Modified BP-TEOS tungsten-plug contact process
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1996-02-26
•
Granted: 1996-09-10
•
Expires: 2016-02-26
Abstract
Abstract An improved method for the fabrication of an ohmic, low resistance contact to heavily doped silicon is described using a CVD deposited tungsten plug provided with Ti/TiN barrier metallurgy. The method provides for surface planarizatiion by depositing first a layer of silicon oxide followed by a layer of borophosphosilicate glass onto a silicon wafer containing integrated circuit devices. After the glass is thermally flowed to planarize its surface, it is etched back to a suitable thickness and a second layer of silicon oxide is deposited over the now-planar surface. Contact holes are patterned in the composite silicon oxide-glass-silicon oxide structure and the exposed silicon device contacts are ion-implanted. The implant is then activated by rapid-thermal-annealing. The presence of the second silicon oxide layer prevents the upper corners of the contact openings from flowing and encroaching into the opening as would occur in its absence. Not only does this provide for void-free filling of the contact openings by the tungsten contact deposition but it also permits the use of higher temperatures for the implant anneal.
Inventors
- 👤 Jhon-Jhy Liaw
- 👤 Jin-Yuan Lee
- 👤 Ming-Chang Teng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:55
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/047; H10W20/056; H10W20/071; H10W20/081
Claims Analysis
Total Claims: 51
Claim 1
Independent Claim
227 words
A method of forming a contact to a silicon semiconductor device and providing connection to a metallic interconnection network comprising: providing a semiconductor wafer; forming semiconductor devices within the surface of said semiconductor wafer; forming a first layer of silicon oxide over said semiconductor devices; forming a layer of glass over said first layer of silicon oxide; flowing said layer of glass by heating; etching said layer of glass utilizing an anisotropic etching procedure; forming a second layer of silicon oxide over said layer of glass to form a composite dielectric sandwich comprising said first layer of silicon oxide, said layer of glass and said second layer of silicon oxide; depositing a layer of photoresist on said second layer of silicon oxide; patterning said photoresist to define contact hole openings; etching said composite dielectric sandwich with a unidirectional dry etching technique to provide vertical walled openings in said composite dielectric sandwich, exposing the subjacent contact regions of the semiconductor devices; implanting dopant atoms into the contact openings; removing said photoresist layer; subjecting said semiconductor wafer to a first rapid thermal annealing(RTA) to activate said implanted dopant atoms; forming a titanium layer over said semiconductor wafer; forming a metal barrier layer over said titanium layer; subjecting said semiconductor wafer to a second rapid thermal annealing(RTA); depositing a tungsten layer; and etching said tungsten layer to form tungsten plugs.
Claim 2
Independent Claim
227 words
A method of forming a contact to a silicon semiconductor device and providing connection to a metallic interconnection network comprising: providing a semiconductor wafer; forming semiconductor devices within the surface of said semiconductor wafer; forming a first layer of silicon oxide over said semiconductor devices; forming a layer of glass over said first layer of silicon oxide; flowing said layer of glass by heating; etching said layer of glass utilizing an anisotropic etching procedure; forming a second layer of silicon oxide over said layer of glass to form a composite dielectric sandwich comprising said first layer of silicon oxide, said layer of glass and said second layer of silicon oxide; depositing a layer of photoresist on said second layer of silicon oxide; patterning said photoresist to define contact hole openings; etching said composite dielectric sandwich with a unidirectional dry etching technique to provide vertical walled openings in said composite dielectric sandwich, exposing the subjacent contact regions of the semiconductor devices; implanting dopant atoms into the contact openings; removing said photoresist layer; subjecting said semiconductor wafer to a first rapid thermal annealing(RTA) to activate said implanted dopant atoms; forming a titanium layer over said semiconductor wafer; forming a metal barrier layer over said titanium layer; subjecting said semiconductor wafer to a second rapid thermal annealing(RTA); depositing a tungsten layer; and etching said tungsten layer to form tungsten plugs.
Claim 3
Dependent Claim
34 words
The method of claim 1 wherein the implanted dopant atoms are at a dosage of between about 2×10 14 to 2×10 15 atoms/cm 2 and are implanted at energies between 30 and 100 keV.
Claim 4
Dependent Claim
11 words
The method of claim 1 wherein the semiconductor wafer is p-type.
Claim 5
Dependent Claim
12 words
The method of claim 3 wherein the implanted dopant atoms are phosphorous.
Claim 6
Dependent Claim
11 words
The method of claim 1 wherein the semiconductor wafer is n-type.
Claim 7
Dependent Claim
17 words
The method of claim 5 wherein the implanted dopant atoms are boron as BF 2 + .
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein the first silicon oxide layer is between about 1000 and 2000 Angstroms thick.
Claim 9
Dependent Claim
20 words
The method of claim 1 wherein the first silicon oxide layer is deposited by the thermal decomposition of tetraethyl orthosilicate.
Claim 10
Dependent Claim
22 words
The method of claim 1 wherein the first silicon oxide layer is deposited at a temperature between 300° C. and 700° C.
Claim 11
Dependent Claim
20 words
The method of claim 1 wherein the glass is borophosphosilicate glass(BPSG) of between about 5,000 to 15,000 Angstroms in thickness.
Claim 12
Dependent Claim
20 words
The method of claim 1 wherein the glass is phosphosilicate glass(PSG) of between about 5,000 to 5,000 Angstroms in thickness.
Claim 13
Dependent Claim
22 words
The method of claim 1 wherein the second silicon oxide layer is deposited by PECVD from the thermal decomposition of tetraethyl orthosilicate.
Claim 14
Dependent Claim
33 words
The method of claim 1 wherein the second silicon oxide layer is deposited by PECVD from the reaction of silane with a gas selected from the group consisting of oxygen and nitrous oxide.
Claim 15
Dependent Claim
22 words
The method of claim 1 wherein the second silicon oxide layer is deposited at a temperature between 300° C. and 700° C.
Claim 16
Dependent Claim
22 words
The method of claim 1 wherein the second silicon oxide layer is deposited to thickness of between about 1,000 and 3,000 Angstroms.
Claim 17
Dependent Claim
19 words
The method of claim 1 wherein the glass is flowed at a temperature between 800° C. and 900° C.
Claim 18
Dependent Claim
31 words
The method of claim 1 wherein the unidirectional etching technique is reactive-ion-etching using tetrafluoromethane and etching parameters to provide vertical sidewalls, a high silicon-to-oxide etch rate ratio, and precise end-point control.
Claim 19
Dependent Claim
21 words
The method of claim 1 wherein the glass is etched back to a thickness of between about 4,000 and 7,000 Angstroms.
Claim 20
Dependent Claim
17 words
The method of claim 1 wherein the titanium layer is between about 300 and 800 Angstroms thick.
Claim 21
Dependent Claim
22 words
The method of claim 1 wherein the barrier metal layer is titanium nitride(TiN) and is between about 800 and 2,000 Angstroms thick.
Claim 22
Dependent Claim
20 words
The method of claim 1 wherein the barrier metal is TiW and is between about 800 and 2,000 Angstroms thick.
Claim 23
Dependent Claim
42 words
The method of claim 1 wherein the first rapid thermal annealing and the second rapid thermal annealing are accomplished in a nitrogen ambient using a halogen lamp as a heat source and lasting for a period of between 20 and 30 seconds.
Claim 24
Dependent Claim
23 words
The method of claim 1 wherein the first rapid thermal annealing temperature of the wafer surface is between 900° C. and 1000° C.
Claim 25
Dependent Claim
23 words
The method of claim 1 wherein the second rapid thermal annealing temperature of the wafer surface is between 600° C. and 700° C.
Claim 26
Dependent Claim
36 words
The method of claim 1 wherein the tungsten layer is deposited at a temperature between 415° C. to 500° C. in a cold walled, low temperature CVD system by the reduction of WF 6 with hydrogen.
Claim 27
Independent Claim
304 words
A method of forming contacts to silicon semiconductor devices with both n and p type diffusions on the same semiconductor substrate and providing connection from these contacts to a metallic interconnection network comprising: providing a semiconductor wafer; forming semiconductor devices with both n and p type active areas within the surface of said semiconductor wafer; forming a first layer of silicon oxide over said semiconductor devices; forming a layer of glass over said first layer of silicon oxide; flowing said layer of glass by heating; etching said layer of glass utilizing an anisotropic etching procedure; forming a second layer of silicon oxide over said layer of glass to form a composite dielectric sandwich comprising said first layer of silicon oxide, said layer of glass and said second layer of silicon oxide and further comprising; depositing a layer of photoresist on said second layer of silicon oxide; patterning said photoresist to define contact hole openings; etching said composite dielectric sandwich with a unidirectional dry etching technique to provide vertical walled openings in said composite dielectric sandwich, exposing the subjacent contact regions of the semiconductor devices; implanting a first dose of p-type dopant atoms into the contact openings; depositing a second layer of photoresist over said first layer of photoresist; patterning said second layer of photoresist to expose only the contact openings to n-type contact areas; implanting a second dose of n-type dopant atoms into said exposed n-type contact openings; removing said first and second photoresist layers; subjecting said semiconductor wafer to a first rapid thermal annealing(RTA) to activate said n-type and said p-type dopant atoms; forming a titanium layer over said semiconductor wafer; forming a metal barrier layer over said titanium layer; subjecting said semiconductor wafer to a second rapid thermal annealing(RTA); depositing a tungsten layer; and etching said tungsten layer to form tungsten plugs.
Claim 28
Independent Claim
304 words
A method of forming contacts to silicon semiconductor devices with both n and p type diffusions on the same semiconductor substrate and providing connection from these contacts to a metallic interconnection network comprising: providing a semiconductor wafer; forming semiconductor devices with both n and p type active areas within the surface of said semiconductor wafer; forming a first layer of silicon oxide over said semiconductor devices; forming a layer of glass over said first layer of silicon oxide; flowing said layer of glass by heating; etching said layer of glass utilizing an anisotropic etching procedure; forming a second layer of silicon oxide over said layer of glass to form a composite dielectric sandwich comprising said first layer of silicon oxide, said layer of glass and said second layer of silicon oxide and further comprising; depositing a layer of photoresist on said second layer of silicon oxide; patterning said photoresist to define contact hole openings; etching said composite dielectric sandwich with a unidirectional dry etching technique to provide vertical walled openings in said composite dielectric sandwich, exposing the subjacent contact regions of the semiconductor devices; implanting a first dose of p-type dopant atoms into the contact openings; depositing a second layer of photoresist over said first layer of photoresist; patterning said second layer of photoresist to expose only the contact openings to n-type contact areas; implanting a second dose of n-type dopant atoms into said exposed n-type contact openings; removing said first and second photoresist layers; subjecting said semiconductor wafer to a first rapid thermal annealing(RTA) to activate said n-type and said p-type dopant atoms; forming a titanium layer over said semiconductor wafer; forming a metal barrier layer over said titanium layer; subjecting said semiconductor wafer to a second rapid thermal annealing(RTA); depositing a tungsten layer; and etching said tungsten layer to form tungsten plugs.
Claim 29
Dependent Claim
19 words
The method of claim 26 wherein said first dose of dopant atoms are boron as BF 2 + .
Claim 30
Dependent Claim
14 words
The method of claim 26 wherein said second dose of dopant atoms are phosphorous.
Claim 31
Dependent Claim
28 words
The method of claim 26 wherein said first dose of dopant atoms is between 2'10 14 to 5×10 - atoms/cm 2 at energies between 30 and 100 keV.
Claim 32
Dependent Claim
28 words
The method of claim 26 wherein said second dose of dopant atoms is between 1×10 15 to 2×10 15 atoms/cm 2 at energies between 30 and 100 keV.
Claim 33
Dependent Claim
19 words
The method of claim 26 wherein said first silicon oxide layer is between about 1,000 and 2,000 Angstroms thick.
Claim 34
Dependent Claim
20 words
The method of claim 26 wherein said first silicon oxide layer is deposited by the thermal decomposition of tetraethyl orthosilicate.
Claim 35
Dependent Claim
22 words
The method of claim 26 wherein the first silicon oxide layer is deposited at a temperature between 300° C. and 700° C.
Claim 36
Dependent Claim
19 words
The method of claim 26 wherein the glass is borophosphosilicate glass(BPSG) of between about 5,000 to 15,000 Angstroms thickness.
Claim 37
Dependent Claim
19 words
The method of claim 26 wherein the glass is phosphosilicate glass(PSG) of between about 5,000 to 15,000 Angstroms thickness.
Claim 38
Dependent Claim
22 words
The method of claim 26 wherein the second silicon oxide layer is deposited by PECVD from the thermal decomposition of tetraethyl orthosilicate.
Claim 39
Dependent Claim
33 words
The method of claim 26 wherein the second silicon oxide layer is deposited by PECVD from the reaction of silane with a gas selected from the group consisting of oxygen and nitrous oxide.
Claim 40
Dependent Claim
22 words
The method of claim 26 wherein the second silicon oxide layer is deposited at a temperature between 300° C. and 700° C.
Claim 41
Dependent Claim
22 words
The method of claim 26 wherein the second silicon oxide layer is deposited to thickness of between about 1,000 and 3,000 Angstroms.
Claim 42
Dependent Claim
19 words
The method of claim 26 wherein the glass is flowed at a temperature between 800° C. and 900° C.
Claim 43
Dependent Claim
31 words
The method of claim 26 wherein the unidirectional etching technique is reactive-ion-etching using tetrafluoromethane and conditions conducive to provide vertical sidewalls, a high silicon-to-oxide etch rate ratio, and precise end-point control.
Claim 44
Dependent Claim
21 words
The method of claim 26 wherein the glass is etched back to a thickness of between about 4,000 and 7,000 Angstroms.
Claim 45
Dependent Claim
17 words
The method of claim 26 wherein the titanium layer is between about 300 and 800 Angstroms thick.
Claim 46
Dependent Claim
22 words
The method of claim 26 wherein the barrier metal layer is titanium nitride(TiN) and is between about 800 and 2,000 Angstroms thick.
Claim 47
Dependent Claim
20 words
The method of claim 26 wherein the barrier metal is TiW and is between about 800 and 2,000 Angstroms thick.
Claim 48
Dependent Claim
42 words
The method of claim 26 wherein the first rapid thermal annealing and the second rapid thermal annealing are accomplished in a nitrogen ambient using a halogen lamp as a heat source and lasting for a period of between 20 and 30 seconds.
Claim 49
Dependent Claim
23 words
The method of claim 26 wherein the first rapid thermal annealing temperature of the wafer surface is between 900° C. and 1000° C.
Claim 50
Dependent Claim
23 words
The method of claim 26 wherein the second rapid thermal annealing temperature of the wafer surface is between 600° C. and 700° C.
Claim 51
Dependent Claim
36 words
The method of claim 26 wherein the tungsten layer is deposited at a temperature between 415° C. to 500° C. in a cold walled, low temperature CVD system by the reduction of WF 6 with hydrogen.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1999-09-10 | 2000-03-11 | 2000-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2003-09-10 | 2004-03-11 | 2004-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2007-09-10 | 2008-03-11 | 2008-09-10 | $7700.00 | Window Closed / Lapsed |