Manufacturing method for fiber reinforced silicon ceramics sintered body
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1983-09-21
•
Granted: 1988-06-28
•
Expires: 2003-09-21
Abstract
Abstract A method for manufacturing a fiber reinforced silicon carbide or silicon nitride ceramic sintered body having silicon carbide or silicon nitride ceramic whiskers dispersed therein, which method involves mixing together silicon carbide or silicon nitride ceramic powder, whisker formation agents made up of at least one material selected from metal Si or an inorganic compound containing Si, an organic containing Si, amorphous silicon ceramic powder or a mixture of SiO2 and carbon, or Si, sintering additives, and a whisker accelerating amount of a whisker formation accelerator selected from Fe, Ni, Co, Cr, V, Ti, Ta, W or Mo; molding the mixture into a predetermined shape; heat treating the molded body at a temperature of 1300 DEG C. to 1750 DEG C. to produce silicon carbide or silicon nitride whiskers in the molded body and thereafter densifying and sintering the molded body at sintering temperatures in a non-oxidizing atmosphere. The silicon carbide and silicon nitride ceramics produced by said method have excellent heat-resistance characteristics and excellent impact and corrosion resistance, thus making these ceramics eminently suitable for structural materials where these properties are required.
Inventors
- 👤 Eiji Kamijo
- 👤 Matsuo Higuchi
- 👤 Osamu Komura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 13:13
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/584; C04B35/56; C04B35/565; C04B35/71; C04B35/78; C04B35/80; F; F02; F02B; F02B3/00; F02B3/06
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
170 words
A method for manufacturing a fiber reinforced silicon carbide or silicon nitride ceramic sintered body having silicon carbide or silicon nitride ceramic whiskers dispersed therein, said method comprising mixing together silicon carbide or silicon nitride ceramic powder, 1-75% by weight of whisker formation agents selected from the group consisting of at least one metal Si, an inorganic compound containing Si, an organic compound containing Si, an amorphous silicon ceramic powder, and a mixture of SiO 2 and carbon, or a mixture of SiO 2 and Si; sintering additives, and a whisker formation accelerator, which is at least one metal or alloy thereof selected from the group consisting of Fe, Ni, Co, Cr, V, Ti, Ta, W and Mo; molding said mixture into a predetermined shape; heat treating said molded body in a non-oxidizing atmosphere at temperatures of 1300° C. to 1750° C. to produce silicon carbide or silicon nitride whiskers in said molded body; and thereafter further densifying and sintering said molded body at sintering temperatures in a non-oxidizing atmosphere.
Claim 2
Independent Claim
170 words
A method for manufacturing a fiber reinforced silicon carbide or silicon nitride ceramic sintered body having silicon carbide or silicon nitride ceramic whiskers dispersed therein, said method comprising mixing together silicon carbide or silicon nitride ceramic powder, 1-75% by weight of whisker formation agents selected from the group consisting of at least one metal Si, an inorganic compound containing Si, an organic compound containing Si, an amorphous silicon ceramic powder, and a mixture of SiO 2 and carbon, or a mixture of SiO 2 and Si; sintering additives, and a whisker formation accelerator, which is at least one metal or alloy thereof selected from the group consisting of Fe, Ni, Co, Cr, V, Ti, Ta, W and Mo; molding said mixture into a predetermined shape; heat treating said molded body in a non-oxidizing atmosphere at temperatures of 1300° C. to 1750° C. to produce silicon carbide or silicon nitride whiskers in said molded body; and thereafter further densifying and sintering said molded body at sintering temperatures in a non-oxidizing atmosphere.
Claim 3
Independent Claim
167 words
A method for manufacturing a fiber reinforced silicon carbide or silicon nitride ceramic sintered body in which silicon carbide or silicon nitride ceramic whiskers are dispersed therein, said method comprising mixing together silicon carbide or silicon nitride ceramic powder, 1-75% by weight of whisker formation agents selected from the group consisting of at least one metal Si, an inorganic compound containing Si, an organic compound containing Si, an amorphous silicon ceramic powder, and a mixture of SiO 2 and carbon, or a mixture of SiO 2 and Si; sintered additives, and a whisker accelerating amount of a whisker formation accelerator which is at least one metal or alloy thereof selected from the group consisting of Fe, Ni, Co, Cr, V, Ti, Ta, W and Mo; applying to said mixture a heat treatment of 1300° to 1750° C. to produce silicon carbide or silicon nitride whiskers; molding said mixtures into a predetermined shape; and thereafter densifying and sintering said molded body at sintering temperatures in a non-oxidizing atmosphere.
Claim 4
Independent Claim
167 words
A method for manufacturing a fiber reinforced silicon carbide or silicon nitride ceramic sintered body in which silicon carbide or silicon nitride ceramic whiskers are dispersed therein, said method comprising mixing together silicon carbide or silicon nitride ceramic powder, 1-75% by weight of whisker formation agents selected from the group consisting of at least one metal Si, an inorganic compound containing Si, an organic compound containing Si, an amorphous silicon ceramic powder, and a mixture of SiO 2 and carbon, or a mixture of SiO 2 and Si; sintered additives, and a whisker accelerating amount of a whisker formation accelerator which is at least one metal or alloy thereof selected from the group consisting of Fe, Ni, Co, Cr, V, Ti, Ta, W and Mo; applying to said mixture a heat treatment of 1300° to 1750° C. to produce silicon carbide or silicon nitride whiskers; molding said mixtures into a predetermined shape; and thereafter densifying and sintering said molded body at sintering temperatures in a non-oxidizing atmosphere.
Claim 5
Dependent Claim
32 words
A method for manufacturing a fiber reinforced silicon carbide or silicon nitride sintered body according to claim 1, wherein the whisker accelerating agents are used in amounts of 0.01 to 5 wt.%.
Claim 6
Dependent Claim
32 words
A method of manufacturing a fiber reinforced silicon carbide or silicon nitride sintered body according to claim 2 wherein the whisker accelerating agents are used in amounts of 0.1 to 5 wt.%.
Claim 7
Dependent Claim
30 words
A method of manufacturing a fiber reinforced silicon carbide or silicon nitride sintered body according to claim 1, wherein the whiskers have a length of about 40 to 50 μm.
Claim 8
Dependent Claim
30 words
A method of manufacturing a fiber reinforced silicon carbide or silicon nitride sintered body according to claim 2, wherein the whiskers have a length of about 40 to 50 μm.
References Cited (Backward Citations)
US4097293A
Cited
JPS56100168A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1991-06-28 | 1991-12-28 | 1992-06-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1995-06-28 | 1995-12-28 | 1996-06-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1999-06-28 | 1999-12-28 | 2000-06-28 | $7700.00 | Window Closed / Lapsed |