US5851302A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for dry etching sidewall polymer
Assignee: United Microelectronics Corp
•
Filing: 1997-02-19
•
Granted: 1998-12-22
•
Expires: 2017-02-19
Abstract
Abstract A method of plasma etching photoresist and sidewall polymer with an etch gas mixture comprising CF 4 and H 2 O demonstrating very aggressive ashrate of photoresist but maintains an exceptionally low etch rate for titanium nitride and other metals is provided. The very low TiN etch rate permits the inventive method to effectively breakdown sidewall polymer without removing any significant amount of these metals. The invention is particularly suited for stripping sidewall polymer from etched via holes and from etched metal lines.
Inventors
- 👤 Ramiro Solis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:57
CPC Classifications
H; H10; H10P; H10P70/00; H10P70/20; H10P70/27; H10P70/273; G; G03; G03F; G03F7/00; G03F7/26; G03F7/36; G03F7/42; G03F7/427; H10P50/00; H10P50/20; H10P50/28; H10P50/286; H10P50/287; H10P70/23; H10P70/234; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/081
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
128 words
A method of removing polymer from a semiconductor wafer which includes a multilayer metal structure on the wafer that comprises a first metal layer, a second metal layer, and optionally, a third metal layer that is a barrier layer which presents diffusion of second metal into the wafer, said method comprising the steps of: (a) positioning said wafer into a chamber wherein the wafer includes polymer that is adjacent to the multilayer metal structure; (b) introducing etchant gases comprising CF 4 and H 2 O into the chamber; (c) applying energy to the etchant gases to generate a plasma; and (d) etching the polymer, wherein the ratio of the etch rate for polymer to the etch rate for the multilayer metal structure is at least 5 to 1.
Claim 2
Independent Claim
128 words
A method of removing polymer from a semiconductor wafer which includes a multilayer metal structure on the wafer that comprises a first metal layer, a second metal layer, and optionally, a third metal layer that is a barrier layer which presents diffusion of second metal into the wafer, said method comprising the steps of: (a) positioning said wafer into a chamber wherein the wafer includes polymer that is adjacent to the multilayer metal structure; (b) introducing etchant gases comprising CF 4 and H 2 O into the chamber; (c) applying energy to the etchant gases to generate a plasma; and (d) etching the polymer, wherein the ratio of the etch rate for polymer to the etch rate for the multilayer metal structure is at least 5 to 1.
Claim 3
Dependent Claim
31 words
The method of claim 1 wherein the ratio of the H 2 O flow rate to the CF 4 flow rate into the chamber is at least about 2.5 to 1.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein the polymer is etched at a rate of at least about 5000 Å per minute.
Claim 5
Dependent Claim
48 words
The method of claim 1 wherein the first metal layer and third metal layer each comprises material that is selected from the group consisting of Ti, W, TiN, and TiW, and the second metal layer comprises material that is selected from the group consisting of aluminum and AlCu.
Claim 6
Dependent Claim
17 words
The method of claim 1 wherein the first metal layer and third metal layer each comprises TiN.
Claim 7
Independent Claim
112 words
A method of removing post etch polymer residue from a semiconductor device containing a metal layer that is formed of material that is selected from the group consisting of Ti, W, TiN, and TiW and wherein the metal layer is adjacent to the polymer residue, said method comprising the steps of: (a) positioning said semiconductor device into a chamber; (b) introducing etchant gases consisting essentially of CF 4 and H 2 O into the chamber; (c) applying energy to the etchant gases; and (d) etching the polymer residue wherein the ratio of the etch rate for residue polymer to the etch rate for the metal layer is at least 5 to 1.
Claim 8
Independent Claim
112 words
A method of removing post etch polymer residue from a semiconductor device containing a metal layer that is formed of material that is selected from the group consisting of Ti, W, TiN, and TiW and wherein the metal layer is adjacent to the polymer residue, said method comprising the steps of: (a) positioning said semiconductor device into a chamber; (b) introducing etchant gases consisting essentially of CF 4 and H 2 O into the chamber; (c) applying energy to the etchant gases; and (d) etching the polymer residue wherein the ratio of the etch rate for residue polymer to the etch rate for the metal layer is at least 5 to 1.
Claim 9
Dependent Claim
31 words
The method of claim 6 wherein the ratio of the H 2 O flow rate to the fluorine-containing compound flow rate into the chamber is at least about 2.5 to 1.
Claim 10
Dependent Claim
28 words
The method of claim 6 wherein the ratio of the etch rate for residue polymer to the etch rate for metal layer is at least 5 to 1.
Claim 11
Dependent Claim
22 words
The method of claim 6 wherein the residue polymer is etched at a rate of at least about 5000 Å per minute.
Claim 12
Independent Claim
181 words
A method of forming a via contact hole in a semiconductor device that comprises the steps of: (a) forming a metal structure on a wafer wherein the metal structure comprises a first metal layer and a second metal layer that is underneath the first metal layer; (b) forming a dielectric layer on said first metal layer; (c) forming a photoresist pattern after a photoresist layer is coated on said dielectric layer; (d) forming a via contact hole by an etching process employing said photoresist pattern as a mask; and (e) removing a layer of polymer on said via contact hole and at least a part of said photoresist layer by a process comprising the steps of: (i) positioning said semiconductor device comprising said via contact hole into a chamber; (ii) introducing etchant gases comprising CF 4 and H 2 O into the chamber; (iii) applying energy to the etchant gases generate a plasma; and (iv) etching the polymer wherein the ratio of the etch rate for polymer to the etch rate for the capping metal is at least 5 to 1.
Claim 13
Independent Claim
181 words
A method of forming a via contact hole in a semiconductor device that comprises the steps of: (a) forming a metal structure on a wafer wherein the metal structure comprises a first metal layer and a second metal layer that is underneath the first metal layer; (b) forming a dielectric layer on said first metal layer; (c) forming a photoresist pattern after a photoresist layer is coated on said dielectric layer; (d) forming a via contact hole by an etching process employing said photoresist pattern as a mask; and (e) removing a layer of polymer on said via contact hole and at least a part of said photoresist layer by a process comprising the steps of: (i) positioning said semiconductor device comprising said via contact hole into a chamber; (ii) introducing etchant gases comprising CF 4 and H 2 O into the chamber; (iii) applying energy to the etchant gases generate a plasma; and (iv) etching the polymer wherein the ratio of the etch rate for polymer to the etch rate for the capping metal is at least 5 to 1.
Claim 14
Dependent Claim
27 words
The method of claim 10 wherein the ratio of the etch rate for sidewall polymer to the etch rate for metal is at least 5 to 1.
Claim 15
Dependent Claim
21 words
The method of claim 10 wherein the polymer is etched at a rate of at least about 5000 Å per minute.
Claim 16
Dependent Claim
24 words
The method of claim 10 wherein the first metal is material that is selected from the group consisting of TiN, TiW, Ti and W.
Claim 17
Dependent Claim
12 words
The method of claim 10 wherein the first metal layer is TiN.
Claim 18
Dependent Claim
17 words
The method of claim 10 wherein the second conductor metal layer is selected from aluminum and AlCu.
Claim 19
Dependent Claim
18 words
The method of claim 1 wherein the etchant gases consist essentially of CF 4 and H 2 O.
Claim 20
Dependent Claim
31 words
The method of claim 5 wherein the ratio of the H 2 O flow rate to the CF 4 flow rate into the chamber is at least about 2.5 to 1.
Claim 21
Dependent Claim
52 words
The method of claim 5 wherein the ratio of the etch rate for polymer to the etch rate for the capping metal layer is at least 50 to 1 and the ratio of the etch rate for polymer to the etch rate for barrier metal layer is at least 50 to 1.
Claim 22
Dependent Claim
18 words
The method of claim 5 wherein the etchant gases consist essentially of CF 4 and H 2 O.
Claim 23
Dependent Claim
28 words
The method of claim 6 wherein the ratio of the etch rate for residue polymer to the etch rate for metal layer is at least 50 to 1.
Claim 24
Dependent Claim
18 words
The method of claim 10 wherein the etchant gases consist essentially of CF 4 and H 2 O.
Claim 25
Dependent Claim
31 words
The method of claim 21 wherein the ratio of the H 2 O flow rate to the CF 4 flow rate into the chamber is at least about 2.5 to 1.
Claim 26
Dependent Claim
28 words
The method of claim 10 wherein the ratio of the etch rate for polymer to the etch rate for first metal layer is at least 5 to 1.
Claim 27
Dependent Claim
29 words
The method of claim 10 wherein the ratio of the etch rate for polymer to the etch rate for the first metal layer is at least 50 to 1.
References Cited (Backward Citations)
US4123841A
Cited
US4514254A
Cited
US4670091A
Cited
US4897153A
Cited
US5077598A
Cited
US5578163A
Cited
US5451291A
Cited
US5348619A
Cited
US5382316A
Cited
US5358602A
Cited
US5485304A
Cited
US5497262A
Cited
US5512507A
Cited
US5526951A
Cited
US5521104A
Cited
US5573971A
Cited
US5661083A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-12-21 | 2002-06-22 | 2002-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-12-21 | 2006-06-22 | 2006-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-12-21 | 2010-06-22 | 2010-12-22 | $7700.00 | Window Closed / Lapsed |