Fabrication of sintered high-silica glasses
Assignee: AT&T Inc
•
Filing: 1981-07-31
•
Granted: 1983-12-06
•
Expires: 2001-07-31
Abstract
Abstract High-silica glasses are formed by sintering a dried gel at temperatures below the liquidus. The gel may be formed by mixing colloidal silica particles or silica-containing liquids with appropriate liquids. Fragmentation of the gel during drying is advantageously avoided by redispersing the dried gel or sol in a liquid to yield a colloidal suspension which is then gelled, dried, and finally sintered below the liquidus.
Inventors
- 👤 David W. Johnson, Jr.
- 👤 John B. MacChesney
- 👤 Eliezer M. Rabinovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 12:41
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/06; C03B; C03B19/00; C03B19/12; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/016; C03C1/00; C03C1/006; C03C2201/00; C03C2201/02; C03C2201/06; C03C2201/08; C03C2201/10; C03C2201/20; C03C2201/28; C03C2201/30; C03C2201/31; C03C2203/00; C03C2203/20; C03C2203/22; Y; Y10; Y10S; Y10S65/00; Y10S65/901
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
116 words
A method of fabricating a high-silica glass comprising; (a) forming a substantially alkali-free first sol of particles in a liquid, the particles comprising silica; (b) gelling the first sol to form a first gel; (c) drying substantially the first gel, to form a dried first gel; (d) forming particles from the dried first gel; (e) forming a substantially alkali-free second sol of particles in a liquid, by dispersing the previously prepared, substantially alkali-free particles provided in step (d) in a liquid; (f) gelling the second sol to form a second gel; (g) drying substantially the second gel; and (h) sintering the dried second gel to a glass at a temperature below the liquidus for the glass.
Claim 2
Independent Claim
116 words
A method of fabricating a high-silica glass comprising; (a) forming a substantially alkali-free first sol of particles in a liquid, the particles comprising silica; (b) gelling the first sol to form a first gel; (c) drying substantially the first gel, to form a dried first gel; (d) forming particles from the dried first gel; (e) forming a substantially alkali-free second sol of particles in a liquid, by dispersing the previously prepared, substantially alkali-free particles provided in step (d) in a liquid; (f) gelling the second sol to form a second gel; (g) drying substantially the second gel; and (h) sintering the dried second gel to a glass at a temperature below the liquidus for the glass.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the first gel is heated to a temperature less than 1150 degrees Celsius prior to particle formation.
Claim 4
Dependent Claim
22 words
The method of claim 3 wherein the first or second gel is heated to between 750 degrees Celsius and 800 degrees Celsius.
Claim 5
Independent Claim
21 words
The method of claims 1, 2 or 3 wherein the first sol is formed by mixing fumed silica with the liquid.
Claim 6
Dependent Claim
25 words
The method of claim 5 wherein a boron doped glass is obtained by adding boron to the liquid in the form of a boron-containing solution.
Claim 7
Dependent Claim
22 words
The method of claim 5 wherein a boric acid solution is added during formation of the first or second sol or gel.
Claim 8
Dependent Claim
22 words
The method of claim 5 wherein a boric acid solution is added by dipping the second gel in a boric acid solution.
Claim 9
Independent Claim
24 words
The method of claims 1 or 2 wherein the first or second sol is exposed to a pressure less than atmospheric pressure during formation.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein the second sol is gelled in a mold to yield ultimately a shaped glass.
Claim 11
Dependent Claim
19 words
The method of claim 5 wherein the boron-containing solution is an aqueous, glycerine, or water-glycerine solution of boric acid.
Claim 12
Dependent Claim
27 words
The method of claim 1 wherein a dopant is added during formation of the first or second sol or by impregnation of the first or second gel.
Claim 13
Dependent Claim
26 words
The method of claim 11 wherein the dopant is phosphorus oxide or germanium oxide, added as their liquid compouds or as solutions or their soluble compounds.
Claim 14
Dependent Claim
23 words
The method of claim 12 wherein the dopant is added by mixing germanium tetrachloride or phosphoric acid with the first or second sol.
Claim 15
Dependent Claim
17 words
The method of claim 1 wherein the first sol is formed by mixing silicon tetrachloride with water.
Claim 16
Dependent Claim
19 words
The method of claim 1 wherein the first sol is formed by mixing silicon tetrachloride, germanium tetrachloride and water.
Claim 17
Independent Claim
20 words
The method of claims 14 or 15 wherein additional dopants containing materials are added to the first or second sol.
Claim 18
Independent Claim
26 words
The method of claims 1 wherein the first or second gel is sintered at a temperature below 1300 degrees Celsius to obtain a nontransparent high-silica glass.
Claim 19
Dependent Claim
23 words
The method of claim 1 wherein a monolithic body is obtained by drying the first or second gel in a controlled humidity environment.
Claim 20
Dependent Claim
17 words
The method of claim 1 wherein an optical fiber is formed from the glass of step (b).
Claim 21
Dependent Claim
17 words
The method of claim 19 wherein the fiber is a step index or a graded index fiber.
Claim 22
Dependent Claim
30 words
The method of claim 20 wherein the second gel is formed into a layer and at least one such gelled layer is formed on the interior of a tubular structure.
References Cited (Backward Citations)
US2215039A
Cited
US2106744A
Cited
US2221709A
Cited
US2286275A
Cited
US3597252A
Cited
US3640093A
Cited
US3759683A
Cited
USRE28028E
Cited
US4217027B1
Cited
US4217027A
Cited
US4059658A
Cited
US4042361A
Cited
US4323381A
Cited
US4324576A
Cited
US4317668A
Cited
US4278632A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |