Method for producing low scatter, low loss, environmentally stable dielectric coatings
Assignee: Newport Corp USA
•
Filing: 1997-05-27
•
Granted: 1998-12-15
•
Expires: 2017-05-27
Abstract
Abstract A method for creating a dielectric coating on a substrate produces near bulk density metal oxide coatings with extremely low surface roughness, microstructure and low defect density. The coatings have a low scatter of less than 50 ppm, low loss of less than 100 ppm, and an environmental stability of 0.1 or less spectral shift. A high vacuum chamber is provided which includes a substrate carrier device, an electron beam gun, a substrate, an evaporant source of coating material, a plasma bridge neutralizer and an ion gun. Coating material is evaporated with the electron beam gun to form a coating material evaporant that is directed to the substrate. An ion gun is directed toward the substrate and produces ions that arrive substantially simultaneously with the coating material evaporant at the substrate. The ions provide a momentum assist to the coating material. The result is a formation of a desirable dielectric thin film of coating material on the substrate.
Inventors
- 👤 Hakchu Lee
- 👤 Ronald Kubota
- 👤 Larry Basegio
- 👤 Marc Kevin von Gunten
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:10
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/02; C23C14/021; C23C14/022; C23C14/22
Claims Analysis
Total Claims: 42
Claim 1
Independent Claim
134 words
A method for coating a substrate with a dielectric coating material, comprising; providing a high vacuum chamber including a substrate carrier device, an electron beam gun, the substrate, an evaporant source of the dielectric coating material and an ion gun; evaporating the dielectric coating material with the electron beam gun to form a dielectric coating material evaporant that is directed to the substrate; directing the ion gun toward the substrate and producing ions that arrive substantially simultaneously with the dielectric coating material evaporant at the substrate, the ions providing a momentum assist to the dielectric coating material evaporant; and forming a dielectric optical coating on the substrate at a deposition rate less than or equal to about 2.3 Angstroms per second so the coating has a low optical loss of 100 ppm or less.
Claim 2
Independent Claim
134 words
A method for coating a substrate with a dielectric coating material, comprising; providing a high vacuum chamber including a substrate carrier device, an electron beam gun, the substrate, an evaporant source of the dielectric coating material and an ion gun; evaporating the dielectric coating material with the electron beam gun to form a dielectric coating material evaporant that is directed to the substrate; directing the ion gun toward the substrate and producing ions that arrive substantially simultaneously with the dielectric coating material evaporant at the substrate, the ions providing a momentum assist to the dielectric coating material evaporant; and forming a dielectric optical coating on the substrate at a deposition rate less than or equal to about 2.3 Angstroms per second so the coating has a low optical loss of 100 ppm or less.
Claim 3
Dependent Claim
22 words
The method of claim 1, wherein a plurality of dielectric thin films of the dielectric coating material is formed on the substrate.
Claim 4
Dependent Claim
19 words
The method of claim 1, further comprising: controlling a stoichiometry of the dielectric optical coating formed on the substrate.
Claim 5
Dependent Claim
28 words
The method of claim 1, further comprising: controlling an ion/dielectric coating material evaporant arrival ratio at the substrate to create a desired density of the dielectric optical coating.
Claim 6
Dependent Claim
23 words
The method of claim 1, wherein an energy of the dielectric coating evaporant material deposited on the substrate is greater than 5 eV.
Claim 7
Dependent Claim
23 words
The method of claim 1, wherein an energy of the dielectric coating material evaporant deposited on the substrate is greater than 7.5 eV.
Claim 8
Dependent Claim
23 words
The method of claim 1, wherein an energy of the dielectric coating material evaporant deposited on the substrate is greater than 9.0 eV.
Claim 9
Dependent Claim
23 words
The method of claim 1, wherein an energy of the dielectric coating material evaporant deposited on the substrate is 10.0 eV or greater.
Claim 10
Dependent Claim
20 words
The method of claim 1, wherein the dielectric optical coating has a low optical scatter of less than 50 ppm.
Claim 11
Dependent Claim
28 words
The method of claim 1, wherein the ion gun produces positively charged particles along a longitudinal axis of the ion gun at an exterior of the ion gun.
Claim 12
Dependent Claim
49 words
The method of claim 10, wherein the high vacuum chamber includes a plasma beam neutralizer that produces a plurality of electrons which mix with the positively charged particles along the longitudinal axis of the ion gun at the exterior of the ion gun, producing a beam of flowing plasma.
Claim 13
Dependent Claim
16 words
The method of claim 11, wherein the plasma beam neutralizer is a filamentless plasma bridge neutralizer.
Claim 14
Dependent Claim
15 words
The method of claim 1, wherein the ion gun is a cold cathode ion gun.
Claim 15
Dependent Claim
13 words
The method of claim 1, wherein the dielectric coating material is an oxide.
Claim 16
Dependent Claim
55 words
The method of claim 14, wherein the oxide is selected from the group, SiO 2 , HfO 2 , Ta 2 O 5 , ZrO 2 , TiO 2 ,, Nb 2 O 5 , Y 2 O 3 , Al 2 O 3 , Se 2 O 3 , BeO and Gd 2 O.
Claim 17
Dependent Claim
14 words
The method of claim 1, wherein the dielectric coating material is a metal fluoride.
Claim 18
Dependent Claim
14 words
The method of claim 1, wherein the dielectric coating material is a metal carbide.
Claim 19
Dependent Claim
14 words
The method of claim 1, wherein the dielectric coating material is a metal nitride.
Claim 20
Dependent Claim
20 words
The method of claim 1, wherein the deposition rate is less than or equal to about 0.5 angstroms per second.
Claim 21
Dependent Claim
20 words
The method of claim 1, wherein the deposition rate is less than or equal to about 0.3 angstroms per second.
Claim 22
Independent Claim
187 words
A method for coating a substrate with a dielectric coating material, comprising: providing a high vacuum chamber including a substrate carrier device, an electron beam gun, the substrate, an evaporant source of the dielectric coating material, a plasma beam neutralizer that produces a plurality of electrons and an ion gun producing positively charged particles along a longitudinal axis of the ion gun; positioning the plasma beam neutralizer adjacent to and in a lateral direction relative to the ion gun longitudinal axis; generating the plurality of electrons from the plasma beam neutralizer which mix with the positively charged particles along the longitudinal axis of the ion gun, producing a beam of flowing plasma; evaporating the dielectric coating material with the electron beam gun to form a dielectric coating material evaporant that is directed to the substrate; providing a momentum assist from the beam of flowing plasma to the dielectric coating material evaporant; and forming a dielectric optical coating on the substrate at a deposition rate less than or equal to about 2.3 Angstroms per second so the coating has a low optical loss of 100 ppm or less.
Claim 23
Independent Claim
187 words
A method for coating a substrate with a dielectric coating material, comprising: providing a high vacuum chamber including a substrate carrier device, an electron beam gun, the substrate, an evaporant source of the dielectric coating material, a plasma beam neutralizer that produces a plurality of electrons and an ion gun producing positively charged particles along a longitudinal axis of the ion gun; positioning the plasma beam neutralizer adjacent to and in a lateral direction relative to the ion gun longitudinal axis; generating the plurality of electrons from the plasma beam neutralizer which mix with the positively charged particles along the longitudinal axis of the ion gun, producing a beam of flowing plasma; evaporating the dielectric coating material with the electron beam gun to form a dielectric coating material evaporant that is directed to the substrate; providing a momentum assist from the beam of flowing plasma to the dielectric coating material evaporant; and forming a dielectric optical coating on the substrate at a deposition rate less than or equal to about 2.3 Angstroms per second so the coating has a low optical loss of 100 ppm or less.
Claim 24
Dependent Claim
22 words
The method of claim 2, wherein a plurality of dielectric thin films of the dielectric coating material is formed on the substrate.
Claim 25
Dependent Claim
19 words
The method of claim 21, further comprising: controlling a stoichiometry of the dielectric optical coating formed on the substrate.
Claim 26
Dependent Claim
19 words
The method of claim 21, further comprising: controlling in the plasma an arrival ratio of electrons/dielectric coating material evaporant.
Claim 27
Dependent Claim
26 words
The method of claim 21, wherein the beam of flowing plasma increases an energy of the dielectric coating material evaporant deposited as the dielectric optical coating.
Claim 28
Dependent Claim
24 words
The method of claim 21, wherein an energy of the dielectric coating material evaporant deposited on the substrate is greater than b 5 eV.
Claim 29
Dependent Claim
23 words
The method of claim 21, wherein an energy of the dielectric coating material evaporant deposited on the substrate is greater than 7.5 eV.
Claim 30
Dependent Claim
23 words
The method of claim 21, wherein an energy of the dielectric coating material evaporant deposited on the substrate is greater than 9.0 eV.
Claim 31
Dependent Claim
23 words
The method of claim 21, wherein an energy of the dielectric coating material evaporant deposited on the substrate is 10.0 eV or greater.
Claim 32
Dependent Claim
20 words
The method of claim 21, wherein the dielectric optical coating has a low optical scatter of less than 50 ppm.
Claim 33
Dependent Claim
29 words
The method of claim 21, wherein the ion gun produces the positively charged particles along the longitudinal axis of the ion gun at an exterior of the ion gun.
Claim 34
Dependent Claim
16 words
The method of claim 21, wherein the plasma beam neutralizer is a filamentless plasma bridge neutralizer.
Claim 35
Dependent Claim
15 words
The method of claim 21, wherein the ion gun is a cold cathode ion source.
Claim 36
Dependent Claim
13 words
The method of claim 21, wherein the dielectric coating material is an oxide.
Claim 37
Dependent Claim
72 words
The method of claim 34, wherein the oxide is selected from the group, SiO 2 , HfO 2 , Ta 2 O 5 , ZrO 2 , TiO 2 , SiO 2 , HfO 2 , Ta 2 O 5 , ZrO 2 , TiO 2 ,, Nb 2 O 5 , Y 2 O 3 , Al 2 O 3 , Se 2 O 3 , BeO and Gd 2 O.
Claim 38
Dependent Claim
14 words
The method of claim 21, wherein the dielectric coating material is a metal fluoride.
Claim 39
Dependent Claim
14 words
The method of claim 21, wherein the dielectric coating material is a metal carbide.
Claim 40
Dependent Claim
14 words
The method of claim 21, wherein the dielectric coating material is a metal nitride.
Claim 41
Dependent Claim
20 words
The method of claim 21, wherein the deposition rate is less than or equal to about 0.5 angstroms per second.
Claim 42
Dependent Claim
20 words
The method of claim 21, wherein the deposition rate is less than or equal to about 0.3 angstroms per second.
References Cited (Backward Citations)
US4201798A
Cited
US4310614A
Cited
US4381453A
Cited
US4541890A
Cited
US4440108A
Cited
US4617192A
Cited
US4634600A
Cited
US4490229A
Cited
US4652795A
Cited
US4877504A
Cited
US4759948A
Cited
US4997673A
Cited
US4800100A
Cited
US5098736A
Cited
US4948626A
Cited
US4925700A
Cited
US5053245A
Cited
US5227363A
Cited
US5597622A
Cited
US5240583A
Cited
US5340607A
Cited
US5274661A
Cited
US5415756A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-12-14 | 2002-06-15 | 2002-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-12-14 | 2006-06-15 | 2006-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-12-14 | 2010-06-15 | 2010-12-15 | $7700.00 | Window Closed / Lapsed |