Assignee: International Business Machines Corp
•
Filing: 1993-04-14
•
Granted: 1994-08-23
•
Expires: 2013-04-14
Abstract
Abstract The present invention is directed to a method for forming a self-aligned epitaxial base transistor in a double polysilicon type process using non-selective low temperature epitaxy (LTE) to form the base layer. The present invention utilizes a thin very heavily doped LTE layer that is both a conductive etch stop and a diffusion source for doping the extrinsic base of the transistor. The deposition of the non-selective LTE base layer is followed immediately by the deposition of the conductive etch stop layer. A layer of undoped polycrystalline semiconductor is deposited on the conductive etch stop layer and subsequently ion implanted. Oxide and nitride insulating layers are deposited and the structure is patterned using a highly directional reactive ion etch to form the emitter window leaving a thin layer of the polycrystalline layer. The thin polycrystalline layer is selectively removed in a KOH solution leaving the conductive etch stop layer. The portion of the etch stop layer exposed in the emitter window is selectively removed by oxidation. Thereafter, conventional double polysilicon processing techniques are continued to form the insulator sidewalls and the emitter region in the window. During an annealing drive-in step, the conductive etch stop layer acts as an additional dopant source to the extrinsic base. The etch stop layer provides a conductive contact between the instrinsic base and the extrinsic base of the transistor.
Inventors
- 👤 Ernest Bassous
- 👤 Gary L. Patton
- 👤 Johannes M. C. Stork
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:37
CPC Classifications
H; H10; H10D; H10D10/00; H10D10/01; H10D10/051; H10D10/054; H10D10/021; H10D10/80; H10D10/821; H10D10/891; H10D62/00; H10D62/10; H10D62/17; H10D62/177; H10P; H10P14/00; H10P14/20; H10P14/24; H10P14/29; H10P14/2901; H10P14/2902; H10P14/2905; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; Y; Y10; Y10S; Y10S148/00; Y10S148/011; Y10S148/124
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
267 words
A method for forming a self-aligned epitaxial base transistor comprising the steps of: (a) depositing an intrinsic base layer of epitaxial semiconductor on a substrate structure having shallow and deep trench isolation regions defining a collector region doped with a first conductivity type, said intrinsic base layer being doped with a second conductivity type; (b) depositing a conductive etch stop layer of heavily doped epitaxial semiconductor on said intrinsic base layer, said conductive etch stop layer having a thickness substantially thinner than said intrinsic base layer and being heavily doped with said second conductivity type; (c) depositing an extrinsic base layer of undoped polycrystalline semiconductor on said conductive etch stop layer, and implanting a dopant of said second conductivity type in an upper surface of said extrinsic base layer; (d) depositing an oxide layer on said extrinsic base layer; (e) depositing a nitride layer on said oxide layer; (f) forming an emitter window vertically through said nitride and oxide layers and a portion of said extrinsic base layer; (g) selectively removing the remaining portion of said extrinsic base layer within said emitter window; (h) selectively oxidizing said conductive etch stop layer within said emitter window; (i) forming oxide and nitride sidewalls within said emitter window; and (j) forming an emitter region of polycrystalline semiconductor within said emitter window, said emitter region being doped with said first conductivity type; and, (k) driving dopant of said second conductivity type from said heavily doped conductive etch stop layer into said undoped extrinsic base layer and from said upper surface of said extrinsic base layer into said undoped extrinsic base layer.
Claim 2
Independent Claim
267 words
A method for forming a self-aligned epitaxial base transistor comprising the steps of: (a) depositing an intrinsic base layer of epitaxial semiconductor on a substrate structure having shallow and deep trench isolation regions defining a collector region doped with a first conductivity type, said intrinsic base layer being doped with a second conductivity type; (b) depositing a conductive etch stop layer of heavily doped epitaxial semiconductor on said intrinsic base layer, said conductive etch stop layer having a thickness substantially thinner than said intrinsic base layer and being heavily doped with said second conductivity type; (c) depositing an extrinsic base layer of undoped polycrystalline semiconductor on said conductive etch stop layer, and implanting a dopant of said second conductivity type in an upper surface of said extrinsic base layer; (d) depositing an oxide layer on said extrinsic base layer; (e) depositing a nitride layer on said oxide layer; (f) forming an emitter window vertically through said nitride and oxide layers and a portion of said extrinsic base layer; (g) selectively removing the remaining portion of said extrinsic base layer within said emitter window; (h) selectively oxidizing said conductive etch stop layer within said emitter window; (i) forming oxide and nitride sidewalls within said emitter window; and (j) forming an emitter region of polycrystalline semiconductor within said emitter window, said emitter region being doped with said first conductivity type; and, (k) driving dopant of said second conductivity type from said heavily doped conductive etch stop layer into said undoped extrinsic base layer and from said upper surface of said extrinsic base layer into said undoped extrinsic base layer.
Claim 3
Dependent Claim
37 words
The method of claim 1 further including the step of depositing a nitride sidewall layer in said emitter window prior to the selective removal of the remaining portion of the extrinsic base layer within said emitter window.
Claim 4
Dependent Claim
25 words
The method of claim 1 wherein said intrinsic base layer, said conducting etch stop layer and said extrinsic base layer are each formed of silicon.
Claim 5
Dependent Claim
31 words
The method of claim 1 wherein the intrinsic base layer is formed of a compound semiconductor, and, said conducting etch stop layer and said extrinsic base layer are formed of silicon.
Claim 6
Dependent Claim
12 words
The method of claim 4 wherein the compound semiconductor is silicon germanium.
Claim 7
Dependent Claim
16 words
The method of claim 1 wherein the intrinsic base layer is deposited by low temperature epitaxy.
Claim 8
Dependent Claim
21 words
The method of claim 6 wherein the low temperature epitaxy is performed using an ultra high vacuum chemical vapor deposition process.
Claim 9
Dependent Claim
17 words
The method of claim 1 wherein the conductive etch stop layer is deposited by low temperature epitaxy.
Claim 10
Dependent Claim
21 words
The method of claim 8 wherein the low temperature epitaxy is performed using an ultra high vacuum chemical vapor deposition process.
Claim 11
Dependent Claim
24 words
The method of claim 1 wherein said conductive etch stop layer is deposited to a thickness in the range of 10 to 20 nm.
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein the extrinsic base layer is deposited by low pressure chemical vapor deposition.
Claim 13
Dependent Claim
21 words
The method of claim 11 wherein the extrinsic base layer is ion implanted with the dopant of the second conductivity type.
Claim 14
Dependent Claim
63 words
The method of claim 1 wherein the intrinsic base layer and the conductive etch stop layer are deposited in a single deposition process in which the dopant concentration of said intrinsic base layer is abruptly increased from a range of about 10 17 -10 19 cm -3 to a concentration of about 10 21 cm -3 to form said conductive etch stop layer.
Claim 15
Dependent Claim
16 words
The method of claim 1 wherein the emitter window is formed by a reactive ion etch.
Claim 16
Dependent Claim
16 words
The method of claim 14 wherein the reactive ion etch is a highly directional timed etch.
Claim 17
Dependent Claim
21 words
The method of claim 1 wherein the remaining portion of said extrinsic base layer is selectively removed in a KOH solution.
Claim 18
Dependent Claim
36 words
The method of claim 1 wherein the step of forming said emitter region further includes the step of annealing, said conductive etch stop layer being a dopant source for said extrinsic base layer during said annealing.
References Cited (Backward Citations)
US3929528A
Cited
US4338622A
Cited
US4534806A
Cited
US4381953A
Cited
US4733287A
Cited
US4641416A
Cited
US4703554A
Cited
US5006912A
Cited
JPS63289863A
Cited
US4892837A
Cited
US5008207A
Cited
US5132765A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1997-08-22 | 1998-02-21 | 1998-08-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2001-08-22 | 2002-02-21 | 2002-08-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2005-08-22 | 2006-02-21 | 2006-08-23 | $7700.00 | Window Closed / Lapsed |