US5851912A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Modified tungsten-plug contact process
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1997-03-10
•
Granted: 1998-12-22
•
Expires: 2017-03-10
Abstract
Abstract An method for the fabrication of an ohmic, low resistance contact to heavily doped silicon is described using a CVD deposited tungsten plug provided with Ti/TiN barrier metallurgy. The method provides for surface planarization using a borophosphosilicate glass insulator deposited on the silicon. After the glass is flowed to planarize its surface, contact holes are patterned in the glass and the exposed silicon substrate contacts are implanted. Instead of activating the implant with a rapid-thermal-anneal at this point the Ti/TiN barrier metallurgy is applied first followed by the anneal. This provides support for the glass at the upper corners of the contact opening during the anneal and thus prevents them from deforming and encroaching into the contact hole opening. By using the Ti/TiN metallurgy to support the glass, higher annealing temperatures are permitted, providing not only for adequate dopant activation but also for a lower contact resistance and improved bonding of the metallurgy to the silicate glass.
Inventors
- 👤 Jhon-Jhy Liaw
- 👤 Jin-Yuan Lee
- 👤 Ming-Chang Teng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 14:32
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10W20/033; H10W20/035; H10W20/056
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
173 words
A method of forming a void free tungsten plug to a silicon semiconductor device comprising: providing a semiconductor substrate; forming semiconductor devices within the surface of said semiconductor substrate; forming a layer of silicate glass, which is flowable within the temperature range of between about 800° and 900° C., over said semiconductor substrate; flowing said silicate glass by heating; depositing a photoresist layer over said layer of silicate glass; patterning said photoresist layer to define a contact hole opening; etching said layer of silicate glass with a unidirectional dry etching technique thereby forming a contact opening with a vertical walled profile; implanting dopant atoms into the contact opening; removing said photoresist layer; forming a titanium layer over said layer of silicate glass; forming a barrier metal layer over said titanium layer; subjecting said semiconductor substrate to rapid thermal annealing after said barrier metal layer has been formed whereby said vertical walled profile is sustained; depositing a tungsten layer over said semiconductor substrate; and etching said tungsten layer to form an isolated tungsten plug.
Claim 2
Independent Claim
173 words
A method of forming a void free tungsten plug to a silicon semiconductor device comprising: providing a semiconductor substrate; forming semiconductor devices within the surface of said semiconductor substrate; forming a layer of silicate glass, which is flowable within the temperature range of between about 800° and 900° C., over said semiconductor substrate; flowing said silicate glass by heating; depositing a photoresist layer over said layer of silicate glass; patterning said photoresist layer to define a contact hole opening; etching said layer of silicate glass with a unidirectional dry etching technique thereby forming a contact opening with a vertical walled profile; implanting dopant atoms into the contact opening; removing said photoresist layer; forming a titanium layer over said layer of silicate glass; forming a barrier metal layer over said titanium layer; subjecting said semiconductor substrate to rapid thermal annealing after said barrier metal layer has been formed whereby said vertical walled profile is sustained; depositing a tungsten layer over said semiconductor substrate; and etching said tungsten layer to form an isolated tungsten plug.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the layer of silicate glass is borophosphosilicate glass(BPSG) of approximately 5,000 to 15,000 Angstroms thickness.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the titanium layer is between 300 and 800 Angstroms thick.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein the barrier metal layer is titanium nitride(TiN) and is between 800 and 2,000 Angstroms thick.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein the barrier metal layer is TiW and is between 800 and 2,000 Angstroms thick.
Claim 7
Dependent Claim
25 words
The method of claim 1 wherein said rapid thermal annealing produces a surface temperature of between 900° C. and 1000° C. on said semiconductor substrate.
Claim 8
Independent Claim
248 words
A method of forming void free tungsten plug contacts to silicon semiconductor devices with both n and p type active areas on the same semiconductor substrate and providing connection from these active areas to a metallic interconnection network comprising: providing a semiconductor substrate; forming semiconductor devices with both n and p type active areas within the surface of said semiconductor substrate; forming a layer of silicate glass, which is flowable within the temperature range of between about 800° and 900° C., over said semiconductor substrate; flowing said layer of silicate glass by heating; depositing a first photoresist layer over said layer of silicate glass; patterning said first photoresist layer to define contact hole openings; etching said layer of silicate glass with a unidirectional dry etching technique thereby forming contact openings with an vertical walled profile; implanting a first dose of dopant atoms into the contact openings; depositing a second photoresist layer over said first photoresist layer; patterning said second photoresist layer to expose only the contact openings to n-type active areas; implanting a second dose of dopant atoms; removing said first photoresist layer and said second photoresist layer; forming a titanium layer over said layer of silicate glass; forming a barrier metal layer over said titanium layer; subjecting said semiconductor substrate to rapid thermal annealing after said barrier metal layer has been formed whereby said vertical walled profile is sustained; depositing a tungsten layer over said semiconductor substrate; and etching said tungsten layer to form tungsten plug contacts.
Claim 9
Independent Claim
248 words
A method of forming void free tungsten plug contacts to silicon semiconductor devices with both n and p type active areas on the same semiconductor substrate and providing connection from these active areas to a metallic interconnection network comprising: providing a semiconductor substrate; forming semiconductor devices with both n and p type active areas within the surface of said semiconductor substrate; forming a layer of silicate glass, which is flowable within the temperature range of between about 800° and 900° C., over said semiconductor substrate; flowing said layer of silicate glass by heating; depositing a first photoresist layer over said layer of silicate glass; patterning said first photoresist layer to define contact hole openings; etching said layer of silicate glass with a unidirectional dry etching technique thereby forming contact openings with an vertical walled profile; implanting a first dose of dopant atoms into the contact openings; depositing a second photoresist layer over said first photoresist layer; patterning said second photoresist layer to expose only the contact openings to n-type active areas; implanting a second dose of dopant atoms; removing said first photoresist layer and said second photoresist layer; forming a titanium layer over said layer of silicate glass; forming a barrier metal layer over said titanium layer; subjecting said semiconductor substrate to rapid thermal annealing after said barrier metal layer has been formed whereby said vertical walled profile is sustained; depositing a tungsten layer over said semiconductor substrate; and etching said tungsten layer to form tungsten plug contacts.
Claim 10
Dependent Claim
21 words
The method of claim 7 wherein the layer of silicate glass is borophosphosilicate glass(BPSG) of approximately 5,000 to 15,000 Angstroms thickness.
Claim 11
Dependent Claim
16 words
The method of claim 7 wherein the titanium layer is between 300 and 800 Angstroms thick.
Claim 12
Dependent Claim
21 words
The method of claim 7 wherein the barrier metal layer is titanium nitride(TiN) and is between 800 and 2,000 Angstroms thick.
Claim 13
Dependent Claim
20 words
The method of claim 7 wherein the barrier metal layer is TiW and is between 800 and 2,000 Angstroms thick.
Claim 14
Dependent Claim
25 words
The method of claim 7 wherein said rapid thermal annealing produces a surface temperature of between 900° C. and 1000° C. on said semiconductor substrate.
References Cited (Backward Citations)
US5422308A
Cited
US5102826A
Cited
US5302549A
Cited
US5238872A
Cited
US5322812A
Cited
US5227191A
Cited
US5272112A
Cited
US5364817A
Cited
US5510296A
Cited
US5554565A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-12-21 | 2002-06-22 | 2002-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-12-21 | 2006-06-22 | 2006-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-12-21 | 2010-06-22 | 2010-12-22 | $7700.00 | Window Closed / Lapsed |