Assignee: Micron Technology Inc
•
Filing: 1994-04-15
•
Granted: 1997-04-29
•
Expires: 2014-04-15
Abstract
Abstract The present invention is described in several embodiments depicted structures and methods to form these structures. A first embodiment is a structure having a silicon dioxide film bonded to a metal film comprising: a metal nitride film bonded to the metal film; and the silicon dioxide film bonded to the metal nitride film. A second embodiment is a structure having a silicon dioxide film bonded to a metal film comprising: a metal oxide film bonded to the metal film; and the silicon dioxide film bonded to the metal oxide film. A third embodiment is a structure having a silicon dioxide film bonded to a metal film comprising: a metal/oxide/nitride film bonded to the metal film; and the silicon dioxide film bonded to the metal/oxide/nitride film.
Inventors
- 👤 Ravi Iyer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:49
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/65; H10P14/6502; H10P14/6506; H10P14/6512; H10P14/6514; H10P14/69; H10P14/692; H10P14/6921; H10P14/69215
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
79 words
A semiconductor fabrication process for adhering silicon dioxide to metal comprising the steps of: forming an oxygen deficient film onto said metal surface, said oxygen deficient film comprising SiO x formed by the plasma dissociation of TEOS, where x ranges from 1 to less than 2; and forming a silicon dioxide layer onto said oxygen deficient film, thereby causing a chemical reaction between said oxygen deficient film and said metal to form an interfacial metal oxide bonding layer therebetween.
Claim 2
Dependent Claim
79 words
A semiconductor fabrication process for adhering silicon dioxide to metal comprising the steps of: forming an oxygen deficient film onto said metal surface, said oxygen deficient film comprising SiO x formed by the plasma dissociation of TEOS, where x ranges from 1 to less than 2; and forming a silicon dioxide layer onto said oxygen deficient film, thereby causing a chemical reaction between said oxygen deficient film and said metal to form an interfacial metal oxide bonding layer therebetween.
Claim 3
Dependent Claim
10 words
The process of claim 1, wherein said metal comprises titanium.
Claim 4
Dependent Claim
12 words
The process of claim 1, wherein said interfacial layer comprises titanium oxide.
Claim 5
Dependent Claim
24 words
The process of claim 1, wherein said process further comprises cleaning the surface of said metal by subjecting the metal to an argon plasma.
Claim 6
Dependent Claim
47 words
The process of claim 4, wherein subjecting the metal to an argon plasma further comprises a sputter clean at a pressure of approximately 30 mTorr, at an energy of approximately 200 W RF power, at an argon flow rate of approximately 50 sccm for approximately 10 sec.
Claim 7
Dependent Claim
19 words
The process of claim 5, wherein said sputter clean further comprises employing a magnetic field of approximately 60 Gauss.
Claim 8
Dependent Claim
50 words
The process of claim 4, wherein subjecting the metal to an argon plasma further comprises a sputter clean at a pressure range of 10-50 mTorr, at an energy range of 100-500 W RF power, at an argon flow rate of 20-70 sccm for a time period range of 5-50 sec.
Claim 9
Dependent Claim
19 words
The process of claim 1, wherein said metal comprises a metal layered stack of titanium, aluminum, copper and titanium.
Claim 10
Dependent Claim
62 words
A semiconductor fabrication process for adhering silicon dioxide to titanium comprising the steps of: forming a SiO x film, where x is less than 2, onto said titanium surface; and forming a silicon dioxide layer onto said SiO x film, thereby causing a chemical reaction between said SiO x film and said titanium to form an interfacial titanium oxide bonding layer therebetween.
Claim 11
Dependent Claim
62 words
A semiconductor fabrication process for adhering silicon dioxide to titanium comprising the steps of: forming a SiO x film, where x is less than 2, onto said titanium surface; and forming a silicon dioxide layer onto said SiO x film, thereby causing a chemical reaction between said SiO x film and said titanium to form an interfacial titanium oxide bonding layer therebetween.
Claim 12
Dependent Claim
24 words
The process of claim 9, wherein said process further comprises cleaning the surface of said titanium by subjecting the titanium to an argon plasma.
Claim 13
Dependent Claim
52 words
The process of claim 10, wherein subjecting the titanium to an argon plasma further comprises a sputter clean at a pressure of approximately 30 mTorr, at an energy of approximately 200 W RF power, at an argon flow rate of approximately 50 sccm and for a time period of approximately 10 sec.
Claim 14
Dependent Claim
19 words
The process of claim 11, wherein said sputter clean further comprises employing a magnetic field of approximately 60 Gauss.
Claim 15
Dependent Claim
84 words
A semiconductor fabrication process for adhering silicon dioxide to metal comprising the steps of: converting the metal material at the surface of said metal to a metal nitride to form said metal nitride on a remaining portion of non-converted metal; forming an oxygen deficient film on the metal nitride; and forming a silicon dioxide layer onto said oxygen deficient film, thereby causing a chemical reaction between said oxygen deficient film, said metal nitride and said metal to form an interfacial metal/oxide/nitride bonding layer therebetween.
Claim 16
Dependent Claim
84 words
A semiconductor fabrication process for adhering silicon dioxide to metal comprising the steps of: converting the metal material at the surface of said metal to a metal nitride to form said metal nitride on a remaining portion of non-converted metal; forming an oxygen deficient film on the metal nitride; and forming a silicon dioxide layer onto said oxygen deficient film, thereby causing a chemical reaction between said oxygen deficient film, said metal nitride and said metal to form an interfacial metal/oxide/nitride bonding layer therebetween.
Claim 17
Dependent Claim
10 words
The process of claim 13, wherein said metal comprises titanium.
Claim 18
Dependent Claim
11 words
The process of claim 14, wherein said interfacial layer comprises titanium/oxide/nitride.
Claim 19
Dependent Claim
24 words
The process of claim 13, wherein said process further comprises cleaning the surface of said metal by subjecting the metal to an argon plasma.
Claim 20
Dependent Claim
52 words
The process of claim 16, wherein subjecting the metal to an argon plasma further comprises a sputter clean at a pressure of approximately 30 mTorr, at an energy of approximately 200 W RF power, at an argon flow rate of approximately 50 sccm and for a time period of approximately 10 sec.
Claim 21
Dependent Claim
19 words
The process of claim 17, wherein said sputter clean further comprises employing a magnetic field of approximately 60 Gauss.
Claim 22
Dependent Claim
50 words
The process of claim 16, wherein subjecting the metal to an argon plasma further comprises a sputter clean at a pressure range of 10-50 mTorr, at an energy range of 100-500 W RF power, at an argon flow rate of 20-70 sccm for a time period range of 5-50 sec.
Claim 23
Dependent Claim
29 words
The process of claim 13, wherein said oxygen deficient film comprises SiO x formed by the plasma dissociation of TEOS, where x ranges from 1 to less than 2.
Claim 24
Dependent Claim
19 words
The process of claim 13, wherein said metal comprises a metal layered stack of titanium, aluminum, copper and titanium.
Claim 25
Dependent Claim
89 words
A semiconductor fabrication process for adhering silicon dioxide to titanium comprising the steps of: converting the titanium material at the surface of said titanium to a titanium nitride to form said titanium nitride on a remaining portion of non-convened titanium; forming an SiO x film on the titanium nitride; forming a silicon dioxide layer on said SiO x film where x is less than 2, thereby causing a chemical reaction between said SiO x film, said titanium nitride and said titanium to form an interfacial titanium/oxide/nitride bonding layer therebetween.
Claim 26
Dependent Claim
89 words
A semiconductor fabrication process for adhering silicon dioxide to titanium comprising the steps of: converting the titanium material at the surface of said titanium to a titanium nitride to form said titanium nitride on a remaining portion of non-convened titanium; forming an SiO x film on the titanium nitride; forming a silicon dioxide layer on said SiO x film where x is less than 2, thereby causing a chemical reaction between said SiO x film, said titanium nitride and said titanium to form an interfacial titanium/oxide/nitride bonding layer therebetween.
Claim 27
Dependent Claim
24 words
The process of claim 21, wherein said process further comprises cleaning the surface of said titanium by subjecting the titanium to an argon plasma.
Claim 28
Dependent Claim
52 words
The process of claim 23, wherein subjecting the titanium to an argon plasma further comprises a sputter clean at a pressure of approximately 30 mTorr, at an energy of approximately 200 W RF power, at an argon flow rate of approximately 50 sccm and for a time period of approximately 10 sec.
Claim 29
Dependent Claim
19 words
The process of claim 23, wherein said sputter clean futher comprises employing a magnetic field of approximately 60 Gauss.
Claim 30
Dependent Claim
50 words
The process of claim 23, wherein subjecting the titanium to an argon plasma further comprises a sputter clean at a pressure range of 10-50 mTorr, at an energy range of 100-500 W RF power, at an argon flow rate of 20-70 sccm for a time period range of 5-50 sec.
Claim 31
Dependent Claim
58 words
A semiconductor fabrication process for adhering silicon dioxide to titanium comprising the steps of: forming an oxygen deficient film onto a surface of said titanium; and forming a silicon dioxide layer onto said oxygen deficient film, thereby causing a chemical reaction between said oxygen deficient film and said titanium to form an interfacial titanium oxide bonding layer therebetween.
Claim 32
Dependent Claim
58 words
A semiconductor fabrication process for adhering silicon dioxide to titanium comprising the steps of: forming an oxygen deficient film onto a surface of said titanium; and forming a silicon dioxide layer onto said oxygen deficient film, thereby causing a chemical reaction between said oxygen deficient film and said titanium to form an interfacial titanium oxide bonding layer therebetween.
Claim 33
Dependent Claim
24 words
The process of claim 27, wherein said process further comprises cleaning the surface of said titanium by subjecting the metal to an argon plasma.
Claim 34
Dependent Claim
47 words
The process of claim 28, wherein subjecting the metal to an argon plasma further comprises a sputter clean at a pressure of approximately 30 mTorr, at an energy of approximately 200 W RF power, at an argon flow rate of approximately 50 sccm for approximately 10 sec.
Claim 35
Dependent Claim
19 words
The process of claim 29, wherein said sputter clean further comprises employing a magnetic field of approximately 60 Gauss.
Claim 36
Dependent Claim
50 words
The process of claim 28, wherein subjecting the titanium to an argon plasma further comprises a sputter clean at a pressure range of 10-50 mTorr, at an energy range of 100-500 W RF power, at an argon flow rate of 20-70 sccm for a time period range of 5-50 sec.
Claim 37
Dependent Claim
29 words
The process of claim 27, wherein said oxygen deficient film comprises SIO x formed by the plasma dissociation of TEOS, where x ranges from 1 to less than 2.
References Cited (Backward Citations)
US3916041A
Cited
US4350563A
Cited
US4462881A
Cited
US4448633A
Cited
US4821085A
Cited
US4931411A
Cited
US4713260A
Cited
US4931410A
Cited
US5130267A
Cited
US5093710A
Cited
US5268217A
Cited
JPH04214630A
Cited
US5252515A
Cited
US5202152A
Cited
US5326724A
Cited
US5275715A
Cited
US5416045A
Cited
US5440167A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2000-04-28 | 2000-10-28 | 2001-04-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2004-04-28 | 2004-10-28 | 2005-04-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2008-04-28 | 2008-10-28 | 2009-04-29 | $7700.00 | Window Closed / Lapsed |