Method of making a solar cell having improved anti-reflection passivation layer
Assignee: Electric Power Research Institute
•
Filing: 1996-10-21
•
Granted: 1999-05-25
•
Expires: 2016-10-21
Abstract
Abstract A silicon solar cell has increased efficiency by providing an anti-reflection and passivation layer comprising a layer of silicon dioxide thermally grown on a surface of a silicon body and a layer of titanium dioxide deposited on the layer of silicon oxide. In fabricating the composite anti-reflection passivation layer, a layer of aluminum is first deposited on a surface of the thermally grown silicon oxide. After annealing the aluminum layer, the aluminum is removed from the silicon dioxide layer, and the layer of titanium dioxide is then deposited on the surface of the silicon dioxide from which the aluminum was removed. A layer of magnesium fluoride can be deposited on the surface of the titanium dioxide.
Inventors
- 👤 Richard M. Swanson
- 👤 Pierre J. Verlinden
- 👤 Ronald A. Sinton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:45
CPC Classifications
H; H10; H10F; H10F77/00; H10F77/30; H10F77/306; H10F77/311; H10F77/315; Y; Y02; Y02E; Y02E10/00; Y02E10/50
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
70 words
A method of fabricating an anti-reflection passivation layer on a surface of a silicon solar cell comprising the steps of: (a) forming a silicon dioxide layer on said surface, (b) depositing a layer of aluminum on said silicon dioxide layer, (c) annealing said layer of aluminum and said layer of silicon dioxide, (d) removing said aluminum layer, and (e) forming a layer of titanium dioxide on said silicon dioxide layer.
Claim 2
Independent Claim
70 words
A method of fabricating an anti-reflection passivation layer on a surface of a silicon solar cell comprising the steps of: (a) forming a silicon dioxide layer on said surface, (b) depositing a layer of aluminum on said silicon dioxide layer, (c) annealing said layer of aluminum and said layer of silicon dioxide, (d) removing said aluminum layer, and (e) forming a layer of titanium dioxide on said silicon dioxide layer.
Claim 3
Dependent Claim
23 words
The method as defined by claim 1, wherein step (b) includes depositing a layer of aluminum having a thickness of approximately 0.05 μm.
Claim 4
Dependent Claim
38 words
The method as defined by claim 2, wherein step (c) includes heating said silicon solar cell to a temperature of approximately 400° C. in nitrogen for 40 minutes followed by annealing in a forming gas for 10 minutes.
Claim 5
Dependent Claim
23 words
The method as defined by claim 1, wherein step (c) includes heating said silicon solar cell to a temperature at approximately 400° C.
Claim 6
Dependent Claim
20 words
The method as defined by claim 1 wherein step (a) includes thermally growing said silicon dioxide layer on said surface.
Claim 7
Dependent Claim
23 words
The method as defined by claim 5 wherein step (e) includes evaporatively depositing said layer of titanium dioxide on said silicon dioxide layer.
Claim 8
Dependent Claim
45 words
The method as defined by claim 6 wherein step (a) forms a silicon dioxide layer having a thickness in the range of 50 Å to 300 Å and, step (e) forms a layer of titanium dioxide having a thickness on the order of 500 Å.
Claim 9
Dependent Claim
26 words
The method as defined by claim 1 and further including the step of: (f) forming a layer of magnesium fluoride on said layer of titanium dioxide.
Claim 10
Dependent Claim
28 words
The method as defined by claim 8 wherein step (f) forms a layer of magnesium fluoride having a thickness in the range of 1300 Å to 1400 Å.
References Cited (Backward Citations)
US3614548A
Cited
US4239810A
Cited
US4389534A
Cited
JPS5922003A
Cited
US4479027A
Cited
US4492813A
Cited
US4735488A
Cited
US4642414A
Cited
US4612698A
Cited
US4830879A
Cited
JPS63119274A
Cited
US4940495A
Cited
US5010040A
Cited
US5030295A
Cited
US5106671A
Cited
US5338370A
Cited
US5261970A
Cited
US5321717A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-05-24 | 2002-11-23 | 2003-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-05-24 | 2006-11-23 | 2007-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-05-24 | 2010-11-23 | 2011-05-25 | $7700.00 | Window Closed / Lapsed |