In-situ etch of BARC layer during formation of local interconnects
Assignee: Advanced Micro Devices Inc
•
Filing: 1997-09-05
•
Granted: 1999-07-06
•
Expires: 2017-09-05
Abstract
Abstract An in-situ etching process for creating local interconnects in a semiconductor device includes using one etching tool to: etch through an organic, or inorganic BARC layer using O 2 gas, or C 2 F 6 /O 2 gases, respectively; a masked dielectric layer to a stop layer using a mixture of C 4 F 8 , CH 3 F and argon (Ar) gasses; etch away the mask layer using a mixture of O 2 and Ar gasses; and, etch through the stop layer using a mixture of CH 3 F gas and O 2 gas. Remaining portions of the BARC layer, whether organic or inorganic, are also removed during the in-situ etching process using appropriate gases. The method then includes depositing conductive material within the openings that were etched to form local interconnects.
Inventors
- 👤 Fei Wang
- 👤 Allison Holbrook
- 👤 James K. Kai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 18:39
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283; H10P76/00; H10P76/20; H10P76/204; H10P76/2041; H10P76/2043; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/0698
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
179 words
A method for forming openings in a semiconductor wafer having a plurality of layers including a bottom anti-reflective layer, the method comprising: using a single etching tool to etch through selected portions of a bottom anti-reflective layer, wherein the selected portions of the bottom anti-reflective layer are defined by etch windows formed by a mask layer above the bottom anti-reflective layer; using the etching tool to etch through selected portions of a first underlying layer below the bottom anti-reflective layer, wherein the selected portions of the first underlying layer are defined by extended etch windows formed by the bottom anti-reflective layer above the first underlying layer; using the etching tool to substantially etch away the mask layer using O 2 gas; using the etching tool to etch through selected portions of a second underlying layer that is below the first underlying layer using a mixture of CH 3 F gas and O 2 gas, wherein the selected portions of the second underlying layer are defined by etched openings in the first underlying layer corresponding to the extended etch windows.
Claim 2
Independent Claim
179 words
A method for forming openings in a semiconductor wafer having a plurality of layers including a bottom anti-reflective layer, the method comprising: using a single etching tool to etch through selected portions of a bottom anti-reflective layer, wherein the selected portions of the bottom anti-reflective layer are defined by etch windows formed by a mask layer above the bottom anti-reflective layer; using the etching tool to etch through selected portions of a first underlying layer below the bottom anti-reflective layer, wherein the selected portions of the first underlying layer are defined by extended etch windows formed by the bottom anti-reflective layer above the first underlying layer; using the etching tool to substantially etch away the mask layer using O 2 gas; using the etching tool to etch through selected portions of a second underlying layer that is below the first underlying layer using a mixture of CH 3 F gas and O 2 gas, wherein the selected portions of the second underlying layer are defined by etched openings in the first underlying layer corresponding to the extended etch windows.
Claim 3
Dependent Claim
28 words
The method as recited in claim 1, wherein the bottom anti-reflective layer includes organic material, and is substantially etched away in the etching tool using O 2 gas.
Claim 4
Dependent Claim
33 words
The method as recited in claim 1, wherein the bottom anti-reflective layer includes inorganic material and is substantially etched away in the etching tool using CH 3 F gas and O 2 gas.
Claim 5
Dependent Claim
16 words
The method as recited in claim 1, wherein the first underlying layer is a dielectric layer.
Claim 6
Dependent Claim
16 words
The method as recited in claim 1, wherein the first underlying layer is an oxide layer.
Claim 7
Dependent Claim
15 words
The method as recited in claim 1, wherein the mask layer is a resist layer.
Claim 8
Dependent Claim
37 words
The method as recited in claim 1, wherein the selected portions of a first underlying layer below the bottom anti-reflective layer are etched using a mixture of C 4 F 8 gas and CH 3 F gas.
Claim 9
Dependent Claim
17 words
The method as recited in claim 1, wherein the mask layer is etched using O 2 gas.
Claim 10
Dependent Claim
26 words
The method as recited in claim 1, wherein the first underlying layer is etched using a mixture of CH 3 F gas and O 2 gas.
Claim 11
Dependent Claim
29 words
The method as recited in claim 1, further comprising supplying argon (Ar) gas to the etching tool when etching at least one of the first underlying and mask layers.
Claim 12
Dependent Claim
31 words
The method as recited in claim 1, wherein the bottom anti-reflective layer is an organic material, and the selected portions of the bottom anti-reflective layer are etched using O 2 gas.
Claim 13
Dependent Claim
33 words
The method as recited in claim 1, wherein the bottom anti-reflective layer is an inorganic material, and the selected portions of the bottom anti-reflective layer are etched using C 2 F 6 gas.
Claim 14
Dependent Claim
25 words
The method as recited in claim 1, wherein the etching tool is a plasma etching tool configured to anisotropically etch one or more semiconductor wafers.
Claim 15
Dependent Claim
26 words
The method as recited in claim 13, wherein the etching tool includes a biasing power supply configured to supply a biasing power to a plasma chamber.
Claim 16
Dependent Claim
31 words
The method as recited in claim 14, wherein when etching away the mask layer further includes selectively supplying approximately 100 to 400 Watts of the biasing power to the plasma chamber.
Claim 17
Dependent Claim
29 words
The method as recited in claim 1, wherein the etching through of the first underlying layer includes using approximately 5 to 20 sccm of C 4 F 8 gas.
Claim 18
Dependent Claim
26 words
The method as recited in claim 10, wherein the etching through of the first underlying layer includes using approximately 200 sccm or less of Argon gas.
Claim 19
Dependent Claim
25 words
The method as recited in claim 1, wherein the etching away the mask layer includes using approximately 5 to 300 sccm of O 2 gas.
Claim 20
Dependent Claim
24 words
The method as recited in claim 10, wherein the etching away the mask layer includes using approximately 100 sccm or less of Argon gas.
Claim 21
Dependent Claim
28 words
The method as recited in claim 1, wherein the etching through of the second underlying layer includes using approximately 20 to 60 sccm of CH 3 F gas.
Claim 22
Dependent Claim
27 words
The method as recited in claim 1, wherein the etching through of the second underlying layer includes using approximately 20 sccm or less of O 2 gas.
Claim 23
Dependent Claim
16 words
The method as recited in claim 1, wherein the second underlying layer is a stop layer.
Claim 24
Dependent Claim
16 words
The method as recited in claim 1, wherein the second underlying layer is a nitride layer.
Claim 25
Dependent Claim
27 words
The method as recited in claim 1 further comprising depositing a conductive material within a local interconnect opening that extends through the first and second underlying layers.
Claim 26
Dependent Claim
28 words
The method as recited in claim 24 wherein the conductive material includes at least one material selected from the set consisting of tungsten (W), and titanium (Ti)/titanium-nitride (TiN).
References Cited (Backward Citations)
US4920065A
Cited
US5453400A
Cited
US5391520A
Cited
US5516726A
Cited
US5387535A
Cited
US5580700A
Cited
US5621235A
Cited
US5521106A
Cited
US5621232A
Cited
US5600165A
Cited
US5489797A
Cited
US5589415A
Cited
US5563096A
Cited
US5780338A
Cited
US5792684A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-07-05 | 2003-01-04 | 2003-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-07-05 | 2007-01-04 | 2007-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-07-05 | 2011-01-04 | 2011-07-06 | $7700.00 | Window Closed / Lapsed |