Low temperature fired ceramics
Assignee: Murata Manufacturing Co Ltd
•
Filing: 1985-03-27
•
Granted: 1986-11-04
•
Expires: 2005-03-27
Abstract
Abstract Low temperature fired ceramics produced by firing at a low temperature a mixture consisting of, in weight percentages: (a) 50 to 65% of powder glass consisting of 10 to 55% of CaO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 and up to 10% of impurities; and (b) 50 to 35% of powder Al 2 O 3 containing up to 10% of impurities. The glass component (a) may further contains B 2 O 3 up to 20% based on the total weight of the former glass-forming components. The ceramics exhibit excellent thermal conductivity, high mechanical strength, low thermal expansion and small dielectric constant and such advantageous combination of properties make them useful in many applications, more especially highly suited to the use as substrate of various electronic parts, components or multilayer integrated circuits. Also, since the ceramics can be prepared at lower firing temperatures and a higher heating rate, the production cost and time can be advantageously saved.
Inventors
- 👤 Susumu Nishigaki
- 👤 Shinsuke Yano
- 👤 Shirohito Matsuyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 09:56
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/02; H01B3/08; C; C03; C03C; C03C10/00; C03C10/0036; H01B3/12; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/129; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/46; H05K3/4611; H05K3/4626; H05K3/4629
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
81 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of from 800° to 1000° C., a mixture consisting essentially of, in weight percentages: (a) 50 to 65% of powdered, noncrystalline, glass consisting of 10to 55% of CaO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , and up to 10% of impurities; and (b) 50 to 35% of powdered Al 2 O 3 containing up to 10% of impurities.
Claim 2
Dependent Claim
81 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of from 800° to 1000° C., a mixture consisting essentially of, in weight percentages: (a) 50 to 65% of powdered, noncrystalline, glass consisting of 10to 55% of CaO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , and up to 10% of impurities; and (b) 50 to 35% of powdered Al 2 O 3 containing up to 10% of impurities.
Claim 3
Dependent Claim
51 words
A partially crystallized ceramic article as claimed in claim 1 and having the properties: (i) a thermal expansion coefficient of from 4.8×10 -6 to 7×10 -6 /°C., (ii) a dielectric constant of 6.5 to 9, at 1 MH z , and (iii) a density of 2.7 to 3.2 g/cm 3 .
Claim 4
Dependent Claim
37 words
A partially crystaillized ceramic article as claimed in claim 1 which consists essentially of a noncrystallized glass phase, alumina and a crystallized phase of anorthite or anorthite plus calcium silicate formed by partial crystallization of glass (a).
Claim 5
Dependent Claim
70 words
A partially crystallized ceramic article as claimed in claim 1 in which said powdered, noncrystalline glass (a) was prepared by melting CaO, SiO 2 and Al 2 O 3 , or their corresponding carbonates or hydroxides, at a temperature of 1300° to 1450° C., to form molten glass then pouring the molten glass into water to obtain glass frit and then milling the glass frit to obtain the glass (a).
Claim 6
Dependent Claim
99 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of from 800° to 1000° C., a mixture consisting essentially of, in weight percentages: (a) 50 to 65% of powdered, noncrystalline, glass consisting of (i) 10 to 55% of CaO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , and up to 10% of impurities; and (ii) up to 20% of B 2 O 3 , based on the total weight of (i); and (b) 50 to 35% Al 2 O 3 containing up to 10% of impurities.
Claim 7
Dependent Claim
99 words
A partially crystallized ceramic article which has been prepared by firing at a temperature of from 800° to 1000° C., a mixture consisting essentially of, in weight percentages: (a) 50 to 65% of powdered, noncrystalline, glass consisting of (i) 10 to 55% of CaO, 45 to 70% of SiO 2 , 0 to 30% of Al 2 O 3 , and up to 10% of impurities; and (ii) up to 20% of B 2 O 3 , based on the total weight of (i); and (b) 50 to 35% Al 2 O 3 containing up to 10% of impurities.
Claim 8
Dependent Claim
51 words
A partially crystallized ceramic article as claimed in claim 5 and having the properties: (i) a thermal expansion coefficent of from 4.8×10 -6 to 7×10 -6 /°C., (ii) a dielectric constant of 6.5 to 9, at 1 MH z , and (iii) a density of 2.7 to 3.2 g/cm 3 .
Claim 9
Dependent Claim
37 words
A partially crystallized ceramic article as claimed in claim 5 which consists essentially of a noncrystallized glass phase, alumina and a crystallized phase of anorthite or anorthite plus calcium silicate formed by partial crystallization of glass (a).
Claim 10
Dependent Claim
75 words
A paritally crystallized ceramic article as claimed in claim 5 in which said powdered, noncrystalline glass (a) was prepared by melting CaO, SiO 2 , Al 2 O 3 and B 2 O 3 , or their corresponding carbonates or hydroxides, at a temperature of 1300° to 1450° C., to form molten glass then pouring the molten glass into water to obtain glass frit and then milling the glass frit to obtain the glass (a).
References Cited (Backward Citations)
US3471306A
Cited
US3847582A
Cited
US3923528A
Cited
DE2460931A1
Cited
JPS50119814A
Cited
US4187115A
Cited
US4522926A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-03 | 1990-05-05 | 1990-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-03 | 1994-05-05 | 1994-11-04 | $3760.00 | Window Closed / Lapsed |