Method for making a moisture resistant semiconductor device having an organic substrate
Assignee: NXP USA Inc
•
Filing: 1995-11-02
•
Granted: 1998-05-26
•
Expires: 2015-11-02
Abstract
Abstract A method for making moisture resistant semiconductor devices having organic substrates targets each of the potentially critical interfaces within a semiconductor device having the potential for delamination and cracking. An organic substrate (110) is designed to include a solid pad (116) having a chemically created oxide layer (118) formed thereon. A silicone-based die attach material (108) is dispensed and gelled very soon after dispensing to prevent excessive bleed. A semiconductor die (102) is mounted to the substrate after undergoing a cleaning operation to remove contaminants from the backside of the die. Prior to molding compound encapsulation and subsequent to die attach material cure, the substrate is cleaned to improve adhesion to the die attach material fillet (122). In practicing these operations, the following interfaces are targeted and their adhesion characteristics are improved: die attach material to die pad; die attach material to die; molding compound to die pad; and molding compound to die attach material.
Inventors
- 👤 Howard M. Berg
- 👤 Sankaranarayanan Ganesan
- 👤 Gary L. Lewis
- 👤 George W. Hawkins
- 👤 James W. Sloan
- 👤 Scott C. Bolton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 16:32
CPC Classifications
H; H10; H10W; H10W74/00; H10W74/10; H10W74/111; H10W74/114; H10W74/117; H10W70/00; H10W70/60; H10W70/62; H10W70/65; H10W70/654; H10W70/655; H10W70/656; H10W72/00; H10W72/071; H10W72/073; H10W72/07351; H10W72/07353; H10W72/075; H10W72/30; H10W72/331; H10W72/334; H10W72/50; H10W72/531; H10W72/536; H10W72/5363; H10W72/851; H10W72/874; H10W72/884; H10W72/90; H10W72/931; H10W72/951; H10W72/952; H10W90/00; H10W90/701; H10W90/731; H10W90/734; H10W90/751; H10W90/754
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
130 words
A method for making a moisture resistant semiconductor device comprising the steps of: providing an organic substrate having a top surface, a bottom surface, a plurality of conductive traces terminating into a plurality of bonding pads on the top surface, a die receiving pad on the top surface, and a chemically created oxide layer on the die receiving pad; dispensing a silicone-based die attach material on the chemically created oxide layer of the die receiving pad; providing a semiconductor die placing the semiconductor die on the silicone-based die attach material within the die receiving area; curing the silicone-based die attach material; electrically coupling the semiconductor die to the plurality of bonding pads; and encapsulating the semiconductor die and portions of the top surface of the organic substrate with a plastic.
Claim 2
Independent Claim
130 words
A method for making a moisture resistant semiconductor device comprising the steps of: providing an organic substrate having a top surface, a bottom surface, a plurality of conductive traces terminating into a plurality of bonding pads on the top surface, a die receiving pad on the top surface, and a chemically created oxide layer on the die receiving pad; dispensing a silicone-based die attach material on the chemically created oxide layer of the die receiving pad; providing a semiconductor die placing the semiconductor die on the silicone-based die attach material within the die receiving area; curing the silicone-based die attach material; electrically coupling the semiconductor die to the plurality of bonding pads; and encapsulating the semiconductor die and portions of the top surface of the organic substrate with a plastic.
Claim 3
Dependent Claim
70 words
The method of claim 1 wherein the step of providing an organic substrate comprises providing an organic substrate wherein the plurality of conductive traces, the plurality of bonding pads and the die receiving pad comprise copper, wherein the plurality of conductive traces further comprises a plating layer, and wherein the chemically created oxide layer is formed on the die receiving pad without being formed on the plurality of bonding pads.
Claim 4
Dependent Claim
29 words
The method of claim 1 wherein the step of providing an organic substrate comprises providing an organic substrate wherein the chemically created oxide layer is a cuprous oxide layer.
Claim 5
Dependent Claim
29 words
The method of claim 1 wherein the step of providing an organic substrate comprises providing an organic substrate wherein the chemically created oxide layer is a cupric oxide layer.
Claim 6
Dependent Claim
25 words
The method of claim 1 further comprising the step of gelling the silicone-based die attach material within three minutes after dispensing to prevent excessive bleed.
Claim 7
Dependent Claim
75 words
The method of claim 1 wherein the step of providing an organic substrate comprises providing an organic substrate wherein the die receiving pad has a quadrangle shape and is a solid metal pattern where the top surface of the organic substrate is continuous, and wherein the step of placing the semiconductor die comprises placing the semiconductor die so that the top surface of the organic substrate, where continuous, is fully metallized beneath the semiconductor die.
Claim 8
Dependent Claim
27 words
The method of claim 1 further comprising the step of cleaning a mounting surface of the semiconductor die prior to the step of placing the semiconductor die.
Claim 9
Dependent Claim
26 words
The method of claim 1 further comprising the step of cleaning the silicone-based die attach material after the step of curing the silicone-based die attach material.
Claim 10
Dependent Claim
25 words
The method of claim 8 wherein the step of cleaning the silicone-based die attach material comprises cleaning in an environment of ultraviolet radiation and ozone.
Claim 11
Independent Claim
158 words
A method for making a moisture resistant semiconductor device comprising the steps of: providing an organic substrate having a surface, a plurality of conductive traces formed on the surface, a die receiving area, and a die receiving pad formed on the surface within the die receiving area, wherein the plurality of conductive traces are formed of copper having an overlying plating layer, wherein the die receiving pad is formed of copper having a chemically created oxide layer, and wherein the die receiving pad is a solid metal pattern within the die receiving area where the surface is continuous; providing a semiconductor die; dispensing a silicone-based die attach material on the die receiving pad; attaching the semiconductor die to the die receiving pad using the silicone-based die attach material; electrically coupling the semiconductor die to the plurality of conductive traces; and encapsulating the semiconductor die and portions of the surface of the organic substrate with a resin molding compound.
Claim 12
Independent Claim
158 words
A method for making a moisture resistant semiconductor device comprising the steps of: providing an organic substrate having a surface, a plurality of conductive traces formed on the surface, a die receiving area, and a die receiving pad formed on the surface within the die receiving area, wherein the plurality of conductive traces are formed of copper having an overlying plating layer, wherein the die receiving pad is formed of copper having a chemically created oxide layer, and wherein the die receiving pad is a solid metal pattern within the die receiving area where the surface is continuous; providing a semiconductor die; dispensing a silicone-based die attach material on the die receiving pad; attaching the semiconductor die to the die receiving pad using the silicone-based die attach material; electrically coupling the semiconductor die to the plurality of conductive traces; and encapsulating the semiconductor die and portions of the surface of the organic substrate with a resin molding compound.
Claim 13
Dependent Claim
23 words
The method of claim 10 further comprising the step of cleaning the semiconductor die using ultraviolet radiation prior to the step of attaching.
Claim 14
Dependent Claim
47 words
The method of claim 11 wherein the step of cleaning comprises cleaning the semiconductor die to achieve a degree of cleanliness on a backside of the semiconductor die, wherein the degree of cleanliness is measured as a contact angle of dispensed water of less than ten degrees.
Claim 15
Dependent Claim
24 words
The method of claim 10 further comprising the step of gelling the silicone-based die attach material within three minutes after the step of dispensing.
Claim 16
Dependent Claim
46 words
The method of claim 10 wherein as a result of attaching the semiconductor die a fillet of the silicone-based die attach material is formed around a perimeter of the semiconductor die, and further comprising the step of cleaning the fillet prior to the step of encapsulating.
Claim 17
Dependent Claim
19 words
The method of claim 14 wherein the step of cleaning the fillet comprises cleaning the fillet using ultraviolet radiation.
Claim 18
Dependent Claim
18 words
The method of claim 14 wherein the step of cleaning the fillet comprises cleaning the fillet using ozone.
Claim 19
Independent Claim
172 words
A method for making a moisture resistant semiconductor device comprising the steps of: providing a semiconductor die, the semiconductor die having an active frontside and an inactive backside; cleaning the inactive backside of the semiconductor die; providing an organic substrate having a top surface, a bottom surface, a pattern of metal traces on the top surface, a die receiving pad larger in area than the semiconductor die and formed of a solid metal pattern where the top surface is continuous, and an oxide layer formed on an entirety of the die receiving pad; dispensing a silicone-based die attach material on the die receiving pad; mounting the semiconductor die on the die receiving pad using the silicone-based die attach material; gelling the silicone-based die attach material within three minutes after the step of dispensing to prevent excessive bleed; curing the silicone-based die attach material; electrically coupling the semiconductor die to the pattern of metal traces; and encapsulating the semiconductor die and portions of the top surface of the organic substrate with a resin.
Claim 20
Independent Claim
172 words
A method for making a moisture resistant semiconductor device comprising the steps of: providing a semiconductor die, the semiconductor die having an active frontside and an inactive backside; cleaning the inactive backside of the semiconductor die; providing an organic substrate having a top surface, a bottom surface, a pattern of metal traces on the top surface, a die receiving pad larger in area than the semiconductor die and formed of a solid metal pattern where the top surface is continuous, and an oxide layer formed on an entirety of the die receiving pad; dispensing a silicone-based die attach material on the die receiving pad; mounting the semiconductor die on the die receiving pad using the silicone-based die attach material; gelling the silicone-based die attach material within three minutes after the step of dispensing to prevent excessive bleed; curing the silicone-based die attach material; electrically coupling the semiconductor die to the pattern of metal traces; and encapsulating the semiconductor die and portions of the top surface of the organic substrate with a resin.
Claim 21
Dependent Claim
27 words
The method of claim 17 wherein the step of cleaning comprises cleaning the inactive backside of the semiconductor die in an environment of ultraviolet radiation and ozone.
Claim 22
Dependent Claim
33 words
The method of claim 18 further comprising the step of cleaning exposed portions of the silicone-based die attach material, after the step of mounting the semiconductor die and before the step of encapsulating.
Claim 23
Dependent Claim
28 words
The method of claim 19 wherein the step of cleaning exposed portions of the silicone-based die attach material comprises cleaning in an environment of ultraviolet radiation and ozone.
Claim 24
Dependent Claim
43 words
The method of claim 17 wherein the step of providing an organic substrate comprises providing an organic substrate wherein the oxide layer on the die receiving pad is comprised of an oxide selected from a group consisting of cupric oxide and cuprous oxide.
References Cited (Backward Citations)
US4159221A
Cited
US4028135A
Cited
US4507672A
Cited
JPS59114832A
Cited
US5011786A
Cited
US4816426A
Cited
US4769399A
Cited
US5150193A
Cited
US5072283A
Cited
EP0350021A2
Cited
JPH02275618A
Cited
US5175060A
Cited
US5173766A
Cited
US5143785A
Cited
US5296738A
Cited
US5274913A
Cited
US5469333A
Cited
US5473814A
Cited
US5436203A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-05-25 | 2001-11-24 | 2002-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-05-25 | 2005-11-24 | 2006-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-05-25 | 2009-11-24 | 2010-05-26 | $7700.00 | Window Closed / Lapsed |