Fabrication of semiconductor devices using phosphosilicate glasses
Assignee: Nokia Bell Labs
•
Filing: 1989-05-01
•
Granted: 1991-09-10
•
Expires: 2009-05-01
Abstract
Abstract This invention is directed to a process of producing semiconductor devices which involves deposition of protective glass layers by a particle beam technique from targets of phosphosilicate glass, as well as a process for production of such targets. The phosphosilicate glass containing 1-15 mole percent P 2 O 5 is produced by a sol/gel technique which involves mixing of a fumed silica, with a surface area of 50-400 m 2 /g, preferably about 200 m 2 /g, with phosphoric acid and water to form a sol with 20-55 wt. % silica, allowing it to gel, drying at ambient conditions, dehydrating at about 650° C. in an atmosphere of an inert gas and chlorine and fluorine containing gases, heating up at a certain rate of from 100° to 180° C. per hour to a peak sintering temperature below 1200° C. and cooling so as to produce amorphous and transparent glass suitable for use as a target. The glass layers are highly advantageous as encapsulating layers, diffusion barrier layers, etc., especially for optical type and semiconductor devices. Production of the phosphosilicate glass by the sol/gel technique is highly advantageous over the conventional melting technique, being faster and much less expensive than the latter.
Inventors
- 👤 Debra A. Fleming
- 👤 David W. Johnson, Jr.
- 👤 Shobha Singh
- 👤 LeGrand G. VanUitert
- 👤 George J. Zydzik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:01
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6329; H10P14/6342; H10P14/65; H10P14/6516; H10P14/6529; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6923; Y; Y10; Y10S; Y10S148/00; Y10S148/133; Y10S438/00; Y10S438/902
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
264 words
A process for fabricating a semiconductor device, which comprises depositing by a particle beam deposition a phosphosilicate glass target material on at least a portion of a semiconductor surface so that said at least a portion of said surface is covered with a contacting phosphosilicate glass region comprising from 1 to 15 mole percent P 2 O 5 , wherein said glass material is prepared by a procedure comprising the steps of a) forming a gel by mixing together fumed silica, aqueous solution of reagent grade phosphoric acid and water, and permitting said sol to gel, said silica having surface area within a range of from 50 to 400 m 2 /g and is added in an amount sufficient to form a sol containing from 20 to 55 weight percent silica, b) drying said gel at ambient atmosphere and temperature conditions for a period of up to 14 days, c) dehydrating the dried gel by heating at a rate of from 250 to 350 degrees per hour to a temperature within a range of from 500 to 700 degrees C., and maintaining at said temperature for a period of from 10 minutes to three hours, d) sintering the dehydrated gel into glass by heating the gel at a rate of from 100 to 180 degrees C. per hour from said dehydrating temperature to a desired peak temperature within a range of from 600 to 1200 degrees C., and e) cooling the sintered glass, preferably upon reaching said peak temperature, said dehydrating and sintering stages being conducted in a flowing atmosphere comprising an inert gas.
Claim 2
Dependent Claim
264 words
A process for fabricating a semiconductor device, which comprises depositing by a particle beam deposition a phosphosilicate glass target material on at least a portion of a semiconductor surface so that said at least a portion of said surface is covered with a contacting phosphosilicate glass region comprising from 1 to 15 mole percent P 2 O 5 , wherein said glass material is prepared by a procedure comprising the steps of a) forming a gel by mixing together fumed silica, aqueous solution of reagent grade phosphoric acid and water, and permitting said sol to gel, said silica having surface area within a range of from 50 to 400 m 2 /g and is added in an amount sufficient to form a sol containing from 20 to 55 weight percent silica, b) drying said gel at ambient atmosphere and temperature conditions for a period of up to 14 days, c) dehydrating the dried gel by heating at a rate of from 250 to 350 degrees per hour to a temperature within a range of from 500 to 700 degrees C., and maintaining at said temperature for a period of from 10 minutes to three hours, d) sintering the dehydrated gel into glass by heating the gel at a rate of from 100 to 180 degrees C. per hour from said dehydrating temperature to a desired peak temperature within a range of from 600 to 1200 degrees C., and e) cooling the sintered glass, preferably upon reaching said peak temperature, said dehydrating and sintering stages being conducted in a flowing atmosphere comprising an inert gas.
Claim 3
Dependent Claim
20 words
The process of claim 1 in which the glass material region comprises 1-12 mole percent P 2 O 5 .
Claim 4
Dependent Claim
26 words
The process of claim 1 in which the glass material region consists essentially of 2-10 mole percent P 2 O 5 , remainder SiO 2 .
Claim 5
Dependent Claim
23 words
The process of claim 1 in which said silica comprises surface area within a range of from 150 to 250 m 2 /g.
Claim 6
Dependent Claim
18 words
The process of claim 1 in which said silica comprises surface area of approximately 200 m 2 /g.
Claim 7
Dependent Claim
25 words
The process of claim 1 in which said silica is added so as to form a sol containing from 30 to 50 weight percent silica.
Claim 8
Dependent Claim
22 words
The process of claim 1 in which said drying of the gel is conducted for a period of up to three days.
Claim 9
Dependent Claim
23 words
The process of claim 1 in which said dried gel is heated at a rate of about 300° C./hr to said dehydrating temperature.
Claim 10
Dependent Claim
29 words
The process of claim 1 in which said dehydration is accomplished by heating the dried gel at a temperature of about 650° C. for a period of two hours.
Claim 11
Dependent Claim
30 words
The process of claim 1 in which said heating from the dehydrating to the peak sintering temperature is conducted at a rate of from 140° to 150° C. per hour.
Claim 12
Dependent Claim
16 words
The process of claim 10 in which said heating rate is about 145° C. per hour.
Claim 13
Dependent Claim
21 words
The process of claim 1 in which said peak sintering temperature is within a range of from 1000° to 1200° C.
Claim 14
Dependent Claim
15 words
The process of claim 12 in which said peak sintering temperature is about 1125° C.
Claim 15
Dependent Claim
12 words
The process of claim 1 in which said inert gas comprises helium.
Claim 16
Dependent Claim
37 words
The process of claim 1 in which said dehydration is conducted in an atmosphere comprising in addition to the inert gas at least one of Cl 2 , SiF 4 , fluorocarbons, chlorofluorocarbons and CCl 4 .
Claim 17
Dependent Claim
28 words
The process of claim 1 in which said dehydration is conducted in an atmosphere comprising about 8.5% Cl 2 , 2.5% SiF 4 and 89% He, by volume.
Claim 18
Dependent Claim
15 words
The process of claim 1 in which the particle beam procedure is an e-beam deposition.
Claim 19
Dependent Claim
13 words
The process of claim 1 in which the semiconductor comprises III-V semiconductor compound.
Claim 20
Dependent Claim
29 words
The process of claim 18 in which the III-V semiconductor compound is selected from the group consisting of InP and GaAs and compounds lattice matched to InP and GaAs.
Claim 21
Dependent Claim
16 words
The process of claim 1 in which the phosphosilicate glass region contacts an ion implanted surface.
Claim 22
Dependent Claim
65 words
The process of claim 20 in which the ion implanted surface with contacting glass material is annealed to activate the ion implant, the semiconductor material is GaAs and the anneal is a Rapid Thermal Anneal conducted at a temperature within a range of from 750° to 1000° C. for a period of from 10 seconds to 10 minutes, the lower temperatures corresponding to longer times.
Claim 23
Dependent Claim
48 words
The process of claim 21 in which the Rapid Thermal Anneal carried out at a temperature within a range of from 800 to 1000 degrees C., for about 10 seconds, and at a temperature within a range of from 750 to 850 degrees C., for about 10 minutes.
Claim 24
Dependent Claim
158 words
The process of claim 1 in which said phosphosilicate glass contains from 1 to 12 mole percent P 2 O 5 remainder SiO 2 , said silica has surface area of about 200 m 2 /g, and is combined with water and phosphoric acid to form a sol containing from 30 to 50 weight percent silica, the phosphoric acid is added in an amount to obtain a desired content of P 2 O 5 in the glass, said gel is dried for a period of up to three days, the dried gel is dehydrated by heating at a rate of about 650° C. which then is maintained for two hours, said dehydration being carried out in a flowing atmosphere including helium, Cl 2 and SiF 4 , the dehydrated gel is heated at a rate of from 140° to 150° C. per hour to a peak temperature of from 1000° to 1175° C. and then is furnace cooled.
Claim 25
Dependent Claim
28 words
The process of claim 1 wherein said semiconductor surface is a surface of a compound semiconductor selected from InP and GaAs, and said device is an avalanche photodetector.
Claim 26
Dependent Claim
224 words
A process of producing phosphosilicate glass target material comprising from 1 to 15 mole percent P 2 O 5 , suitable for particle beam deposition, comprising the steps of a) forming a gel by mixing together fumed silica, aqueous solution of reaction grade phosphoric acid and water and permitting the sol to gel, said silica having surface area within a range of from 50 to 400 m 2 /g and is added in an amount sufficient to form a sol containing from 20 to 55 weight percent silica, b) drying said gel at ambient atmosphere and temperature conditions for a period of up to 14 days, c) dehydrating the dried gel by heating the gel at a rate of from 250 to 350 degrees per hour to a temperature within a range of from 500 to 700 degrees C., and maintaining at said temperature for a period of from 10 minutes to three hours, d) sintering the dehydrated gel into glass by heating the gel at a rate of from 100 to 180 degrees C. per hour from said dehydrating temperature to a desired peak temperature within a range of from 600 to 1200 degrees C., and e) cooling the sintered glass, preferably upon reaching said desired peak temperature, said dehydrating and sintering stages being conducted in a flowing atmosphere comprising an inert gas.
Claim 27
Dependent Claim
224 words
A process of producing phosphosilicate glass target material comprising from 1 to 15 mole percent P 2 O 5 , suitable for particle beam deposition, comprising the steps of a) forming a gel by mixing together fumed silica, aqueous solution of reaction grade phosphoric acid and water and permitting the sol to gel, said silica having surface area within a range of from 50 to 400 m 2 /g and is added in an amount sufficient to form a sol containing from 20 to 55 weight percent silica, b) drying said gel at ambient atmosphere and temperature conditions for a period of up to 14 days, c) dehydrating the dried gel by heating the gel at a rate of from 250 to 350 degrees per hour to a temperature within a range of from 500 to 700 degrees C., and maintaining at said temperature for a period of from 10 minutes to three hours, d) sintering the dehydrated gel into glass by heating the gel at a rate of from 100 to 180 degrees C. per hour from said dehydrating temperature to a desired peak temperature within a range of from 600 to 1200 degrees C., and e) cooling the sintered glass, preferably upon reaching said desired peak temperature, said dehydrating and sintering stages being conducted in a flowing atmosphere comprising an inert gas.
Claim 28
Dependent Claim
20 words
The process of claim 25 in which the glass material region comprises 1-12 mole percent P 2 O 5 .
Claim 29
Dependent Claim
26 words
The process of claim 25 in which the glass material region consists essentially of 2-10 mole percent P 2 O 5 , remainder SiO 2 .
Claim 30
Dependent Claim
23 words
The process of claim 25 in which said silica comprises surface area within a range of from 150 to 250 m 2 /g.
Claim 31
Dependent Claim
18 words
The process of claim 25 in which said silica comprises surface area of about 200 m 2 /g.
Claim 32
Dependent Claim
25 words
The process of claim 24 in which said silica is added so as to form a sol containing from 30 to 50 weight percent silica.
Claim 33
Dependent Claim
22 words
The process of claim 25 in which said drying of the gel is conducted for a period of up to three days.
Claim 34
Dependent Claim
23 words
The process of claim 25 in which said dried gel is heated at a rate of about 300° C./hr. to said dehydrating temperature.
Claim 35
Dependent Claim
29 words
The process of claim 25 in which said dehydration is accomplished by heating the dried gel at a temperature of about 650° C. for a period of two hours.
Claim 36
Dependent Claim
30 words
The process of claim 25 in which said heating from the dehydrating to the peak sintering temperature is conducted at a rate of from 140° to 150° C. per hour.
Claim 37
Dependent Claim
16 words
The process of claim 34 in which said heating rate is about 145° C. per hour.
Claim 38
Dependent Claim
21 words
The process of claim 25 in which said peak sintering temperature is within a range of from 1000° to 1200° C.
Claim 39
Dependent Claim
15 words
The process of claim 36 in which said peak sintering temperature is about 1125° C.
Claim 40
Dependent Claim
12 words
The process of claim 25 in which said inert gas comprises helium.
Claim 41
Dependent Claim
37 words
The process of claim 25 in which said dehydration is conducted in an atmosphere comprising in addition to the inert gas, at least one of Cl 2 , SiF 4 , fluorocarbons, chlorofluorocarbons and CCl 4 .
Claim 42
Dependent Claim
27 words
The process of claim 25 in which said dehydration is conducted in an atmosphere comprising about 8.5% Cl 2 2.5% SiF 4 and 89% He, by volume.
Claim 43
Dependent Claim
158 words
The process of claim 25 in which said phosphosilicate glass contains from 1 to 12 mole percent P 2 O 5 remainder SiO 2 , said silica has surface area of about 200 m 2 /g, and is combined with water and phosphoric acid to form a sol containing from 30 to 50 weight percent silica, the phosphoric acid is added in an amount to obtain a desired content of P 2 O 5 in the glass, said gel is dried for a period of up to three days, the dried gel is dehydrated by heating at a rate of about 650° C. which then is maintained for two hours, said dehydration being carried out in a flowing atmosphere including helium, Cl 2 and SiF 4 , the dehydrated gel is heated at a rate of from 140° to 150° C. per hour to a peak temperature of from 1000° to 1175° C. and then is furnace cooled.
References Cited (Backward Citations)
US3616403A
Cited
US3767434A
Cited
US3767432A
Cited
US3743587A
Cited
US4374391A
Cited
US4407061A
Cited
US4419115A
Cited
US4474831A
Cited
US4731293A
Cited
US4732658A
Cited
US4819039A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1994-09-09 | 1995-03-11 | 1995-09-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1998-09-09 | 1999-03-11 | 1999-09-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2002-09-09 | 2003-03-11 | 2003-09-10 | $7700.00 | Window Closed / Lapsed |