US4842893A
Expired / Lapsed
US
⏱️ 0.0 years remaining
High speed process for coating substrates
Assignee: Spectrum Control Inc
•
Filing: 1988-04-29
•
Granted: 1989-06-27
•
Expires: 2008-04-29
Abstract
Abstract A high-speed process for coating substrates with thin organic coatings in a vacuum is disclosed and claimed. The process utilizes relatively low boiling, reactive monomers (e.g., polyacrylates) which are flash vaporized, condensed on the substrates and cured, in situ. The resultant cured films are pin-hole free and exhibit excellent adhesion. The process is capable of being run at very high coating and curing speeds, e.g., between 1 and 1000 cm/second.
Inventors
- 👤 Angelo Yializis
- 👤 David G. Shaw
- 👤 Donald S. Strycker
- 👤 Mooyoung Ham
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 21:56
CPC Classifications
B; B05; B05D; B05D1/00; B05D1/60; B05D3/00; B05D3/06; B05D3/068; B05D7/00; B05D7/24; B05D7/50; B05D7/56; C; C23; C23C; C23C14/00; C23C14/06; C23C14/12; C23C14/22; C23C14/56; C23C14/562; H; H01; H01G; H01G13/00; H01G4/00; H01G4/30; H01G4/306; B05D3/14; B05D3/141; B05D3/145; B05D3/148
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
257 words
A high-speed process for coating the surface of a substrate with an adherent film comprising the following steps: (a) providing a vacuum chamber containing: (i) a movable support, (ii) a vapor outlet of a vaporizer mounted adjacent to an upstream portion of said support, (iii) curing means mounted adjacent to a downstream portion of said support, and (iv) means for maintaining said support at a temperature below that of said vaporizer; (b) placing said substrate in thermal contact with said movable support in a manner permitting the surface of said substrate to move sequentially past said vapor outlet and said curing means; (c) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -2 Torr; (d) selecting a curable component having an average of about two or more olefinic groups per molecule, an average molecular weight between 150 and 1000, and a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (e) metering a quantity of said curable component into an inlet portion of said vaporizer; (f) vaporizing said component within said vaporizer; (g) moving said support at a speed sufficient to pass said substrate relative to said vapor outlet and said curing means at a rate between about 1 cm/sec and 1000 cm/sec; (h) condensing a film of said component on the surface of said substrate, said film having a thickness of less than 4 microns; and (i) activating said curing means whereby a adherent film is formed on said substrate surface.
Claim 2
Dependent Claim
257 words
A high-speed process for coating the surface of a substrate with an adherent film comprising the following steps: (a) providing a vacuum chamber containing: (i) a movable support, (ii) a vapor outlet of a vaporizer mounted adjacent to an upstream portion of said support, (iii) curing means mounted adjacent to a downstream portion of said support, and (iv) means for maintaining said support at a temperature below that of said vaporizer; (b) placing said substrate in thermal contact with said movable support in a manner permitting the surface of said substrate to move sequentially past said vapor outlet and said curing means; (c) evacuating gas from said chamber until the pressure within said chamber is less than about 1×10 -2 Torr; (d) selecting a curable component having an average of about two or more olefinic groups per molecule, an average molecular weight between 150 and 1000, and a vapor pressure in the range of 1×10 -6 to 1×10 -1 Torr at standard temperature and pressure; (e) metering a quantity of said curable component into an inlet portion of said vaporizer; (f) vaporizing said component within said vaporizer; (g) moving said support at a speed sufficient to pass said substrate relative to said vapor outlet and said curing means at a rate between about 1 cm/sec and 1000 cm/sec; (h) condensing a film of said component on the surface of said substrate, said film having a thickness of less than 4 microns; and (i) activating said curing means whereby a adherent film is formed on said substrate surface.
Claim 3
Dependent Claim
17 words
The process of claim 1 wherein said vaporizer comprises means for flash vaporization of said curable component.
Claim 4
Dependent Claim
24 words
The process according to claim 1 wherein said curable component is selected from the group consisting of polyacrylates and mixtures of monoacrylates and polyacrylates.
Claim 5
Dependent Claim
56 words
The method of claim 3 wherein said polyacrylate has the formula: ##STR6## wherein: R 1 is an aliphatic, alicyclic or mixed aliphatic-alicyclic radical derived from a compound of the formula R 1 (OH) m ; R 2 is hydrogen, methyl, ethyl, propyl, butyl or pentyl; n is from 2 to 4; m is 2 or more.
Claim 6
Dependent Claim
47 words
The method of claim 3 wherein said monoacrylate has the formula: ##STR7## wherein: R 2 , r and 2 are defined above; x 1 is H or: ##STR8## and X 3 is CN or COOR 3 wehrein R 3 is an alkyl radical containing 1-4 carbon atoms.
Claim 7
Dependent Claim
34 words
The method according to claim 3 wherein said polyacrylate comprises a diacrylate of the formula: ##STR9## wherein: r and s are each 7 or 8 and the sum of r and s is 15.
Claim 8
Dependent Claim
37 words
The method of claim 3 wherein said polyacrylate is selected from the group consisting of: (a) 1,6-hexane diol diacrylate; (b) alkoxylated cyclohexane dimethanol diacrylates wherein the alkoxy group contains 1 to 4 carbon atoms; and (c) ##STR10##
Claim 9
Dependent Claim
14 words
A process according to claim 1 wherein said movable support comprises a rotating drum.
Claim 10
Dependent Claim
26 words
The method according to claim 1 wherein said movable support is maintained at a temperature in the range of about 20° C. to about 80° C.
Claim 11
Dependent Claim
33 words
The method of claim 1 wherein said movable support comprises a rotating drum and said drum passes said vapor outlet and said curing means at a rate of about 100 cm per second.
Claim 12
Dependent Claim
15 words
The method of claim 1 wherein said curing means comprises a gas discharge electron beam.
Claim 13
Dependent Claim
21 words
The method of claim 1 wherein said curing means is aligned tangentially to said film on the surface of said substrate.
Claim 14
Dependent Claim
19 words
The method of claim 1 wherein said vaporizer is maintained at a temperature between approximately 100° and 400° C.
Claim 15
Dependent Claim
16 words
The method of claim 1 wherein said film has a thickness of less than 2 microns.
Claim 16
Dependent Claim
19 words
The method of claim 1 wherein said curable component has a molecular weight in the range 200 to 300.
Claim 17
Dependent Claim
24 words
The method of claim 1 wherein said substrate is flexible and is selected from the group consisting of paper, fabrics, thin metals and plastics.
Claim 18
Dependent Claim
21 words
The method of claim 16 wherein said flexible substrate is a plastic selected from the group consisting of polyester and polyolefins.
Claim 19
Dependent Claim
22 words
The method of claim 1 further including the step: degassing said curable component prior to metering said component into said vaporizer inlet.
Claim 20
Dependent Claim
13 words
The method of claim 1 wherein said movable support comprises a rotatable disk.
Claim 21
Dependent Claim
13 words
The method of claim 1 wherein said movable support comprises a reciprocating plate.
References Cited (Backward Citations)
US2734478A
Cited
CA789746A
Cited
BE660489A
Cited
US1873548A
Cited
GB550419A
Cited
US2389420A
Cited
US2614524A
Cited
US2590906A
Cited
GB762953A
Cited
CH313676A
Cited
US2820934A
Cited
US3081201A
Cited
US3024394A
Cited
US3252830A
Cited
GB970865A
Cited
US3068510A
Cited
US3123490A
Cited
US3237273A
Cited
US3326718A
Cited
US3457614A
Cited
US3244953A
Cited
GB1104172A
Cited
GB1168641A
Cited
US3547683A
Cited
US3466719A
Cited
US3520987A
Cited
GB1253124A
Cited
US3743532A
Cited
US3654532A
Cited
US3617834A
Cited
US3819990A
Cited
US4076866A
Cited
US4121537A
Cited
DE2641232A1
Cited
US4153925A
Cited
US4301580A
Cited
US4207836A
Cited
DE2737509A1
Cited
DE2759118A1
Cited
JPS5527455A
Cited
EP0009806A1
Cited
US4376329A
Cited
FR2440604A1
Cited
US4508049A
Cited
US4277516A
Cited
US4301765A
Cited
US4261798A
Cited
US4379182A
Cited
US4356608A
Cited
US4290384A
Cited
US4434452A
Cited
US4403381A
Cited
US4414722A
Cited
EP0045058A2
Cited
US4378382A
Cited
WO1982000542A1
Cited
US4329419A
Cited
US4363162A
Cited
US4543275A
Cited
US4387113A
Cited
JPS5874701A
Cited
US4502095A
Cited
DE3231576A1
Cited
JPS59177365A
Cited
US4453199A
Cited
US4490774A
Cited
US4533710A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1992-06-26 | 1992-12-26 | 1993-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1996-06-26 | 1996-12-26 | 1997-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2000-06-26 | 2000-12-26 | 2001-06-27 | $7700.00 | Window Closed / Lapsed |