Recessed side-wall poly plugged local oxidation
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1993-07-28
•
Granted: 1995-02-28
•
Expires: 2013-07-28
Abstract
Abstract A method of forming a field oxide isolation region with reduced bird's beak length and planar topography is described. A first layer of pad oxide is formed on the surface of a silicon substrate. A layer of silicon nitride is formed on the surface of the first pad oxide layer. The silicon nitride layer and part of the first pad oxide layer are patterned to form an opening for the field oxide isolation region. The first pad oxide layer is removed in the area defined by the opening and simultaneously a cavity is formed in the first pad oxide layer under the silicon nitride. A second pad oxide layer is formed by oxidizing the exposed portions of the silicon substrate and the first pad oxide layer. A layer of polysilicon is deposited over the surfaces of the second pad oxide layer and the silicon nitride layer, and inside the cavity. The polysilicon layer is etched to form a polysilicon spacer adjacent to the silicon nitride layer and a polysilicon plug in the cavity. The field oxide isolation region is then formed in and on the silicon substrate. The silicon nitride layer and the remainder of the first pad oxide layer are removed. A sacrificial oxide layer is formed on the surface of the substrate, and is then removed to complete formation of the field oxide.
Inventors
- 👤 Lin-June Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:55
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/61
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
246 words
A method of forming a field oxide isolation region on and in the surface of a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form opening for said field oxide isolation region; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; forming a second pad oxide layer by oxidizing said exposed portion of said silicon substrate and said first pad oxide layer; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming said field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 2
Independent Claim
246 words
A method of forming a field oxide isolation region on and in the surface of a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form opening for said field oxide isolation region; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; forming a second pad oxide layer by oxidizing said exposed portion of said silicon substrate and said first pad oxide layer; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming said field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 3
Dependent Claim
33 words
The method of claim 1 wherein said cavity has a depth of between about 300 and 1200 Angstroms and is formed by etching with hydrofluoric acid for between about 6 and 20 minutes.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein said second pad oxide layer has a thickness of between about 60 and 100 Angstroms.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein said polysilicon spacer has a thickness of between about 300 and 1500 Angstroms.
Claim 6
Dependent Claim
23 words
The method of claim 1 wherein said field oxide isolation region is grown to a thickness of between about 4500 and 6000 Angstroms.
Claim 7
Independent Claim
261 words
A method of forming a field oxide isolation region on and in the surface of a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form opening for said field oxide isolation region; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; removing a thickness of said silicon substrate to provide a recessed area in the substrate, to a depth of between about 300 and 1500 Angstroms; forming a second pad oxide layer by oxidizing said silicon substrate; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming said field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 8
Independent Claim
261 words
A method of forming a field oxide isolation region on and in the surface of a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form opening for said field oxide isolation region; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; removing a thickness of said silicon substrate to provide a recessed area in the substrate, to a depth of between about 300 and 1500 Angstroms; forming a second pad oxide layer by oxidizing said silicon substrate; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming said field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 9
Dependent Claim
18 words
The method of claim 6 wherein said thickness of silicon substrate is removed by a plasma dry etch.
Claim 10
Dependent Claim
33 words
The method of claim 6 wherein said cavity has a depth of between about 300 and 1200 Angstroms, and is formed by etching with hydrofluoric acid for between about 6 and 20 minutes.
Claim 11
Dependent Claim
21 words
The method of claim 6 wherein said second pad oxide layer has a thickness of between about 60 and 100 Angstroms.
Claim 12
Dependent Claim
19 words
The method of claim 6 wherein said polysilicon spacer has a thickness of between about 300 and 1500 Angstroms.
Claim 13
Dependent Claim
23 words
The method of claim 6 wherein said field oxide isolation region is grown to a thickness of between about 4500 and 6000 Angstroms.
Claim 14
Independent Claim
238 words
A method of isolating semiconductor devices on a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form an opening; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; forming a second pad oxide layer by oxidizing said exposed portion of said silicon substrate and said first pad oxide layer; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming a field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed, to isolate said semiconductor devices; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 15
Independent Claim
238 words
A method of isolating semiconductor devices on a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form an opening; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; forming a second pad oxide layer by oxidizing said exposed portion of said silicon substrate and said first pad oxide layer; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming a field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed, to isolate said semiconductor devices; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 16
Dependent Claim
33 words
The method of claim 12 wherein said cavity has a depth of between about 300 and 1200 Angstroms, and is formed by etching with hydrofluoric acid for between about 6 and 12 minutes.
Claim 17
Dependent Claim
21 words
The method of claim 12 wherein said second pad oxide layer has a thickness of between about 60 and 100 Angstroms.
Claim 18
Dependent Claim
19 words
The method of claim 12 wherein said polysilicon spacer has a thickness of between about 300 and 1500 Angstroms.
Claim 19
Dependent Claim
23 words
The method of claim 12 wherein said field oxide isolation region is grown to a thickness of between about 4500 and 6000 Angstroms.
Claim 20
Independent Claim
257 words
A method of isolating semiconductor devices on a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form an opening; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; removing a thickness of said silicon substrate, to provide a recessed area in said substrate, to a depth of between about 300 and 1500 Angstroms; forming a second pad oxide layer by oxidizing said exposed portion of said silicon substrate; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming a field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed, to isolate said semiconductor devices; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 21
Independent Claim
257 words
A method of isolating semiconductor devices on a silicon substrate, comprising: forming a first layer of pad oxide on the surface of said silicon substrate; forming a layer of silicon nitride on the surface of said first pad oxide layer; patterning said silicon nitride layer and a partial thickness of said first pad oxide layer to form an opening; removing said first pad oxide layer in the area defined by said opening to expose a portion of said silicon substrate, and simultaneously forming a cavity by removing a portion of said first pad oxide layer under said silicon nitride layer; removing a thickness of said silicon substrate, to provide a recessed area in said substrate, to a depth of between about 300 and 1500 Angstroms; forming a second pad oxide layer by oxidizing said exposed portion of said silicon substrate; depositing a layer of polysilicon over the surfaces of said second pad oxide layer and said silicon nitride layer, and inside said cavity; forming a polysilicon spacer adjacent to said silicon nitride layer and a polysilicon plug in said cavity by etching said polysilicon layer; forming a field oxide isolation region in and on said silicon substrate, by thermal oxidation of said silicon substrate, whereby said polysilicon spacer and said polysilicon plug are consumed, to isolate said semiconductor devices; removing said silicon nitride layer; removing the remainder of said first pad oxide layer; forming a sacrificial oxide layer on the surface of said substrate; and removing said sacrificial oxide layer to complete said field oxide isolation region.
Claim 22
Dependent Claim
18 words
The method of claim 17 wherein said thickness of silicon substrate is removed by a plasma dry etch.
Claim 23
Dependent Claim
33 words
The method of claim 17 wherein said cavity has a depth of between about 300 and 1200 Angstroms, and is formed by etching with hydrofluoric acid for between about 6 and 20 minutes.
Claim 24
Dependent Claim
21 words
The method of claim 17 wherein said second pad oxide layer has a thickness of between about 60 and 100 Angstroms.
Claim 25
Dependent Claim
19 words
The method of claim 17 wherein said polysilicon spacer has a thickness of between about 300 and 1500 Angstroms.
Claim 26
Dependent Claim
23 words
The method of claim 17 wherein said field oxide isolation region is grown to a thickness of between about 4500 and 6000 Angstroms.
References Cited (Backward Citations)
US4829019A
Cited
US4965221A
Cited
US4927780A
Cited
US5175123A
Cited
US5318922A
Cited
US5326715A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1998-02-27 | 1998-08-29 | 1999-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2002-02-27 | 2002-08-29 | 2003-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2006-02-27 | 2006-08-29 | 2007-02-28 | $7700.00 | Window Closed / Lapsed |