Low temperature reaction bonding
Assignee: Honeywell International Inc
•
Filing: 1993-12-03
•
Granted: 1995-06-27
•
Expires: 2013-12-03
Abstract
Abstract A method for reaction bonding surfaces at low temperatures in which polished and cleaned surfaces are bombarded with a mixture of oxygen and fluorine ions to produce activated surfaces. The activated surfaces are then cleaned to remove particulates, then contacted at room temperature to affect a reaction bond therebetween. The bond energy of the reaction bonded surfaces increase with time at room temperature. The rate at which the bond energy of the reaction bonded surfaces increases may be enhanced by moderate heating at a low temperature below a temperature which would be detrimental to any part of the reaction bonded structure. A satisfactory bond energy for silicon wafers can be achieved in four hours at room temperature and in less than 10 minutes at 50° C.
Inventors
- 👤 George G. Goetz
- 👤 Warren M. Dawson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:50
CPC Classifications
C; C03; C03C; C03C23/00; C03C23/0005; C03C23/0055; C03C27/00; C03C27/06; C04; C04B; C04B37/00; C04B37/003; C04B37/005; C04B37/04; C04B37/045; H; H10; H10W; H10W90/00; C04B2235/00; C04B2235/65; C04B2235/658; C04B2235/6583; C04B2235/6584; C04B2235/70; C04B2235/96; C04B2235/963; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/06; C04B2237/12; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/36; C04B2237/368; C04B2237/50; C04B2237/52; H10W72/00; H10W72/071; H10W72/072; H10W72/07231; H10W72/07236; Y; Y10; Y10S; Y10S148/00; Y10S148/022
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
94 words
A method for reaction bonding solid surfaces at a low temperature comprising the steps of: polishing each solid surface to be reaction bonded to have a maximum roughness of the order of atomic dimensions to produce polished surfaces; cleaning each of said polished surfaces to remove contaminants and particulates to produce cleaned surfaces; ion bombarding said cleaned surfaces with a mixture of oxygen and fluorine ions having an energies preselected to produce activated surfaces; and placing said activated surfaces in physical contact with each other at room temperature to reaction bond said activated surfaces.
Claim 2
Independent Claim
94 words
A method for reaction bonding solid surfaces at a low temperature comprising the steps of: polishing each solid surface to be reaction bonded to have a maximum roughness of the order of atomic dimensions to produce polished surfaces; cleaning each of said polished surfaces to remove contaminants and particulates to produce cleaned surfaces; ion bombarding said cleaned surfaces with a mixture of oxygen and fluorine ions having an energies preselected to produce activated surfaces; and placing said activated surfaces in physical contact with each other at room temperature to reaction bond said activated surfaces.
Claim 3
Dependent Claim
27 words
The method of claim 1 further including the step of storing said reaction bonded surfaces at room temperature to increase a bond energy between said activated surfaces.
Claim 4
Dependent Claim
49 words
The method of claim 1 wherein said reaction bonded surfaces are part of a structure having different parts which may deteriorate at elevated temperatures, said method further comprising the step of heating said reaction bonded surfaces to a temperature which is hot detrimental to any part of said structure.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein said step of polishing produces surfaces having a roughness of less than 1 nanometer.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein said step of ion bombarding includes the step of bombarding said cleaned surfaces using oxygen and fluorine ions having energies preferably in the range from 10 to 400 eV.
Claim 7
Dependent Claim
37 words
The method of claim 1 wherein said step of ion bombardment includes the step of oxygen and fluorine ion bombardment with ions having energies of approximately 20 eV to inhibit sputtering, reactive ion etching and radiation damage.
Claim 8
Dependent Claim
77 words
The method of claim 1 wherein said step of ion bombarding includes the steps of: placing said cleaned surfaces in an ion bombardment chamber having a reduced pressure oxygen atmosphere; adding a predetermined quantity of a gas containing fluorine to said oxygen atmosphere; ionizing said oxygen and said gas containing fluorine to produce oxygen ions and fluorine ions; and bombarding said cleaned surfaces with said oxygen and fluorine ions having preselected energies to produce said activated surfaces.
Claim 9
Independent Claim
131 words
A method for reaction bonding two surfaces at a low temperature comprising the steps of: polishing each of the two surfaces to be reaction bonded to have a roughness less: than a predetermined roughness; cleaning said surfaces to remove contaminants and particulates which would interfere with reaction bonding; placing said cleaned surfaces in an ion bombardment chamber having a reduced pressure oxygen atmosphere containing a predetermined quantity of a gas containing fluorine; ionizing said oxygen and said gas containing fluorine to produce oxygen and fluorine ions; accelerating said oxygen ions and said fluorine ions toward said surfaces with a predetermined energy; bombarding said surfaces with said oxygen and fluorine ions having energies selected to produce activated surfaces; and contacting said activated surfaces at room temperature to produce a reaction bond therebetween.
Claim 10
Independent Claim
131 words
A method for reaction bonding two surfaces at a low temperature comprising the steps of: polishing each of the two surfaces to be reaction bonded to have a roughness less: than a predetermined roughness; cleaning said surfaces to remove contaminants and particulates which would interfere with reaction bonding; placing said cleaned surfaces in an ion bombardment chamber having a reduced pressure oxygen atmosphere containing a predetermined quantity of a gas containing fluorine; ionizing said oxygen and said gas containing fluorine to produce oxygen and fluorine ions; accelerating said oxygen ions and said fluorine ions toward said surfaces with a predetermined energy; bombarding said surfaces with said oxygen and fluorine ions having energies selected to produce activated surfaces; and contacting said activated surfaces at room temperature to produce a reaction bond therebetween.
Claim 11
Dependent Claim
52 words
The method of claim 8 wherein said step of placing includes the step of placing said two surfaces in said ion bombardment chamber having a reduced pressure oxygen atmosphere containing a gas selected from the group of gases consisting of CF 4 , CHF 3 , CF 6 and SF 6 .
Claim 12
Dependent Claim
29 words
The method of claim 8 wherein said step of polishing includes the step of polishing each surface to a roughness of the order of magnitude equal to atomic dimensions.
Claim 13
Dependent Claim
34 words
The method of claim 8 wherein said step of accelerating said oxygen and fluorine ions includes the step of accelerating said oxygen and fluorine ions to preferably have an energy less than 400 eV.
Claim 14
Dependent Claim
42 words
The method of claim 11 wherein said step of accelerating said oxygen and fluorine ions includes the step of accelerating said oxygen and fluorine ions to have an energy of approximately 20 eV to inhibit sputtering, reactive ion etching, and radiation damage.
Claim 15
Dependent Claim
54 words
The method of claim 8 wherein said reaction bonded surfaces are part of a structure having components which may deteriorate at temperatures above a predetermined temperature, said method further comprising the step of heating said structure at a temperature less than said predetermined temperature to enhance the bonding energy of said reaction bonded surfaces.
Claim 16
Independent Claim
150 words
A method for increasing the reaction bond energy between two surfaces at a low temperature comprising the steps of: polishing each of the two surfaces to be reaction bonded to have a roughness less than a predetermined roughness; cleaning said two surfaces to remove contaminants and particulates which would interfere with reaction bonding; placing said cleaned surfaces in an ion bombardment chamber having a reduced pressure atmosphere of oxygen and a gas containing fluorine; ionizing said oxygen and gas containing fluorine to generate oxygen and fluorine ions; accelerating said oxygen and fluorine ions toward said cleaned surfaces with a predetermined energy; bombarding said cleaned surfaces with said oxygen and fluorine ions to produce activated surfaces; reaction bonding said activated surfaces; and storing said reaction bonded surfaces for a preselected time at said low temperature to increase the bond energy of said reaction bonded activated surfaces to a desired minimum value.
Claim 17
Independent Claim
150 words
A method for increasing the reaction bond energy between two surfaces at a low temperature comprising the steps of: polishing each of the two surfaces to be reaction bonded to have a roughness less than a predetermined roughness; cleaning said two surfaces to remove contaminants and particulates which would interfere with reaction bonding; placing said cleaned surfaces in an ion bombardment chamber having a reduced pressure atmosphere of oxygen and a gas containing fluorine; ionizing said oxygen and gas containing fluorine to generate oxygen and fluorine ions; accelerating said oxygen and fluorine ions toward said cleaned surfaces with a predetermined energy; bombarding said cleaned surfaces with said oxygen and fluorine ions to produce activated surfaces; reaction bonding said activated surfaces; and storing said reaction bonded surfaces for a preselected time at said low temperature to increase the bond energy of said reaction bonded activated surfaces to a desired minimum value.
Claim 18
Dependent Claim
52 words
The method of claim 14 wherein said bonded surfaces are part of a structure having at least one component which may deteriorate at temperatures above a limiting temperature, said step of storing further includes the step of heating said structure to a temperature below said limiting temperature to enhance said reaction bond.
Claim 19
Dependent Claim
33 words
The method of claim 15 wherein said step of accelerating includes the step of accelerating said oxygen and fluorine ions towards said cleaned surfaces with an energy preferably between 10 and 400 eV.
Claim 20
Dependent Claim
31 words
The method of claim 15 wherein said step of accelerating includes the step of accelerating said oxygen and fluorine ions toward said cleaned surfaces with an energy of approximately 20 eV.
Claim 21
Dependent Claim
37 words
The method of claim 15 wherein said step of storing includes the step of storing said reaction bonded surfaces at room temperature for at least 4 hours to increase the bond energy to a desired minimum value.
Claim 22
Dependent Claim
12 words
The method of claim 14 wherein said low temperature is room temperature.
References Cited (Backward Citations)
US3679985A
Cited
US4170662A
Cited
US4274483A
Cited
US4345985A
Cited
US4458346A
Cited
US4457972A
Cited
US4765860A
Cited
US4638552A
Cited
US4547432A
Cited
US4983251A
Cited
US4960736A
Cited
US4824008A
Cited
US4886681A
Cited
US4884737A
Cited
US4917843A
Cited
US4849247A
Cited
US4957771A
Cited
JPH0391227A
Cited
US5008723A
Cited
US5010036A
Cited
US5232870A
Cited
USH1164H
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-06-26 | 1998-12-26 | 1999-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-06-26 | 2002-12-26 | 2003-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-06-26 | 2006-12-26 | 2007-06-27 | $7700.00 | Window Closed / Lapsed |