Abstract
Abstract A low dielectric, low temperature fired glass ceramic produced by firing at about 800 DEG -900 DEG C. a mixture comprising at least one glass consisting of, by weight percent, 0 to 50% B2O3, 35 to 65% CaO, and 10 to 65% SiO2, and selected from the glasses of CaO-B2O3-SiO2 glass system. The glass ceramic is light weight, exhibits a dielectric constant of less than about 7.9, has adequate mechanical strength and thermal conductivity, and is compatible with precious metal conductors. The glass ceramic is useful in the manufacture of integrated circuits and any other electronic or mechanical components where a glass ceramic exhibiting this particular combination of characteristics is suitable.
Inventors
- 👤 S. K. Muralidhar
- 👤 Gordon J. Roberts
- 👤 Aziz S. Shaikh
- 👤 David J. Leandri
- 👤 Dana L. Hankey
- 👤 Thomas J. Vlach
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:09
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/02; H01B3/08; H01B3/087; C; C03; C03C; C03C10/00; C03C10/0054; C03C14/00; C03C14/004; C03C8/00; C03C8/22; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; C03C2214/00; C03C2214/04; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
145 words
A composition for producing glass ceramic dielectric compositions for use in multilayer circuits, said composition comprising water or an organic dispersing medium and at least one glass composition dispersed in said water or said organic dispersing medium, said glass composition comprising: (A) at least one glass from the CaO-B 2 O 3 -SiO 2 system, said at least one glass from the CaO-B 2 O 3 -SiO 2 system having a composition comprising up to about 55% by weight B 2 O 3 , about 35% to about 55% by weight CaO, and about 10% to about 65% by weight SiO 2 ; and (B) at least one glass comprising in excess of about 60% by weight SiO 2 , up to about 30% by weight B 2 O 3 , and up to about 10% by weight of at least one alkali metal oxide.
Claim 2
Dependent Claim
145 words
A composition for producing glass ceramic dielectric compositions for use in multilayer circuits, said composition comprising water or an organic dispersing medium and at least one glass composition dispersed in said water or said organic dispersing medium, said glass composition comprising: (A) at least one glass from the CaO-B 2 O 3 -SiO 2 system, said at least one glass from the CaO-B 2 O 3 -SiO 2 system having a composition comprising up to about 55% by weight B 2 O 3 , about 35% to about 55% by weight CaO, and about 10% to about 65% by weight SiO 2 ; and (B) at least one glass comprising in excess of about 60% by weight SiO 2 , up to about 30% by weight B 2 O 3 , and up to about 10% by weight of at least one alkali metal oxide.
Claim 3
Dependent Claim
32 words
A composition as set forth in claim 1 wherein said glass (A) comprises 32% by weight B 2 O 3 , 39% by weight CaO and 29% by weight SiO 2 .
Claim 4
Dependent Claim
51 words
A composition as set forth in claim 1 wherein said glass (B) comprises about 71% by weight SiO 2 , about 26% by weight B 2 O 3 , about 0.5% by weight Na 2 O, about 1% by weight K 2 O and about 0.5% by weight Li 2 O.
Claim 5
Dependent Claim
21 words
A composition as set forth in claim 1 further comprising about 1% by weight crystallizing agent CaB 2 O 4 .
Claim 6
Dependent Claim
130 words
A composition for producing glass ceramic dielectric compositions for use in cofired multilayer circuits comprising a mixture comprising: (A) a glass powder from the CaO-B 2 O 3 -SiO 2 system and having an average particle size of about 1 to 10 μm, said glass powder from the CaO-B 2 O 3 -SiO 2 system having a composition comprising about 32% by weight B 2 O 3 , about 39% by weight CaO, and about 29% by weight SiO 2 ; and (B) a glass powder having an average particle size of about 1 to about 10 μm and having a composition comprising about 40% by weight CaO, about 50% by weight SiO 2 , and about 10% by weight B 2 O 3 ; and (C) an organic binder.
Claim 7
Dependent Claim
130 words
A composition for producing glass ceramic dielectric compositions for use in cofired multilayer circuits comprising a mixture comprising: (A) a glass powder from the CaO-B 2 O 3 -SiO 2 system and having an average particle size of about 1 to 10 μm, said glass powder from the CaO-B 2 O 3 -SiO 2 system having a composition comprising about 32% by weight B 2 O 3 , about 39% by weight CaO, and about 29% by weight SiO 2 ; and (B) a glass powder having an average particle size of about 1 to about 10 μm and having a composition comprising about 40% by weight CaO, about 50% by weight SiO 2 , and about 10% by weight B 2 O 3 ; and (C) an organic binder.
Claim 8
Dependent Claim
24 words
The composition of claim 5 wherein the produced glass ceramic dielectric compositions have a dielectric constant of less than about 7 at 10 megahertz.
Claim 9
Dependent Claim
152 words
A glass ceramic dielectric composition for use with an alumina substrate produced by firing a composition comprising a mixture comprising: (A) a glass powder from the CaO-B 2 O 3 -SiO 2 system and having an average particle size of about 3 to 6 μm and having a composition comprising about 26% by weight B 2 O 3 , about 42% by weight CaO, and about 32% by weight SiO 2 ; (B) a glass powder having an average particle size of about 3 to about 6 μm and having a composition comprising about 71% by weight SiO 2 , about 26% by weight B 2 O 3 , about 0.5% by weight Na 2 O, about 1% by weight K 2 O, about 0.5% by weight Li 2 O; and (C) CaB 2 O 4 having an average particle size of about 1 to 3 μm; and (D) an organic vehicle.
Claim 10
Dependent Claim
152 words
A glass ceramic dielectric composition for use with an alumina substrate produced by firing a composition comprising a mixture comprising: (A) a glass powder from the CaO-B 2 O 3 -SiO 2 system and having an average particle size of about 3 to 6 μm and having a composition comprising about 26% by weight B 2 O 3 , about 42% by weight CaO, and about 32% by weight SiO 2 ; (B) a glass powder having an average particle size of about 3 to about 6 μm and having a composition comprising about 71% by weight SiO 2 , about 26% by weight B 2 O 3 , about 0.5% by weight Na 2 O, about 1% by weight K 2 O, about 0.5% by weight Li 2 O; and (C) CaB 2 O 4 having an average particle size of about 1 to 3 μm; and (D) an organic vehicle.
Claim 11
Dependent Claim
38 words
The dielectric composition of claim 7 having a dielectric constant of less than about 5.2 at 1 megahertz, a breakdown voltage of greater than about 500 volts per mil, and a tan δ of less than about 0.3%.
Claim 12
Dependent Claim
102 words
A glass composition suitable for use in tapes for multilayer circuits and pastes for thick film hybrid circuits which upon firing form a glass ceramic dielectric composition, said glass composition comprising (A) about 20% to about 80% by weight of at least one crystallized glass from the CaO-B 2 O 3 -SiO 2 system having a composition comprising up to about 55% by weight B 2 O 3 , from about 35% to about 55% by weight CaO and from about 10% to about 65% by weight SiO 2 ; (B) a separate and distinct addition of CaB 2 O 4 .
Claim 13
Dependent Claim
102 words
A glass composition suitable for use in tapes for multilayer circuits and pastes for thick film hybrid circuits which upon firing form a glass ceramic dielectric composition, said glass composition comprising (A) about 20% to about 80% by weight of at least one crystallized glass from the CaO-B 2 O 3 -SiO 2 system having a composition comprising up to about 55% by weight B 2 O 3 , from about 35% to about 55% by weight CaO and from about 10% to about 65% by weight SiO 2 ; (B) a separate and distinct addition of CaB 2 O 4 .
Claim 14
Dependent Claim
35 words
A glass composition as set forth in claim 9 wherein said crystallized glass (A) comprises about 26% by weight B 2 O 3 , about 42% by weight CaO and about 32% SiO 2 .
Claim 15
Dependent Claim
49 words
A glass composition as set forth in claim 9 including a noncrystallized glass (C) comprising about 60% or more by weight SiO 2 , up to about 30% by weight B 2 O 3 , and up to about 10% by weight of at least one alkali metal oxide.
Claim 16
Dependent Claim
19 words
A glass composition as set forth in claim 9 comprising about 1% by weight CaB 2 O 4 .
Claim 17
Dependent Claim
22 words
A glass composition as set forth in claim 11 comprising about 20% to about 80% by weight of said noncrystallized glass (C).
Claim 18
Dependent Claim
53 words
A glass composition as set forth in claim 11 wherein said noncrystallized glass (C) comprises about 60% by weight SiO 2 , about 26% by weight B 2 O 3 , about 0.5% by weight Na 2 O, about 1.0% by weight K 2 O and about 0.5% by weight LiO 2 .
Claim 19
Dependent Claim
115 words
A composition for producing glass ceramic dielectric compositions, said composition comprising: (A) at least one glass from the CaO-B 2 O 3 -SiO 2 system, said at least one glass from the CaO-B 2 O 3 -SiO 2 system having a composition comprising up to about 50% by weight B 2 O 3 , about 35% to about 55% by weight CaO, and about 10% to about 65% by weight SiO 2 ; and (B) at least one glass comprising in excess of about 60% by weight SiO 2 , up to about 30% by weight B 2 O 3 , and up to about 10% by weight of at least one alkali metal oxide.
Claim 20
Dependent Claim
115 words
A composition for producing glass ceramic dielectric compositions, said composition comprising: (A) at least one glass from the CaO-B 2 O 3 -SiO 2 system, said at least one glass from the CaO-B 2 O 3 -SiO 2 system having a composition comprising up to about 50% by weight B 2 O 3 , about 35% to about 55% by weight CaO, and about 10% to about 65% by weight SiO 2 ; and (B) at least one glass comprising in excess of about 60% by weight SiO 2 , up to about 30% by weight B 2 O 3 , and up to about 10% by weight of at least one alkali metal oxide.
References Cited (Backward Citations)
DE232767C
Cited
DE209776C
Cited
US3816172A
Cited
US4084975A
Cited
US4084976A
Cited
US4301324A
Cited
US4413061A
Cited
JPS5571646A
Cited
US4323652A
Cited
US4443550A
Cited
US4547625A
Cited
US4764233A
Cited
US4435511A
Cited
US4532221A
Cited
US4547467A
Cited
US4598167A
Cited
US4649125A
Cited
US4642148A
Cited
EP0163155A1
Cited
US4621066A
Cited
US4752531A
Cited
US4654095A
Cited
US4593006A
Cited
US4672152A
Cited
US4749665A
Cited
US4830988A
Cited
US4714687A
Cited
US4861646A
Cited
US4816615A
Cited
US4849379A
Cited
WO1990000966A1
Cited
WO1991002363A1
Cited
US5071794A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-11-01 | 1997-05-03 | 1997-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-11-01 | 2001-05-03 | 2001-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-11-01 | 2005-05-03 | 2005-11-02 | $7700.00 | Window Closed / Lapsed |