Aqueous silicone dispersions comprised of aminosilanes/amidosilanes and crosslinkable into elastomeric state
Assignee: Rhodia Chimie SAS
•
Filing: 1990-02-05
•
Granted: 1992-08-18
•
Expires: 2010-02-05
Abstract
Abstract Aqueous silicone dispersions crosslinkable into elastomeric state upon removal of water therefrom, well adapted for the production of paints and silicone elastomer seals, e.g., for the construction industry, include: (A) 100 parts by weight of an oil-in-water emulsion of an α,ω-(dihydroxy)polydiorganosiloxane, stabilized with an anionic and/or nonionic surfactant; (B) 0.1 to 20 parts by weight of an aminosilane and/or amidosilane; (C) 0 to 3 parts by weight of a metal curing catalyst; and (D) 0 to 250 parts by weight of a non-siliceous inorganic filler, such emulsion having a pH of from 7 to 13 and a dry solids content of at least 40%.
Inventors
- 👤 Michel Feder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 18:13
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; A; A61; A61K; A61K9/00; A61K9/20; A61K9/28; A61K9/2806; A61K9/2833; A61K9/2853; C08J2383/00; C08J2383/04; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31663; Y10T428/3167
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
182 words
An aqueous silicone dispersion crosslinkable into elastomeric state upon removal of water therefrom under ambient conditions, comprising: (A) 100 parts by weight of an oil-in-water emulsion of an α,ω-(dihydroxy)polydiorganosiloxane, stabilized with at least one anionic or nonionic surfactant, or mixture thereof; (B) 0.1 to 20 parts by weight of a silane of the formula: in which X is a hydrolyzable amino or amido radical, in which the N-atom is directly linked to the Si-atom; R 1 is a monovalent C 1 -C 13 hydrocarbon radical; R 2 is a C 1 -C 8 alkyl radical, alkyl ether radical, alkyl ester radical or cyanoalkyl radical, or a C 7 -C 13 aralkyl radical; a is an integer equal to 2, 3 or 4; b is an integer equal to 0 to 1; and a+b is equal to 2, 3 or 4; (C) 0 to 3 parts by weight of a catalytic metal curing compound; (D) 0 to 250 parts by weight of a non-siliceous inorganic filler; and said dispersion having a pH above 7 and a dry solids content of at least 40%.
Claim 2
Dependent Claim
182 words
An aqueous silicone dispersion crosslinkable into elastomeric state upon removal of water therefrom under ambient conditions, comprising: (A) 100 parts by weight of an oil-in-water emulsion of an α,ω-(dihydroxy)polydiorganosiloxane, stabilized with at least one anionic or nonionic surfactant, or mixture thereof; (B) 0.1 to 20 parts by weight of a silane of the formula: in which X is a hydrolyzable amino or amido radical, in which the N-atom is directly linked to the Si-atom; R 1 is a monovalent C 1 -C 13 hydrocarbon radical; R 2 is a C 1 -C 8 alkyl radical, alkyl ether radical, alkyl ester radical or cyanoalkyl radical, or a C 7 -C 13 aralkyl radical; a is an integer equal to 2, 3 or 4; b is an integer equal to 0 to 1; and a+b is equal to 2, 3 or 4; (C) 0 to 3 parts by weight of a catalytic metal curing compound; (D) 0 to 250 parts by weight of a non-siliceous inorganic filler; and said dispersion having a pH above 7 and a dry solids content of at least 40%.
Claim 3
Dependent Claim
59 words
The aqueous silicone dispersion of claim 1, wherein the amino radicals, X, are of the formula: R.sub.3 NH-- and amido radicals are of the formula: ##STR3## wherein R 3 is a C 1 -C 6 alkyl radical, a phenyl radical or a cyclohexyl radical and R 4 is a C 1 -C 6 alkyl radical or a phenyl radical.
Claim 4
Dependent Claim
20 words
The aqueous silicone dispersion as defined by claim 1, comprising 0.01 to 3 parts of said metal curing compound (C).
Claim 5
Dependent Claim
21 words
The aqueous silicone dispersion as defined by claim 2, said metal compound (C) comprising an aqueous emulsion of an organotin salt.
Claim 6
Dependent Claim
23 words
The aqueous silicone dispersion as defined by claim 1, said emulsion (A) having a dry solids content of at least 45% by weight.
Claim 7
Dependent Claim
44 words
The aqueous silicone dispersion as defined by claim 1, said filler (D) comprising 5 to 200 parts by weight of hydrated alumina, alumina, calcium carbonate, expanded vermiculite, non-expanded vermiculite, carbon black, zinc oxide, titanium dioxide, mica, talc, iron oxide, barium sulfate or slaked lime.
Claim 8
Dependent Claim
25 words
The aqueous silicone dispersion as defined by claim 6, said filler (D) comprising calcium carbonate having a mean particle diameter of less than 0.1 μm.
Claim 9
Dependent Claim
104 words
The aqueous silicone dispersion as defined by claim 1, comprising: (A) 100 parts by weight of an oil-in-water emulsion of an α,ω-(dihydroxy)polydiorganosiloxane having a viscosity at 25° C. of from 50,000 to 1,500,000 mPa.s, such emulsion being stabilized with an alkali metal salt of an aromatic hydrocarbon-based sulfonic acid or polyoxyethylenated alkylphenol surfactant; (B) 0.5 to 10 parts by weight of silane; (C) 0.05 to 2 parts by weight of a diorganotin dicarboxylate; (D) 10 to 20 parts by weight of an inorganic filler; and said emulsion having a pH ranging from 8 to 13 and a dry solids content of at least 60%.
Claim 10
Dependent Claim
107 words
The silicone dispersion as defined in claim 1, further comprising, per 100 parts by weight of emulsion (A), 1 to 40 parts by weight of a hydroxylated silicone resin (F) which comprises, per molecule, at least two different recurring units selected from among those of the formulae R 3 SiO 0 .5, R 2 SiO, RSiO 1 .5 and SiO 2 , wherein the radicals R, which may be identical or different, are vinyl, phenyl or 3,3,3-trifluoropropyl radicals, or linear or branched chain alkyl radicals having from 1 to 6 carbon atoms, said resin (F) having a weight content of hydroxyl groups ranging from 0.1% to 10%.
Claim 11
Dependent Claim
22 words
The aqueous silicone dispersion as defined by claim 1, comprising a pH-adjusting amount of an alkali metal or alkaline earth metal hydroxide.
Claim 12
Dependent Claim
13 words
The aqueous silicone dispersion as defined by claim 1, in crosslinked elastomeric state.
Claim 13
Dependent Claim
14 words
A substrate article coated with the aqueous silicone dispersion as defined by claim 1.
Claim 14
Dependent Claim
12 words
A substrate article coated with the elastomer as defined by claim 11.
Claim 15
Dependent Claim
15 words
The substrate article as defined by claim 12, comprising a coated pharmaceutical or agricultural chemical.
Claim 16
Dependent Claim
12 words
The substrate article as defined by claim 12, comprising a bottle cork.
Claim 17
Dependent Claim
11 words
A shaped article comprising the elastomer as defined by claim 11.
Claim 18
Dependent Claim
38 words
The aqueous silicone dispersion as defined by claim 1, further comprising: (E) a silicon-containing additive selected from sodium silicate (0.3 to 30 parts by weight) and a siliceous reinforcing or semi-reinforcing filler (1 to 150 parts by weight).
Claim 19
Dependent Claim
70 words
The aqueous silicone dispersion as defined by claim 17, further comprising, per 100 parts by weights of the emulsion (A), 0.3 to 30 parts by weight of sodium silicate and 100 to 150 parts by weight of a siliceous reinforcing or semi-reinforcing filler, with the proviso that the sum of the parts by weight of (D)+(E) is less than 300 parts by weight per 100 parts by weight of (A).
References Cited (Backward Citations)
US2676182A
Cited
US2891920A
Cited
FR1248826A
Cited
US3294725A
Cited
US3364160A
Cited
FR1423477A
Cited
US3360491A
Cited
US3355406A
Cited
US3697469A
Cited
US3779967A
Cited
FR2064563A5
Cited
GB1289900A
Cited
FR2094322A5
Cited
US3925242A
Cited
FR2110358A1
Cited
US3706695A
Cited
GB1336195A
Cited
FR2114230A5
Cited
FR2195655A1
Cited
US4052331A
Cited
US3862919A
Cited
US4028339A
Cited
US4152343A
Cited
US4056492A
Cited
US4221688A
Cited
US4244849A
Cited
FR2463163A1
Cited
GB2056473A
Cited
US4322518A
Cited
US4496687A
Cited
US4525502A
Cited
US4554187A
Cited
US4535109A
Cited
EP0143541A1
Cited
EP0147323A2
Cited
EP0169098A1
Cited
US4624900A
Cited
US4618642A
Cited
EP0201284A2
Cited
US4618645A
Cited
US4608412A
Cited
EP0212827A2
Cited
EP0235049A1
Cited
US4749766A
Cited
US4717599A
Cited
WO1988009923A2
Cited
US4978710A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-08-18 | 1996-02-17 | 1996-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-08-18 | 2000-02-17 | 2000-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-08-18 | 2004-02-17 | 2004-08-18 | $7700.00 | Window Closed / Lapsed |