Method for manufacturing heat-resistant reinforced composite materials
Assignee: Toshiba Corp
•
Filing: 1976-07-26
•
Granted: 1978-06-27
•
Expires: 1996-07-26
Abstract
Abstract A method for manufacturing heat-resistant reinforced composite materials having a fibrous structure which comprises mixing 99.8 to 90 percent by weight of a first component selected from the group consisting of the nitrides or carbides of aluminum, silicon and boron and mixtures thereof and 0.2 to 10 percent by weight of a second component selected from the group consisting of the rare earth oxides and mixtures thereof, molding the mixture into a desired shape, and sintering the molded mass to create a fibrous structure therein, said first component being 0.2 to 3.0 microns in average particle size, and said second component being 0.1 to 2.0 microns in average particle size.
Inventors
- 👤 Katsutoshi Komeya
- 👤 Hiroshi Inoue
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 01:23
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/583; C04B35/56; C04B35/563; C04B35/565; C04B35/581; C04B35/584
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
203 words
A method for manufacturing heat-resistant reinforced composite materials having a fibrous structure which comprises: A. providing a mixture of: (a) 99.8 to 90 percent by weight of a first component selected from the group consisting of nitrides and carbides of aluminum, silicon and boron and mixtures thereof, said first component being 0.2 to 3.0 microns in average particle size, and (b) 0.2 to 10 percent by weight of a second component selected from the group consisting of oxides of scandium, yttrium and elements of the lanthanum series and mixtures thereof, said second component being 0.1 to 2.0 microns in average particle size, B. molding said mixture by pressure into a desired form, and C. sintering the molded mass without application of pressure thereon in at least one gas selected from the group consisting of nitrogen, ammonia and inert gas at a temperature as specified below with respect to the first component contained in said mixture: aluminum nitride -- 1600° to -- 2200° C silicon nitride -- 1500° to -- 1900° C boron nitride -- 1700° to -- 2200° C aluminum carbide -- 1700° to -- 2300° C silicon carbide -- 1600° to -- 2200° C boron carbide -- 1800° to -- 2200° C
Claim 2
Independent Claim
203 words
A method for manufacturing heat-resistant reinforced composite materials having a fibrous structure which comprises: A. providing a mixture of: (a) 99.8 to 90 percent by weight of a first component selected from the group consisting of nitrides and carbides of aluminum, silicon and boron and mixtures thereof, said first component being 0.2 to 3.0 microns in average particle size, and (b) 0.2 to 10 percent by weight of a second component selected from the group consisting of oxides of scandium, yttrium and elements of the lanthanum series and mixtures thereof, said second component being 0.1 to 2.0 microns in average particle size, B. molding said mixture by pressure into a desired form, and C. sintering the molded mass without application of pressure thereon in at least one gas selected from the group consisting of nitrogen, ammonia and inert gas at a temperature as specified below with respect to the first component contained in said mixture: aluminum nitride -- 1600° to -- 2200° C silicon nitride -- 1500° to -- 1900° C boron nitride -- 1700° to -- 2200° C aluminum carbide -- 1700° to -- 2300° C silicon carbide -- 1600° to -- 2200° C boron carbide -- 1800° to -- 2200° C
Claim 3
Dependent Claim
13 words
The method according to claim 1 wherein the first component is aluminum nitride.
Claim 4
Dependent Claim
13 words
The method according to claim 1 wherein the second component is yttrium oxide.
Claim 5
Dependent Claim
13 words
The method according to claim 1 wherein the first component is silicon nitride.
Claim 6
Independent Claim
159 words
A method for manufacturing heat-resistant reinforced composite materials having a fibrous structure which comprises: A. providing a mixture of: (a) 99.3 to 80 percent by weight of a first component having 0.2 to 3.0 microns in average particle size, said first component being aluminum nitride, (b) 0.2 to 10 percent by weight of a second component selected from the group consisting of oxides of scandium, yttrium, and elements of the lanthanum series and mixtures thereof, said second component being 0.1 to 2.0 microns in average particle size, and (c) 0.5 to 10 percent by weight of a third component having 0.1 to 2.5 microns in average particle size, said third component being silicates, B. molding said mixture by pressure into a desired form, and C. sintering the molded mass without application of pressure thereon in at least one gas selected from the group consisting of nitrogen, ammonia and inert gas at a temperature of from 1600° to 2200° C.
Claim 7
Independent Claim
159 words
A method for manufacturing heat-resistant reinforced composite materials having a fibrous structure which comprises: A. providing a mixture of: (a) 99.3 to 80 percent by weight of a first component having 0.2 to 3.0 microns in average particle size, said first component being aluminum nitride, (b) 0.2 to 10 percent by weight of a second component selected from the group consisting of oxides of scandium, yttrium, and elements of the lanthanum series and mixtures thereof, said second component being 0.1 to 2.0 microns in average particle size, and (c) 0.5 to 10 percent by weight of a third component having 0.1 to 2.5 microns in average particle size, said third component being silicates, B. molding said mixture by pressure into a desired form, and C. sintering the molded mass without application of pressure thereon in at least one gas selected from the group consisting of nitrogen, ammonia and inert gas at a temperature of from 1600° to 2200° C.
Claim 8
Dependent Claim
28 words
The method of claim 5 wherein said silicate is selected from the group consisting of aluminum silicate, magnesium silicate, calcium silicate, silicon dioxide, feldspar, pyroxene, olivine and mica.
Claim 9
Dependent Claim
42 words
A heat resistive, reinforced article formed of composite material which consists essentially of fibrous crystals of a first component as defined in claim 1 and an amorphous matrix of garnet containing said second component element formed by the method of claim 1.
Claim 10
Dependent Claim
38 words
A heat resistive, reinforced article formed of composite material which consists essentially of fibrous crystals of aluminum nitride and an amorphous matrix of garnet containing Sc, Y, or La series elements formed by the method of claim 5.
References Cited (Backward Citations)
US3108887A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |