Self-reinforced silicon nitride ceramic with crystalline grain boundary phase, and a method of preparing the same
Assignee: Dow Chemical Co
•
Filing: 1991-02-19
•
Granted: 1992-03-24
•
Expires: 2011-02-19
Abstract
Abstract A fully densified, self-reinforced silicon nitride ceramic body of high fracture toughness and high fracture strength is disclosed comprising (a) β-silicon nitride in the form of whiskers having an average aspect ratio of at least about 2.5, and (b) a crystalline grain boundary phase having an oxynitride apatite structure, as determined by X-ray crystallography. A process for preparing the above identified silicon nitride body comprising hot-pressing a powder mixture containing silicon nitride; silica; a densification aid including strontium oxide; a conversion aid, such as, yttrium oxide; and a compound, such as, calcium oxide which enhances growth of β-silicon nitride whiskers, under conditions such that densification and the in situ formation of β-silicon nitride whiskers having a high aspect ratio occur, and thereafter annealing the densified composition for a time sufficient to produce a crystalline grain boundary phase having an oxynitride apatite structure.
Inventors
- 👤 Chinmau J. Hwang
- 👤 Aleksander J. Pyzik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:03
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/622; C04B35/64; C04B35/645; C04B35/584; C04B35/593; C04B35/71; C04B35/78; C04B35/80
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
301 words
A process for preparing a silicon nitride ceramic body containing predominantly β-silicon nitride whiskers having a high average aspect ratio and further containing a crystalline grain boundary phase having an oxynitride apatite structure, the process comprising: subjecting a powder mixture comprising (a) silicon nitride in an amount sufficient to provide a ceramic body; (b) a densification aid, said densification aid being a source of strontium, optionally, in combination with a source of an element selected from the group consisting of lithium, sodium, calcium, barium or mixture thereof, said source(s) being present in an amount sufficient to promote densification of the powder; (c) a conversion aid, said conversion aid being a source of an element selected from the group consisting of yttrium, lanthanum, cerium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, ytterbium and thorium, and mixtures thereof, said source being present in an amount sufficient to promote the conversion of the starting silicon nitride to predominantly β-silicon nitride; (d) at least one whisker growth enhancing compound in an amount sufficient to promote the formation of β-silicon nitride whiskers, said compound being a metal oxide or metal non-oxide derivative wherein the metal is selected from the group consisting of lithium, sodium, calcium, scandium, titanium and aluminum, and mixtures thereof; the optional densification aid in (b) and the whisker growth enhancing compound of (d) being derived from different elements; and (e) silica in an amount sufficient to provide the oxynitride apatite crystalline grain boundary phase; to conditions of temperature and pressure sufficient to provide for densification and in situ formation of β-silicon nitride whiskers having an average aspect ratio of at least about 2.5, and thereafter subjecting the densified composition to annealing for a time sufficient to produce a crystalline grain boundary phase having an oxynitride apatite structure, as determined by X-ray crystallography.
Claim 2
Dependent Claim
301 words
A process for preparing a silicon nitride ceramic body containing predominantly β-silicon nitride whiskers having a high average aspect ratio and further containing a crystalline grain boundary phase having an oxynitride apatite structure, the process comprising: subjecting a powder mixture comprising (a) silicon nitride in an amount sufficient to provide a ceramic body; (b) a densification aid, said densification aid being a source of strontium, optionally, in combination with a source of an element selected from the group consisting of lithium, sodium, calcium, barium or mixture thereof, said source(s) being present in an amount sufficient to promote densification of the powder; (c) a conversion aid, said conversion aid being a source of an element selected from the group consisting of yttrium, lanthanum, cerium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, ytterbium and thorium, and mixtures thereof, said source being present in an amount sufficient to promote the conversion of the starting silicon nitride to predominantly β-silicon nitride; (d) at least one whisker growth enhancing compound in an amount sufficient to promote the formation of β-silicon nitride whiskers, said compound being a metal oxide or metal non-oxide derivative wherein the metal is selected from the group consisting of lithium, sodium, calcium, scandium, titanium and aluminum, and mixtures thereof; the optional densification aid in (b) and the whisker growth enhancing compound of (d) being derived from different elements; and (e) silica in an amount sufficient to provide the oxynitride apatite crystalline grain boundary phase; to conditions of temperature and pressure sufficient to provide for densification and in situ formation of β-silicon nitride whiskers having an average aspect ratio of at least about 2.5, and thereafter subjecting the densified composition to annealing for a time sufficient to produce a crystalline grain boundary phase having an oxynitride apatite structure, as determined by X-ray crystallography.
Claim 3
Dependent Claim
50 words
The process of claim 1 wherein the β-silicon nitride whiskers have an aspect ratio of between about 2 and about 16 and are present in an amount of at least about 20 volume percent, as measured by viewing one plane of the silicon nitride ceramic body by scanning electron microscopy.
Claim 4
Dependent Claim
20 words
The process of claim 1 wherein the starting silicon nitride contains no greater than about 10 weight percent β-silicon nitride.
Claim 5
Dependent Claim
37 words
The process of claim 1 wherein the densification aid is present in an amount within a range of from about 0.04 weight percent to about 10.0 weight percent based on the total weight of the powder mixture.
Claim 6
Dependent Claim
12 words
The process of claim 4 wherein the densification aid is strontium oxide
Claim 7
Dependent Claim
37 words
The process of claim 1 wherein the conversion aid is present in an amount within a range of from about 0.2 weight percent to about 29.5 weight percent based on the total weight of the powder mixture.
Claim 8
Dependent Claim
36 words
The process of claim 1 wherein the densification aid and the conversion aid are present in amounts sufficient to provide a weight ratio of conversion aid to densification aid of from about 0.25 to about 8.
Claim 9
Dependent Claim
16 words
The process of claim 7 wherein the weight ratio is from about 1:1 to about 1.8:1.
Claim 10
Dependent Claim
12 words
The process of claim 1 wherein the conversion aid is yttrium oxide.
Claim 11
Dependent Claim
33 words
The process of claim 1 wherein the whisker growth enhancing compound is present in an amount of from about 0.01 to about 5.0 weight percent based upon total weight of the powder mixture.
Claim 12
Dependent Claim
14 words
The process of claim 1 wherein the whisker growth enhancing compound is calcium oxide.
Claim 13
Dependent Claim
43 words
The process of claim 1 wherein the powder mixture comprises silica in a total amount, including the silica present on the surface of the silicon nitride, ranging from about 2.3 to about 6 weight percent, based upon total weight of the powder mixture.
Claim 14
Dependent Claim
40 words
The process of claim 1 wherein the annealing step comprises heating the densified composition at a temperature in the range from about 1000° C. to about 1550° C. for a time ranging from about 2 hr to about 100 hr.
Claim 15
Dependent Claim
63 words
The process of claim 1 wherein the powder mixture further comprises a Palmqvist toughness enhancing amount of at least one preformed reinforcing material selected from the group consisting of β-silicon nitride in whisker and fiber form, and silicon carbide, titanium carbide, boron carbide, titanium diboride, and zirconium oxide in a form selected from the group consisting of whisker, fiber, particle and platelet forms.
Claim 16
Dependent Claim
43 words
The process of claim 14 wherein a total of the amount of silicon nitride plus the amount of preformed reinforcing material is in a range of from about 65 to about 99.75 weight percent based on the total weight of the powder mixture
Claim 17
Dependent Claim
35 words
The process of claim 15 wherein the total amount of silicon nitride plus the amount of reinforcing material is from about 80 to about 97 weight percent based upon total weight of the powder mixture.
Claim 18
Dependent Claim
82 words
The process of claim 1 wherein the powder mixture further comprises a Palmqvist toughness enhancing amount of at least one preformed, coated reinforcing material, the material being selected from the group consisting of magnesium oxide, aluminum nitride and mullite and having a coating of a material selected from the group consisting of silicon carbide, titanium carbide, boron carbide, titanium diboride, and zirconium oxide, said coated material being in a physical form selected from the group consisting of whiskers, fibers, particles and platelets.
Claim 19
Dependent Claim
44 words
The process of claim 16 wherein a total of the amount of silicon nitride plus the amount of preformed, coated reinforcing material is in a range of from about 65 to about 99.75 weight percent based on the total weight of the powder mixture.
Claim 20
Dependent Claim
21 words
The process of claim 1 wherein the densification temperature is in the range from about 1700° C. to about 1870° C.
Claim 21
Dependent Claim
21 words
The process of claim 1 wherein the densification pressure is in the range from about 3000 psig to about 6000 psig.
Claim 22
Dependent Claim
23 words
The process of claim 1 wherein the density of the silicon nitride ceramic is at least about 97 percent of the theoretical value.
Claim 23
Dependent Claim
19 words
The process of claim 1 wherein the crystallinity of the grain boundary phase is greater than about 90 percent.
Claim 24
Dependent Claim
194 words
A silicon nitride ceramic body having a Palmqvist fracture toughness greater than about 37 Kg/mm at about 23° C., comprising: (a) a crystalline phase of β-silicon nitride of which at least about 20 volume percent, as measured by viewing one plane of the silicon nitride ceramic body by scanning electron photomicrographs, is in the form of whiskers having an average aspect ratio of at least about 2.5; and (b) a crystalline grain boundary phase having an oxynitride apatite structure, as determined by X-ray crystallography, in an amount not greater than about 35 weight percent of the total weight, represented by the general formula A x B 10-x [Si(O,N) 4 ] 6 (O,N) y wherein A is strontium, optionally, in combination with an element selected from the group consisting of calcium, barium, lithium, sodium, scandium, titanium, aluminum, and mixtures thereof; B is an element selected from the group consisting of yttrium, lanthanum, cerium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, ytterbium and thorium and mixtures thereof; x is a positive number greater than 0 and equal to or less than about 4; and y is a positive number ranging from 0 to about 2.
Claim 25
Dependent Claim
194 words
A silicon nitride ceramic body having a Palmqvist fracture toughness greater than about 37 Kg/mm at about 23° C., comprising: (a) a crystalline phase of β-silicon nitride of which at least about 20 volume percent, as measured by viewing one plane of the silicon nitride ceramic body by scanning electron photomicrographs, is in the form of whiskers having an average aspect ratio of at least about 2.5; and (b) a crystalline grain boundary phase having an oxynitride apatite structure, as determined by X-ray crystallography, in an amount not greater than about 35 weight percent of the total weight, represented by the general formula A x B 10-x [Si(O,N) 4 ] 6 (O,N) y wherein A is strontium, optionally, in combination with an element selected from the group consisting of calcium, barium, lithium, sodium, scandium, titanium, aluminum, and mixtures thereof; B is an element selected from the group consisting of yttrium, lanthanum, cerium, neodymium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, ytterbium and thorium and mixtures thereof; x is a positive number greater than 0 and equal to or less than about 4; and y is a positive number ranging from 0 to about 2.
Claim 26
Dependent Claim
59 words
The body of claim 23 further comprising a Palmqvist toughness enhancing amount of at least one preformed reinforcing material selected from the group consisting of β-silicon nitride in whisker and fiber form, and silicon carbide, titanium carbide, boron carbide, titanium diboride, and zirconium oxide in a form selected from the group consisting of whisker, fiber, particle and platelet forms.
Claim 27
Dependent Claim
78 words
The body of claim 23 further comprising a Palmqvist toughness enhancing amount of at least one preformed, coated reinforcing material, the material being selected from the group consisting of magnesium oxide, aluminum nitride and mullite and having a coating of a material selected from the group consisting of silicon carbide, titanium carbide, boron carbide, titanium diboride, and zirconium oxide, said coated material being in a physical form selected from the group consisting of whiskers, fibers, particles and platelets.
Claim 28
Dependent Claim
20 words
The body of claim 23 wherein the crystallinity of the grain boundary phase is greater than about 90 volume percent.
Claim 29
Dependent Claim
29 words
The body of claim 23 wherein the Vickers hardness as measured at room temperature is in the range from about 1400 kg/mm 2 to about 1700 kg/mm 2 .
Claim 30
Dependent Claim
26 words
The body of claim 23 wherein the Palmqvist toughness, as measured at room temperature, is in the range from about 37 kg/mm to about 50 kg/mm.
Claim 31
Dependent Claim
20 words
The body of claim 23 wherein the fracture strength, as measured at 1375° C. is at least about 350 MPa.
Claim 32
Dependent Claim
10 words
A cutting tool fabricated from the body of claim 23.
References Cited (Backward Citations)
US4097293A
Cited
US4004937A
Cited
US4025351A
Cited
US3950464A
Cited
US4046580A
Cited
US4218257A
Cited
US4296065A
Cited
US4119689A
Cited
US4179301A
Cited
US4227842A
Cited
US4323325A
Cited
US4279657A
Cited
EP0100380A1
Cited
US4407970A
Cited
US4511402A
Cited
EP0079678A1
Cited
JPS5864274A
Cited
US4511525A
Cited
US4406668A
Cited
JPS5921413A
Cited
US4753764A
Cited
US4609633A
Cited
US4543345A
Cited
US4622186A
Cited
US4603116A
Cited
US4699890A
Cited
JPS6178657A
Cited
JPS6197167A
Cited
JPS61106430A
Cited
US4734234A
Cited
US4891342A
Cited
EP0228022A2
Cited
US4830991A
Cited
US4652276A
Cited
US4923829A
Cited
US4717693A
Cited
US5017531A
Cited
US5015608A
Cited
US4920085A
Cited
US5002907A
Cited
WO1989008625A1
Cited
US4870036A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1995-03-24 | 1995-09-23 | 1996-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1999-03-24 | 1999-09-23 | 2000-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2003-03-24 | 2003-09-23 | 2004-03-24 | $7700.00 | Window Closed / Lapsed |