Aqueous emulsion-type silicone compositions
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1984-01-27
•
Granted: 1985-01-29
•
Expires: 2004-01-27
Abstract
Abstract The invention provides a novel organopolysiloxane-containing aqueous emulsion composition which, upon removal of water by drying at room temperature, can give a cured rubbery elastomer having excellent mechanical properties and exhibiting strong adhesion to the substrate on which it has been cured. The inventive composition is prepared by blending (A) an aqueous emulsion of an organopolysiloxane having silicon-bonded hydroxy groups and emulsified in water by use of an anionic surface active agent, (B) a mixture of a reaction product of a carboxylic acid anhydride with an amino-functional organosilane and a colloidal silica in the form of an aqueous suspension and (C) a curing catalyst in limited proportions.
Inventors
- 👤 Fumio Okada
- 👤 Toshio Oba
- 👤 Morizo Nakazato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:28
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08K; C08K13/00; C08K13/02; C08K3/00; C08K3/34; C08K3/36; C08K5/00; C08K5/04; C08K5/09; C08K5/54; C08G; C08G77/00; C08G77/04; C08G77/14; C08G77/16; C08J2383/00; C08J2383/04; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
136 words
An organopolysiloxane-containing aqueous emulsion composition which comprises (A) an aqueous organopolysiloxane emulsion comprising (A-1) 100 parts by weight of an organopolysiloxane having at least two hydroxy groups directly bonded to the silicon atoms in a molecule, (A-2) from 0.3 to 20 parts by weight of an anionic surface active agent, and (A-3) water as the dispersing medium of the components (A-1) and (A-2), (B) from 1 to 60 parts by weight as solid of a uniform dispersion comprising (B-1) from 0.1 to 20% by weight, based on the component (B-2) mentioned below as solid, of a reaction product of a carboxylic acid anhydride with an organosilane having a functional amino group in a molecule or a hydrolysis product thereof, and (B-2) a colloidal silica in an aqueous suspension, (C) a catalytic amount of a curing catalyst.
Claim 2
Dependent Claim
136 words
An organopolysiloxane-containing aqueous emulsion composition which comprises (A) an aqueous organopolysiloxane emulsion comprising (A-1) 100 parts by weight of an organopolysiloxane having at least two hydroxy groups directly bonded to the silicon atoms in a molecule, (A-2) from 0.3 to 20 parts by weight of an anionic surface active agent, and (A-3) water as the dispersing medium of the components (A-1) and (A-2), (B) from 1 to 60 parts by weight as solid of a uniform dispersion comprising (B-1) from 0.1 to 20% by weight, based on the component (B-2) mentioned below as solid, of a reaction product of a carboxylic acid anhydride with an organosilane having a functional amino group in a molecule or a hydrolysis product thereof, and (B-2) a colloidal silica in an aqueous suspension, (C) a catalytic amount of a curing catalyst.
Claim 3
Dependent Claim
21 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the organopolysiloxane has a molecular weight of at least 10,000.
Claim 4
Dependent Claim
35 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the anionic surface active agents is selected from the class consisting of esters of sulfonic acid, sulfuric acid and phosphoric acid and salts thereof.
Claim 5
Dependent Claim
38 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the amount of the anionic surface active agent is in the range from 0.5 to 5 parts by weight per 100 parts by weight of the organopolysiloxane.
Claim 6
Dependent Claim
38 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the amount of water in the component (A) is in the range from 25 to 600 parts by weight per 100 parts by weight of the organopolysiloxane.
Claim 7
Dependent Claim
80 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the oraganosilane having a functional amino group is represented by the general formula R 2 Si(CH 3 ) n-1 (OR 1 ) 4-n , in which R 1 is a monovalent group selected from the class consisting of alkyl and acyl groups, R 2 is a monovalent group selected from the class consisting of 2-aminoethyl, 3-aminopropyl and N-(2-aminoethyl)-3-aminopropyl groups and n is a positive integer of 1 or 2.
Claim 8
Dependent Claim
62 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the carboxylic acid anhydride is selected from the class consisting of the anhydrides of methyl tetrahydrophthalic acid, benzophenone tetracarboxylic acid, phthalic acid, maleic acid, pyromellitic acid, succinic acid, trimellitic acid, phenyl maleic acid, methyl hexahydrophthalic acid, hexahydrophthalic acid, dodecyl succinic acid, dichloromaleic acid and chlorendic acid, ethyleneglycol bistrimellitate and polyazelaic polyanhydride.
Claim 9
Dependent Claim
38 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the amount of the component (B) is in the range from 3 to 30 parts by weight as solid per 100 parts by weight of the organopolysiloxane.
Claim 10
Dependent Claim
33 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the curing catalyst is selected from the class consisting of organotin compounds, metal salts of organic acids, amine compounds and hydrochlorides thereof.
Claim 11
Dependent Claim
36 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 wherein the amount of the curing catalyst is in the range from 0.01 to 10 parts by weight per 100 parts by weight of the organopolysiloxane.
Claim 12
Dependent Claim
23 words
The organopolysiloxane-containing aqueous emulsion composition as claimed in claim 1 which has a value of pH in the range from 3 to 12.
Claim 13
Independent Claim
204 words
A method for the preparation of an organopolysiloxanecontaining aqueous emulsion composition comprising (A) an aqueous organopolysiloxane emulsion comprising (A-1) 100 parts by weight of an organopolysiloxane having at least two hydroxy groups directly bonded to the silicon atoms in a molecule, (A-2) from 0.3 to 20 parts by weight of an anionic surface active agent, and (A-3) water as the dispersing medium of the components (A-1) and (A-2), (B) from 1 to 60 parts by weight as solid of a uniform dispersion comprising (B-1) from 0.1 to 20% by weight, based on the component (B-2) mentioned below as solid, of a reaction product of a carboxylic acid anhydride with an organosilane having a functional amino group in a molecule or a hydrolysis product thereof, and (B-2) a colloidal silica in an aqueous suspension, and (C) a catalytic amount of a curing catalyst, which comprises the steps of: (a) dispersing the colloidal silica as the component (B-2) and the reaction product as the component (B-1) in water to form a uniform aqueous dispersion; and (b) admixing the above prepared uniform aqueous dispersion with an aqueous emulsion of the organopolysiloxane emulsified in water by the aid of the anionic surface active agent and the curing catalyst.
Claim 14
Independent Claim
204 words
A method for the preparation of an organopolysiloxanecontaining aqueous emulsion composition comprising (A) an aqueous organopolysiloxane emulsion comprising (A-1) 100 parts by weight of an organopolysiloxane having at least two hydroxy groups directly bonded to the silicon atoms in a molecule, (A-2) from 0.3 to 20 parts by weight of an anionic surface active agent, and (A-3) water as the dispersing medium of the components (A-1) and (A-2), (B) from 1 to 60 parts by weight as solid of a uniform dispersion comprising (B-1) from 0.1 to 20% by weight, based on the component (B-2) mentioned below as solid, of a reaction product of a carboxylic acid anhydride with an organosilane having a functional amino group in a molecule or a hydrolysis product thereof, and (B-2) a colloidal silica in an aqueous suspension, and (C) a catalytic amount of a curing catalyst, which comprises the steps of: (a) dispersing the colloidal silica as the component (B-2) and the reaction product as the component (B-1) in water to form a uniform aqueous dispersion; and (b) admixing the above prepared uniform aqueous dispersion with an aqueous emulsion of the organopolysiloxane emulsified in water by the aid of the anionic surface active agent and the curing catalyst.
References Cited (Backward Citations)
US3817894A
Cited
US4391765A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-01-29 | 1988-07-30 | 1989-01-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-01-29 | 1992-07-30 | 1993-01-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-01-29 | 1996-07-30 | 1997-01-29 | $7700.00 | Window Closed / Lapsed |