Method of forming metal contact pads and terminals on semiconductor chips
Assignee: International Business Machines Corp
•
Filing: 1991-07-12
•
Granted: 1992-08-11
•
Expires: 2011-07-12
Abstract
Abstract A method of forming metal contact terminals (35) of a determined size having an insulating substrate (17) with a metal land (18) formed thereon and a passivating layer (19) provided with an opening exposing a part of the metal land by forming intermediate metal contact pad (33') in the contact opening, applying and patterning a photoresist, delineating the intermediate metal contact pad (33') using pattern (31) as an in-situ mask, depositing a lead-tin solder layer (34') over a metal mask to form a solder bump (34') on the final metal contact pad, and reflowing the solder to form a solder ball (34). Thereby achieving the metal contact terminal (35) at the contact pad site. The above method has applicability to the fabrication of contact terminals for high density/high count I/O connections for advanced semiconductor chips that are appropriate for flip-chip (C4) or face-down bonding thereof on metallized ceramic (MC) substrates.
Inventors
- 👤 Henri Lochon
- 👤 Georges Robert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:15
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W72/00; H10W72/01; H10W72/019; H10W70/00; H10W70/60; H10W72/012; H10W72/01251; H10W72/01255; H10W72/20; H10W72/241; H10W72/242; H10W72/251; H10W72/252; H10W72/90; H10W72/921; H10W72/923; H10W72/951; H10W72/952; Y; Y10; Y10S; Y10S148/00; Y10S148/143
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
179 words
A method of forming metal contact pads (33) of a determined size on a structure (23) of the type having an insulating substrate (17) with a metal land (18) formed thereon and a passivating layer (19) provided with a contact opening exposing a part of said metal land, said method comprising the steps of: a) depositing a metal layer (28) onto the structure through a metal mask (27) having holes greater than said determined size whereby an intermediate metal contact pad (33') is formed in said contact opening and at the close vicinity thereof; (b) applying a photoresist layer (31) onto the structure and, patterning said photoresist layer to leave a pattern (31) of said determined size aligned and above said intermediate contact pad (33') and leaving exposed a part of said intermediate contact pad in excess of said determinedsize; (c) delineating the intermediate metal contact pad (33'), said pattern (31) providing an in-situ mask, and removing the excess part to provide the metal contact pads (33) of said determined size; and, d) removing the remaining photoresist pattern (31).
Claim 2
Independent Claim
179 words
A method of forming metal contact pads (33) of a determined size on a structure (23) of the type having an insulating substrate (17) with a metal land (18) formed thereon and a passivating layer (19) provided with a contact opening exposing a part of said metal land, said method comprising the steps of: a) depositing a metal layer (28) onto the structure through a metal mask (27) having holes greater than said determined size whereby an intermediate metal contact pad (33') is formed in said contact opening and at the close vicinity thereof; (b) applying a photoresist layer (31) onto the structure and, patterning said photoresist layer to leave a pattern (31) of said determined size aligned and above said intermediate contact pad (33') and leaving exposed a part of said intermediate contact pad in excess of said determinedsize; (c) delineating the intermediate metal contact pad (33'), said pattern (31) providing an in-situ mask, and removing the excess part to provide the metal contact pads (33) of said determined size; and, d) removing the remaining photoresist pattern (31).
Claim 3
Independent Claim
28 words
The method of claim further comprising prior to the step a) of RF cleaning the structure by argon ion bombardment using the metal mask (27) of step a).
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the said metal layer consists of a Cr(28)-Cr/Cu-Cu(29)-Au(30) composite layer.
Claim 5
Dependent Claim
56 words
The method of claim 1, wherein the step b) of patterning comprises the steps of: applying a positive resist layer onto the structure; baking the resist layer; aligning the structure with a chromium mask (32); exposing the resist layer to UV light in a proximity printer or stepper; and, developing the resist layer in a developer.
Claim 6
Dependent Claim
52 words
The method claim 3 wherein the step of removing the excess metal comprises the steps of: etching the Au layer with a iodine and potassium iodide solution; etching the Cu and Cr layers with a nitric acid solution; and, etching the Cr/Cu overlap layer in a mixture of ceric ammonium sulfate solution.
Claim 7
Dependent Claim
22 words
The method of claim 5 wherein the step of etching the Au or Cu layer is completed in a HCl+HNO 3 solution.
Claim 8
Independent Claim
250 words
A method of forming metal contact terminals (35) of a determined size on a structure (23) of the type having an insulating substrate (17) with a metal land (18) formed thereon and a passivating layer (19) provided with a contact opening exposing a part of said metal land, said method characterized by the steps of: a) depositing a metal layer (28) onto the structure through a metal mask (27) having holes greater than said determined size whereby an intermediate metal contact pad (33') is formed in said contact opening and at the close vicinity thereof; b) applying a photoresist layer (31) onto the structure and, patterning said photoresist layer to leave a pattern (31) of said determined size aligned and above said intermediate contact pad (33') and leaving exposed a part of said intermediate contact pad in excess of said determined size; (c) delineating the intermediate metal contact pad (33'), said pattern (31) providing an in-situ mask, and removing the excess part to provide a final metal contact pad (33) of said determined size; d) removing the remaining photoresist pattern (31); e) aligning the structure with a metal mask having a hole centered with said final metal contact pad (33); f) depositing a lead-tin solder layer (34') over the metal mask forming a solder bump (34') on each said final metal contact pad and, g) reflowing each said solder bump to form a solder ball (34), whereby the metal contact terminals are formed (35) at each final metal contact pad.
Claim 9
Independent Claim
250 words
A method of forming metal contact terminals (35) of a determined size on a structure (23) of the type having an insulating substrate (17) with a metal land (18) formed thereon and a passivating layer (19) provided with a contact opening exposing a part of said metal land, said method characterized by the steps of: a) depositing a metal layer (28) onto the structure through a metal mask (27) having holes greater than said determined size whereby an intermediate metal contact pad (33') is formed in said contact opening and at the close vicinity thereof; b) applying a photoresist layer (31) onto the structure and, patterning said photoresist layer to leave a pattern (31) of said determined size aligned and above said intermediate contact pad (33') and leaving exposed a part of said intermediate contact pad in excess of said determined size; (c) delineating the intermediate metal contact pad (33'), said pattern (31) providing an in-situ mask, and removing the excess part to provide a final metal contact pad (33) of said determined size; d) removing the remaining photoresist pattern (31); e) aligning the structure with a metal mask having a hole centered with said final metal contact pad (33); f) depositing a lead-tin solder layer (34') over the metal mask forming a solder bump (34') on each said final metal contact pad and, g) reflowing each said solder bump to form a solder ball (34), whereby the metal contact terminals are formed (35) at each final metal contact pad.
Claim 10
Dependent Claim
19 words
The method of claim 7 wherein the metal mask of step a) is the metal mask of step e).
Claim 11
Dependent Claim
15 words
The method of claim 7 wherein said metal layer consists of a composite Cr-Cr/Cu-Cu-Au layer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-11 | 1996-02-10 | 1996-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-11 | 2000-02-10 | 2000-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-11 | 2004-02-10 | 2004-08-11 | $7700.00 | Window Closed / Lapsed |