Diamond-like nanocomposite corrosion resistant coatings
Assignee: Oerlikon Metaplas GmbH
•
Filing: 1995-06-07
•
Granted: 1998-03-17
•
Expires: 2015-06-07
Abstract
Abstract A method for inhibiting corrosion of a substrate by applying to a substrate a corrosion resistant coating comprising a diamond-like solid state material having interpenetrating atomic scale networks of class of diamond-like solid state materials formed from interpenetrating networks comprising a first network of carbon in a diamond-like carbon network stabilized by hydrogen, a silicon network stabilized by oxygen, and optionally at least one network made from dopant elements or dopant compounds containing elements from groups 1-7b and 8 of the periodic table.
Inventors
- 👤 Veniamin F. Dorfman
- 👤 Arvind Goel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:10
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; A; A61; A61L; A61L27/00; A61L27/28; A61L27/30; A61L27/303; A61L27/306; B; B82; B82Y; B82Y30/00; C04B41/45; C04B41/50; C04B41/5001; C04B41/5002; C04B41/80; C04B41/81; C04B41/85; C23; C23C; C23C14/00; C23C14/0021; C23C14/0036; C23C14/06; C23C14/0605; C23C14/22; C23C14/221; C23C16/00; C23C16/22; C23C16/30; C23C16/44; C23C16/448; C23C16/4481; C23C16/4483; C23C16/4485; C23C16/455; C23C16/45563; C23C16/45568; C23C16/50; C23C16/503; F; F42; F42B; F42B12/00; F42B12/72; F42B12/76; F42B12/80; G02B1/105; G; G02; G02B; G02B1/00; G02B1/10; G02B1/11; G02B1/111; G02B1/14; G11; G11B; G11B5/00; G11B5/84; G11B5/8408; A61F; A61F2310/00; A61F2310/00389; A61F2310/00574; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
73 words
A corrosion resistant material made from a substrate susceptible to corrosion and a corrosion resistant coating, said coating made from a class of diamond-like solid state materials formed from interpenetrating networks, said networks comprising a first network of diamond-like carbon stabilized by hudrogen, a second silicon network stabilized by oxygen and, optionally, at least one network of dopant elements, or dopant compounds containing elements from groups 1-7b and 8 of the periodic table.
Claim 2
Dependent Claim
73 words
A corrosion resistant material made from a substrate susceptible to corrosion and a corrosion resistant coating, said coating made from a class of diamond-like solid state materials formed from interpenetrating networks, said networks comprising a first network of diamond-like carbon stabilized by hudrogen, a second silicon network stabilized by oxygen and, optionally, at least one network of dopant elements, or dopant compounds containing elements from groups 1-7b and 8 of the periodic table.
Claim 3
Dependent Claim
30 words
The material according to claim 1 wherein the carbon, hydrogen, silicon and oxygen are obtained from the decomposition of an organosiloxane having from about 1 to about 10 silicon atoms.
Claim 4
Dependent Claim
11 words
The material according to claim 2 wherein the organosiloxane is polyphenylmethylsiloxane.
Claim 5
Dependent Claim
21 words
The material according to claim 1 wherein the carbon content is from about 40 wt. % to about 98 wt. %.
Claim 6
Dependent Claim
21 words
The material according to claim 1 wherein the carbon content is from about 50 wt. % to about 98 wt. %.
Claim 7
Dependent Claim
20 words
The material according to claim 1 wherein the carbon to silicon weight ratio is from about 2:1 to about 8:1.
Claim 8
Dependent Claim
20 words
The material according to claim 1 wherein the silicon to oxygen weight ration is from about 0.5:1 to about 3:1.
Claim 9
Dependent Claim
46 words
The material according to claim 1 wherein the dopant elements are selected from the group consisting of B, Si, Ge, Te, O, Mo, W, Ta, Nb, Pd, Ir, Pt, V, Fe, Co, Mg, Mn, Ni, Ti, Zr, Cr, Re, Hf, Cu, Al, N, Ag, and Au.
Claim 10
Dependent Claim
57 words
The material according to claim 1 wherein the carbon content of the solid state material is at least 40 atomic % of the coating, the hydrogen content is up to about 40 atomic % of the carbon, and the sum of the silicon, oxygen and dopants together is greater than about 2 atomic % of the coating.
References Cited (Backward Citations)
US4191735A
Cited
GB2158086A
Cited
US4985051A
Cited
US4948388A
Cited
US4877677A
Cited
US4783368A
Cited
US4897829A
Cited
US4915977A
Cited
US4842937A
Cited
US5064801A
Cited
US5040501A
Cited
US4960643A
Cited
US4822466A
Cited
US4816291A
Cited
US5256483A
Cited
US5002899A
Cited
US4992298A
Cited
US5055318A
Cited
US5158828A
Cited
US5068148A
Cited
US5171732A
Cited
US5210430A
Cited
US5142390A
Cited
US4980021A
Cited
US5137784A
Cited
US5101288A
Cited
US5087434A
Cited
US4961958A
Cited
US5206083A
Cited
US5183602A
Cited
US5169579A
Cited
US5198285A
Cited
US5110577A
Cited
US5243199A
Cited
US5219769A
Cited
US5094915A
Cited
US5100424A
Cited
US5077103A
Cited
US5202571A
Cited
US5174983A
Cited
US5135808A
Cited
US5190807A
Cited
US5352493A
Cited
US5177299A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2001-03-16 | 2001-09-15 | 2002-03-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2005-03-16 | 2005-09-15 | 2006-03-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2009-03-16 | 2009-09-15 | 2010-03-17 | $7700.00 | Window Closed / Lapsed |