Method of producing solid electrolyte oxygen-sensing element of laminated structure
Assignee: Nissan Motor Co Ltd
•
Filing: 1980-12-23
•
Granted: 1982-08-24
•
Expires: 2000-12-23
Abstract
Abstract A method of producing an oxygen sensing element which is essentially an oxygen concentration cell in the form of a lamination of relatively thin layers. The first step of the method is to prepare a lamination of a ceramic shield layer, an inner or reference electrode layer, a solid electrolyte layer and an outer or measurement electrode layer which is formed by sintering metal particles applied to the solid electrolyte layer surface in the form of a paste or slurry and dried. Then an additional measurement electrode layer, preferably not thicker than 1.0 micron, is formed on the outer surface of the sintered measurement electrode layer by a physical vapor deposition technique such as ion plating, sputtering or vacuum evaporation. Preferably this electrode layer is formed by a two-stage vapor deposition process wherein the first stage deposition is terminated before the deposited layer becomes thicker than 0.5 microns. The addition of the vapor-deposited measurement electrode layer improves the responsiveness and durability of the oxygen sensing element.
Inventors
- 👤 Masayuki Tohda
- 👤 Hiroshi Takao
- 👤 Shinji Kimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:06
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4071; H; H01; H01M; H01M4/00; H01M4/86; H01M4/90; H01M4/9041; H01M4/905; H01M4/9058; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
302 words
A method of producing an oxygen sensing element of the concentration cell type, the method comprising the steps of: preparing a lamination of a shield layer made of a ceramic material, a reference electrode layer laid on a major surface of said shield layer, an oxygen ion conductive solid electrolyte layer formed on said surface of said shield layer such that said reference electrode layer is tightly sandwiched between said shield layer and said solid electrolyte layer and a first measurement electrode layer which has a microscopically porous and gas-permeable structure and is formed on and in close contact with the outer surface of said solid electrolyte layer by applying a wet composition containing fine particles of a metal onto said surface of said solid electrolyte layer, drying the applied composition to evaporate the liquid component of the applied composition and firing the uncompleted lamination to sinter the metal particles contained in the applied composition; and forming a second measurement electrode layer having a microscopically porous and gas-permeable structure on the outer surface of said first measurement electrode layer by physical vapor deposition of a metal on said surface of said first measurement electrode layer, wherein said forming of said second measurement electrode layer comprises a first sub-step of performing said physical vapor deposition for a limited time such that the thickness of a metal film on said lamination during said first sub-step does not exceed 0.5 microns, a second sub-step of subjecting said lamination with said metal film deposited thereon from said first sub-step to a heat treatment performed in air at a temperature in the range from 900° to 1100° C. and a third sub-step of resuming said physical vapor deposition wherein said metal film subjected to said heat treatment becomes an innermost part of said second measurement electrode layer.
Claim 2
Independent Claim
302 words
A method of producing an oxygen sensing element of the concentration cell type, the method comprising the steps of: preparing a lamination of a shield layer made of a ceramic material, a reference electrode layer laid on a major surface of said shield layer, an oxygen ion conductive solid electrolyte layer formed on said surface of said shield layer such that said reference electrode layer is tightly sandwiched between said shield layer and said solid electrolyte layer and a first measurement electrode layer which has a microscopically porous and gas-permeable structure and is formed on and in close contact with the outer surface of said solid electrolyte layer by applying a wet composition containing fine particles of a metal onto said surface of said solid electrolyte layer, drying the applied composition to evaporate the liquid component of the applied composition and firing the uncompleted lamination to sinter the metal particles contained in the applied composition; and forming a second measurement electrode layer having a microscopically porous and gas-permeable structure on the outer surface of said first measurement electrode layer by physical vapor deposition of a metal on said surface of said first measurement electrode layer, wherein said forming of said second measurement electrode layer comprises a first sub-step of performing said physical vapor deposition for a limited time such that the thickness of a metal film on said lamination during said first sub-step does not exceed 0.5 microns, a second sub-step of subjecting said lamination with said metal film deposited thereon from said first sub-step to a heat treatment performed in air at a temperature in the range from 900° to 1100° C. and a third sub-step of resuming said physical vapor deposition wherein said metal film subjected to said heat treatment becomes an innermost part of said second measurement electrode layer.
Claim 3
Dependent Claim
25 words
A method according to claim 1, wherein said second measurement electrode layer is formed so as to have a thickness not greater than 1.0 micron.
Claim 4
Dependent Claim
32 words
A method according to claim 2, wherein the material for said second measurement electrode layer is a metal which is electronically conducting and can catalyze oxidation reactions of carbon monoxide and hydrocarbons.
Claim 5
Dependent Claim
36 words
A method according to claim 3, wherein said material for said second measurement electrode layer is selected from the group consisting of metals of the platinum group and alloys containing a metal of the platinum group.
Claim 6
Dependent Claim
18 words
A method according to claim 2, wherein said second measurement electrode layer is formed by a sputtering process.
Claim 7
Dependent Claim
19 words
A method according to claim 2, wherein said second measurement electrode layer is formed by a vacuum evaporation process.
Claim 8
Dependent Claim
32 words
A method according to claim 6, wherein said physical vapor deposition is performed in an inert gas atmosphere maintained at a pressure in the range from 2×10 -3 to 1×10 -2 Torr.
Claim 9
Dependent Claim
36 words
A method according to claim 6, wherein the step of forming said second measurement electrode layer further comprises renewing the outer surface of said first measurement electrode layer by sputter-etching in advance of said first sub-step.
Claim 10
Dependent Claim
31 words
A method according to claim 8, wherein the sputtering-etching step is performed in an oxygen-containing gas atmosphere maintained at a pressure in the range from 2×10 -3 to 1×10 -2 Torr.
Claim 11
Dependent Claim
29 words
A method according to claim 1, further comprising the step of providing a heating element in said shield layer for heating the oxygen-sensing element to promote oxygen ion conductivity.
Claim 12
Dependent Claim
22 words
A method according to claim 10, wherein said heating element comprises a thin wire or thin layer of an electrically resistive material.
Claim 13
Dependent Claim
28 words
A method according to claim 10, wherein said shield layer comprises an upper and lower portion wherein said heating element is located between said upper and lower portions.
Claim 14
Dependent Claim
70 words
A method according to claim 3, wherein said second measurement electrode layer is formed by a multi-stage physical vapor deposition process consisting of at least three stages performed with time intervals between the respective stages of said multi-stage deposition process, the first step of said multi-stage process being terminated before the thickness of an innermost layer of said second measurement electrode layer deposited by said first stage exceeds 0.5 microns.
Claim 15
Dependent Claim
32 words
A method according to claim 3, wherein the material for said first measurement electrode layer is a metal which is electronically conducting and can catalyze oxidation reactions of carbon monoxide and hydrocarbons.
Claim 16
Dependent Claim
31 words
A method according to claim 14, wherein the material for said reference electrode layer is a metal which is electronically conducting and can catalyze oxidation reactions of carbon monoxide and hydrocarbons.
Claim 17
Dependent Claim
26 words
A method according to claim 14, wherein the material for said reference electrode layer is an electronically conducting mixture of a metal and an oxide thereof.
Claim 18
Dependent Claim
32 words
A method according to claim 1, further comprising the step of subjecting said lamination to ultrasonic cleaning in an organic solvent prior to the step of forming said second measurement electrode layer.
Claim 19
Dependent Claim
28 words
A method according to claim 1, further comprising the step of forming a porous protecting layer at least on the outer surface of said second measurement electrode layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-23 | 1986-02-22 | 1986-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-23 | 1990-02-22 | 1990-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-23 | 1994-02-22 | 1994-08-24 | $7700.00 | Window Closed / Lapsed |