Process of making pad structure for solder ball limiting metallurgy having reduced edge stress
Assignee: International Business Machines Corp
•
Filing: 1992-12-31
•
Granted: 1994-12-27
•
Expires: 2012-12-31
Abstract
Abstract A two-step masking process is disclosed for forming a ball limiting metallurgy (BLM) pad structure for a solder joint interconnection used between a support substrate and a semiconductor chip. A solder non-wettable layer and a solder wettable layer are deposited on the surface of a support substrate or semiconductor chip which are to be connected. A phased transition layer is deposited between the wettable and non-wettable layers. A thin photo-resist mask defines an area of the solder wettable and phased layers which are etched to form a raised, wettable frustum cone portion. A second mask is deposited on the surface of the support substrate or semiconductor chip, and has an opening concentrically positioned about the frustum cone. Solder is deposited in the opening and covers the frustum cone and the area about its periphery. When solidified, the solder, acting as a mask, is used to sub-etch the underlying solder non-wettable layer thereby defining the BLM pad. When reflowed, the solder beads away from the surface of the solder non-wettable layer to form a ball which securely adheres about the frustum cone.
Inventors
- 👤 Birendra N. Agarwala
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:57
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/099; H05; H05K; H05K3/00; H05K3/30; H05K3/32; H05K3/34; H05K3/3452; H05K1/00; H05K1/02; H05K1/11; H05K1/111; H05K1/112; H05K2201/00; H05K2201/09; H05K2201/09209; H05K2201/09372; H05K2201/09472; H05K2201/095; H05K2201/09509; H05K2201/20; H05K2201/2081; H05K2203/00; H05K2203/04; H05K2203/043; H05K3/3465; H05K3/38; H05K3/388; H10W72/00; H10W72/01; H10W72/012; H10W72/01251; H10W72/01255; H10W72/019; H10W72/20; H10W72/221; H10W72/251; H10W72/29; H10W72/90; H10W72/921; H10W72/923; H10W72/931; H10W72/934; H10W72/941; H10W72/942; H10W72/951; H10W72/952
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
171 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress, comprising the steps of: depositing sequentially first, second and third metal layers on a surface of a substrate to form a stack comprises of said first metal layer, said second metal layer and said third metal layer, said first metal layer adhering to said surface of said substrate and being solder non-wettable, said third metal layer being solder wettable, and said second layer being a phased metal composition of said first and said third metal layers; selectively etching said second and said third metal layers to form at least one raised structure on said first metal layer comprised of said second and third metal layers; depositing solder over said raised structure and a portion of said first metal layer positioned about a perimeter of said raised structure; and selectively etching said first metal layer from said surface of said substrate leaving at least one section of said first metal layer located under said solder.
Claim 2
Independent Claim
171 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress, comprising the steps of: depositing sequentially first, second and third metal layers on a surface of a substrate to form a stack comprises of said first metal layer, said second metal layer and said third metal layer, said first metal layer adhering to said surface of said substrate and being solder non-wettable, said third metal layer being solder wettable, and said second layer being a phased metal composition of said first and said third metal layers; selectively etching said second and said third metal layers to form at least one raised structure on said first metal layer comprised of said second and third metal layers; depositing solder over said raised structure and a portion of said first metal layer positioned about a perimeter of said raised structure; and selectively etching said first metal layer from said surface of said substrate leaving at least one section of said first metal layer located under said solder.
Claim 3
Dependent Claim
47 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress as recited in claim 1, further comprising the step of reflowing said solder to form a solder ball about said raised structure which beads away from said first metal layer.
Claim 4
Dependent Claim
78 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress as recited in claim 1 further comprising the steps of: defining a first area dimension for said raised structure with a first mask prior to said first etching step; and defining a second area dimension larger than said first area dimension for depositing said solder over said raised structure and said portion of said first metal layer with a second mask.
Claim 5
Dependent Claim
39 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress as recited in claim 1 wherein said solder is deposited by a technique selected from the group consisting of plating and evaporation.
Claim 6
Dependent Claim
36 words
A method of making a pad structure for a solder ball limiting metallurgy having reducing edge stress as recited in claim 1 wherein said step of selectively etching said first metal layer slightly undercuts said solder.
Claim 7
Dependent Claim
48 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress as recited in claim 1 wherein said step of selectively etching said second and third metal layers to form said raised structure yields a raised structure with a frustum conical shape.
Claim 8
Dependent Claim
42 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress as recited in claim 1 wherein said first metal layer is selected from the group consisting of chromium, titanium, zirconium, molybdenum, tantalum, and alloys thereof.
Claim 9
Dependent Claim
42 words
A method of making a pad structure for a solder ball limiting metallurgy having reduced edge stress as recited in claim 1 wherein said third metal layer is selected from the group consisting of copper, cobalt, nickel, platinum, palladium, and alloys thereof.
References Cited (Backward Citations)
US4360142A
Cited
JPS5618446A
Cited
JPS5649543A
Cited
US4434434A
Cited
US4514751A
Cited
JPS59117135A
Cited
JPH01120038A
Cited
JPH01120848A
Cited
US5027188A
Cited
JPH0282623A
Cited
US5298459A
Cited
JPH0344935A
Cited
US5137845A
Cited
US5268072A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-12-26 | 1998-06-27 | 1998-12-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-12-26 | 2002-06-27 | 2002-12-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-12-26 | 2006-06-27 | 2006-12-27 | $7700.00 | Window Closed / Lapsed |