Process for preparing oxide superconducting films by radio-frequency generated aerosol-plasma deposition in atmosphere

Claim 2

A process for coating a layer of oxide super-conductive material containing large amount of small grains, with a thickness of from about 0.1 to about 500 microns onto a substrate at a deposition rate of from about 0.01 to about 10 microns per minute per 35 square centimeters of substrate surface, comprising the steps of: (a) providing a solution comprised of an yttrium compound, a barium compound, and a copper compound, wherein said yttrium, said barium, and said copper are present in said solution in the stoichiometric ratio of 1:2:3, and wherein said solution is comprised of from about 0.01 to about 1,000 grams of a mixture consisting esentially of said yttrium compound, said barium compound, and said copper compound per liter of said solution; (b) subjecting said solution to ultrasonic sound waves at a frequency in excess of 20,000 hertz, and to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury, thereby causing said solution to form into an aerosol; (c) providing a radio frequency plasma reactor comprised of a top section, a bottom section, a radio-frequency coil, and inlet means for feeding oxygen into said top section of said reactor; (d) generating a hot plasma within said radio frequency reactor, thereby producing a plasma region; (e) providing a flame region disposed above said top of said radio frequency plasma reactor; (f) contacting said aerosol with said hot plasma gas within said plasma reactor while subjecting said aerosol to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury and to a radio frequency alternating current at a frequency of from about 100 kilohertz to about 30 megahertz, thereby forming a vapor; (g) feeding oxygen into said top section of said radio-frequency plasma reactor between said plasma region and said flame region; (h) providing a substrate disposed above said flame region; and (i) contacting said vapor with said substrate, thereby forming said layer.

Claim 3

The process as recited in claim 1, wherein said deposition rate is from about 0.1 to about 1.0 microns per minute per 35 square centimeters of substrate surface.

Claim 4

The process as recited in claim 2, wherein said aerosol is subjected while within said plasma reactor to a radio frequency alternating current of from about 1 to about 20 megahertz.

Claim 5

The process as recited in claim 3, wherein said solution is subjected to ultrasonic sound waves at a frequency in excess of one megahertz.

Claim 6

The process as recited in claim 4, wherein said solution is comprised of from about 1 to about 300 grams of said mixture consisting essentially of said yttrium compound, said barium compound, and said copper compound, per liter of said solution.

Claim 7

A process for coating a layer of oxide superconductive material containing large amount of small grains, with a thickness of from about 0.1 to about 500 microns onto a substrate at a deposition rate of from about 0.01 to about 10 microns per minute per 35 square centimeters of substrate surface, comprising the steps of: (a) providing a solution comprised of a bismuth compound, a calcium compound, a strontium compound, and a copper compound, wherein said bismuth, said calcium, said strontium, and said copper are present in said solution in the stoichiometric ratio of 2:1:2:2, and wherein said solution is comprised of from about 0.01 to about 1,000 grams of a mixture consisting essentially of said bismuth compound, said calcium compound, said strontium compound, and said copper compound per liter of said solution; (b) subjecting said solution to ultrasonic sound waves at a frequency in excess of 20,000 hertz, and to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury, thereby causing said solution to form into an aerosol; (c) providing a radio frequency plasma reactor comprised of a top section, a bottom section, a radio-frequency coil, and inlet means for feeding oxygen into said top section of said reactor; (d) generating a hot plasma within said radio frequency reactor, thereby producing a plasma region; (e) providing a flame region disposed above said top of said radio frequency plasma reactor; (f) contacting said aerosol with said hot plasma gas within said plasma reactor while subjecting said aerosol to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury and to a radio frequency alternating current at a frequency of from about 100 kilohertz to about 30 megahertz, thereby forming a vapor; (g) feeding oxygen into said top section of said radio-frequency plasma reactor between said plasma region and said flame region; (h) providing a substrate disposed above said flame region; and (i) contacting said vapor with said substrate, thereby forming said layer.

Claim 8

A process for coating a layer of oxide superconductive material containing large amount of small grains, with a thickness of from about 0.1 to about 500 microns onto a substrate at a deposition rate of from about 0.01 to about 10 microns per minute per 35 square centimeters of substrate surface, comprising the steps of: (a) providing a solution comprised of a bismuth compound, a calcium compound, a strontium compound, and a copper compound, wherein said bismuth, said calcium, said strontium, and said copper are present in said solution in the stoichiometric ratio of 2:1:2:2, and wherein said solution is comprised of from about 0.01 to about 1,000 grams of a mixture consisting essentially of said bismuth compound, said calcium compound, said strontium compound, and said copper compound per liter of said solution; (b) subjecting said solution to ultrasonic sound waves at a frequency in excess of 20,000 hertz, and to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury, thereby causing said solution to form into an aerosol; (c) providing a radio frequency plasma reactor comprised of a top section, a bottom section, a radio-frequency coil, and inlet means for feeding oxygen into said top section of said reactor; (d) generating a hot plasma within said radio frequency reactor, thereby producing a plasma region; (e) providing a flame region disposed above said top of said radio frequency plasma reactor; (f) contacting said aerosol with said hot plasma gas within said plasma reactor while subjecting said aerosol to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury and to a radio frequency alternating current at a frequency of from about 100 kilohertz to about 30 megahertz, thereby forming a vapor; (g) feeding oxygen into said top section of said radio-frequency plasma reactor between said plasma region and said flame region; (h) providing a substrate disposed above said flame region; and (i) contacting said vapor with said substrate, thereby forming said layer.

Claim 9

The process as recited in claim 6, wherein said deposition rate is from about 0.1 to about 1.0 microns per minute per 35 square centimeters of substrate surface.

Claim 10

The process as recited in claim 7, wherein said aerosol is subjected while within said plasma reactor to a radio frequency alternating current of from about 1 to about 20 megahertz.

Claim 11

The process as recited in claim 8, wherein said solution is subjected to ultrasonic sound waves at a frequency in excess of one megahertz.

Claim 12

The process as recited in claim 9, wherein said solution is comprised of from about 1 to about 300 grams of said mixture consisting essentially of said bismuth compound, said calcium compound, said strontium compound, and said copper compound, per liter of said solution.

Claim 13

A process for coating a layer of oxide superconductive material containing large amount of small grains, with a thickness of from about 0.1 to about 500 microns onto a substrate at a deposition rate of from about 0.01 to about 10 microns per minute per 35 square centimeters of substrate surface, comprising the steps of: (a) providing a solution comprised of a bismuth compound, a calcium compound, a strontium compound, and a copper compound, wherein said bismuth, said calcium, said strontium, and said copper are present in said solution in the stoichiometric ratio of 2:2:2:3, and wherein said solution is comprised of from about 0.01 to about 1,000 grams of a mixture consisting essentially of said bismuth compound, said calcium compound, said strotium compound and said copper compound per liter of said solution; (b) subjecting said solution to ultrasonic sound waves at a frequency in excess of 20,000 hertz, and to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury, thereby causing said solution to form into an aerosol; (c) providing a radio frequency plasma reactor comprised of a top section, a bottom section, a radio-frequency coil, and inlet means for feeding oxygen into said top section of said reactor; (d) generating a hot plasma within said radio frequency reactor, thereby producing a plasma region; (e) providing a flame region disposed above said top of said radio frequency plasma reactor; (f) contacting said aerosol with said hot plasma gas within said plasma reactor while subjecting said aerosol to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury and to a radio frequency alternating current at a frequency of from about 100 kilohertz to about 30 megahertz, thereby forming a vapor; (g) feeding oxygen into said top section of said radio-frequency plasma reactor between said plasma region and said flame region; (h) providing a substrate disposed above said flame region; and (i) contacting said vapor with said substrate, thereby forming said layer.

Claim 14

A process for coating a layer of oxide superconductive material containing large amount of small grains, with a thickness of from about 0.1 to about 500 microns onto a substrate at a deposition rate of from about 0.01 to about 10 microns per minute per 35 square centimeters of substrate surface, comprising the steps of: (a) providing a solution comprised of a bismuth compound, a calcium compound, a strontium compound, and a copper compound, wherein said bismuth, said calcium, said strontium, and said copper are present in said solution in the stoichiometric ratio of 2:2:2:3, and wherein said solution is comprised of from about 0.01 to about 1,000 grams of a mixture consisting essentially of said bismuth compound, said calcium compound, said strotium compound and said copper compound per liter of said solution; (b) subjecting said solution to ultrasonic sound waves at a frequency in excess of 20,000 hertz, and to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury, thereby causing said solution to form into an aerosol; (c) providing a radio frequency plasma reactor comprised of a top section, a bottom section, a radio-frequency coil, and inlet means for feeding oxygen into said top section of said reactor; (d) generating a hot plasma within said radio frequency reactor, thereby producing a plasma region; (e) providing a flame region disposed above said top of said radio frequency plasma reactor; (f) contacting said aerosol with said hot plasma gas within said plasma reactor while subjecting said aerosol to a substantially atmospheric pressure of from about 600 to about 1,000 millimeters of mercury and to a radio frequency alternating current at a frequency of from about 100 kilohertz to about 30 megahertz, thereby forming a vapor; (g) feeding oxygen into said top section of said radio-frequency plasma reactor between said plasma region and said flame region; (h) providing a substrate disposed above said flame region; and (i) contacting said vapor with said substrate, thereby forming said layer.

Claim 15

The process as recited in claim 11, wherein said deposition rate is from about 0.1 to about 1.0 microns per minute per 35 square centimeters of substrate surface.

Claim 16

The process as recited in claim 12, wherein said aerosol is subjected while within said plasma reactor to a radio frequency alternating current of from about 1 to about 20 megahertz.

Claim 17

The process as recited in claim 13, wherein said solution is subjected to ultrasonic sound waves at a frequency in excess of one megahertz.

Claim 18

The process as recited in claim 14, wherein said solution is comprised of from about 1 to about 300 grams of said mixture consisting essentially of said bismuth compound, said calcium compound, said strontium compound, and said copper compound, per liter of said solution.

Claim 19

The process as recited in claim 15, wherein said layer of superconductive material has a thickness of from about 1 to about 100 microns.