Stable silicone emulsions
Assignee: Momentive Performance Materials GmbH
•
Filing: 1984-06-21
•
Granted: 1985-11-19
•
Expires: 2004-06-21
Abstract
Abstract A silicone emulsion which can be converted into an elastomeric product under ambient conditions by eliminating and evaporating water and alcohol or carboxylic acid, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 1 to 400 parts of a low molecular weight, reactive acyloxy or alkoxy-functional silicone resin, (C) 0.1 to 20 parts of a catalytic compound, (D) 0 to 200 parts of a thixotropic filler and (E) 0 to 200 parts by weight of a non-thixotropic filler, the silicone emulsion having a solids content of about 20 to 85% by weight. The emulsion is especially suited for coatings and sealants.
Inventors
- 👤 Wolfgang Grape
- 👤 Franz Saykowski
- 👤 Ottfried Schlak
- 👤 Thomas Wurminghausen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 21:28
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/14; C08G77/16; C08G77/18
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
102 words
A silicone emulsion which can be converted into an elastomeric product under ambient conditions by eliminating and evaporating water and alcohol or carboxylic acid, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 1-400 parts of a low molecular weight, reactive acyloxy- or alkoxyfunctional silicone resin, (C) 0.1 to 20 parts of a catalytic compound, (D) 0 to 200 parts of a thixotropic filler and (E) 0 to 200 parts by weight of a non-thixotropic filler, the silicone emulsion having a solid content of about 20 to 85% by weight.
Claim 2
Dependent Claim
102 words
A silicone emulsion which can be converted into an elastomeric product under ambient conditions by eliminating and evaporating water and alcohol or carboxylic acid, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 1-400 parts of a low molecular weight, reactive acyloxy- or alkoxyfunctional silicone resin, (C) 0.1 to 20 parts of a catalytic compound, (D) 0 to 200 parts of a thixotropic filler and (E) 0 to 200 parts by weight of a non-thixotropic filler, the silicone emulsion having a solid content of about 20 to 85% by weight.
Claim 3
Dependent Claim
72 words
An emulsion according to claim 1, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 50 to 400 parts of a low molecular weight alkoxyfunctional silicone resin, (C) 0.1 to 20 parts of an alkyltin salt, and (D) 0 to 20 parts of a thixotropic filler, the total mixture having a solid content of about 30 to 60% by weight.
Claim 4
Dependent Claim
72 words
An emulsion according to claim 1, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 50 to 200 parts of a low molecular weight alkoxyfunctional silicone resin, (C) 0.1 to 10 parts of an alkyltin salt, and (D) 0 to 20 parts of a thixotropic filler, the total mixture having a solid content of about 30 to 50% by weight.
Claim 5
Dependent Claim
33 words
In the coating of a surface with a silicone composition, and drying, the improvement which comprises employing as the silicone composition an aqueous emulsion, containing an alkoxyfunctional silicone resin, according to claim 1.
Claim 6
Dependent Claim
81 words
An emulsion according to claim 1, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 1 to 90 parts of a low molecular weight alkoxy-functional silicone resin, (C) 0.1 to 20 parts of an alkyltin salt, (D) 2.5 to 200 parts of a thixotropic filler, and (E) 0 to 200 parts of a non-thixotropic filler, the total mixture having a solid content of about 60 to 85% by weight.
Claim 7
Dependent Claim
81 words
An emulsion according to claim 1, comprising by weight approximately (A) 100 parts of a hydroxyl-terminated polydiorganosiloxane having a molecular weight of at least about 50,000, (B) 4 to 40 parts of a low molecular weight alkoxy-functional silicone resin, (C) 0.1 to 10 parts of an alkyltin salt, (D) 2.5 to 200 parts of a thixotropic filler, and (E) 20 to 200 parts of a non-thixotropic filler, the total mixture having a solid content of about 60 to 85% by weight.
Claim 8
Dependent Claim
32 words
In the joinder of a material to another material employing a sealant, the improvement which comprises employing as the sealant an aqueous emulsion, containg an alkoxyfunctional silicone resin, according to claim 1.
Claim 9
Dependent Claim
46 words
The process for preparing a silicone emulsion according to claim 1, comprising mixing an aqueous emulsion of the hydroxyl-terminated polydiorganosiloxane with an aqueous emulsion of the alkoxy-functional silicone resin, the catalyst and fillers if present being added to either of the individual emulsions or the mixture.
Claim 10
Dependent Claim
32 words
The process according to claim 8, wherein the aqueous emulsion of the hydroxyl-terminated polydiorganosiloxane is produced by polymerizing a diorganosiloxane in water in the presence of a catalyst and an emulsifying agent.
Claim 11
Dependent Claim
28 words
The process according to claim 8, wherein the alkoxyfunctional silicone resin is produced by reacting an alkylchlorosilane with an alkanol and water, and is emulsified in water afterwards.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-11-18 | 1989-05-20 | 1989-11-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-11-18 | 1993-05-20 | 1993-11-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-11-18 | 1997-05-20 | 1997-11-19 | $7700.00 | Window Closed / Lapsed |