diffusion barrier material on the layer of ferroelectric material, the graded diffusion barrier material having a content defined by Ta 5-y Si y O 10 or Nb 5-y Si y O 10 and the number y varying from zero at the surface of the ferroelectric material to five at a desired distance above the surface of the ferroelectric material.
Claim 19
Independent Claim
103 words
The method of fabricating a capacitor, the method comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; d. depositing a graded diffusion barrier material on the layer of ferroelectric material, the graded diffusion barrier material having a content defined by Zr 1-x SiO 2 and x varying from zero at the surface of the ferroelectric material to one at a desired distance above the surface of the ferroelectric material.
Claim 20
Independent Claim
103 words
The method of fabricating a capacitor, the method comprising the steps of: a. depositing and forming a first conductive plate on a substrate; b. depositing and forming a layer of ferroelectric material over the first conductive plate; c. depositing and forming a second conductive plate on the layer of ferroelectric material; d. depositing a graded diffusion barrier material on the layer of ferroelectric material, the graded diffusion barrier material having a content defined by Zr 1-x SiO 2 and x varying from zero at the surface of the ferroelectric material to one at a desired distance above the surface of the ferroelectric material.
References Cited (Backward Citations)
US476274A
Cited
DE370473C
Cited
US2490547A
Cited
US2622184A
Cited
US2801322A
Cited
US2925329A
Cited
US3190262A
Cited
US3404873A
Cited
US3520416A
Cited
US3549412A
Cited
US3659402A
Cited
US3823926A
Cited
US3969449A
Cited
US4036915A
Cited
US4080926A
Cited
US4529427A
Cited
US4288396A
Cited
EP0058571A1
Cited
JPS58125633A
Cited
US4833976A
Cited
US4842893A
Cited
US5097800A
Cited
US4954371A
Cited
US4847469A
Cited
US5034372A
Cited
EP0328333A2
Cited
US5110622A
Cited
US5248787A
Cited
EP0405634A2
Cited
US5139999A
Cited
US5120703A
Cited
US5280012A
Cited
US5204314A
Cited
US5225561A
Cited
US5536323A
Cited
US5165960A
Cited
WO1993004072A1
Cited
US5259995A
Cited
US5376409A
Cited
US5376409B1
Cited
US5780351A
Cited
US5416042A
Cited
US5696018A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-12 | 2003-01-11 | 2003-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-12 | 2007-01-11 | 2007-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-12 | 2011-01-11 | 2011-07-13 | $7700.00 | Window Closed / Lapsed |