Assignee: Kopin Corp
•
Filing: 1989-03-30
•
Granted: 1990-07-31
•
Expires: 2009-03-30
Abstract
Abstract An improved method of forming seed openings for zone-melting and recrystallization of polysilicon film on an insulator over silicon (SOI) is described. This method comprises forming a narrow discontinuous pattern of seed openings formed by an overlapping sub-pattern of discontinuous shaped openings. Alternatively, in an edge bead seed embodiment, a resist is removed from an SOI precursor structure, comprising an insulator on an Si wafer, thus exposing the peripheral edge of the insulator. The exposed insulator is then also removed to provide a peripheral edge seed opening to the underlying Si wafer.
Inventors
- 👤 Lisa P. Allen
- 👤 Duy-Phach Vu
- 👤 Michael W. Batty
- 👤 Richard H. Morrision, Jr.
- 👤 Paul M. Zavracky
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:24
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/02; C30B29/06; C30B13/00; C30B13/16; Y; Y10; Y10S; Y10S117/00; Y10S117/901; Y10S117/902; Y10S117/913
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
90 words
In a zone melting and recrystallization process in which a polysilicon film formed over an insulator film over a silicon wafer is melted, by translating a heater past the wafer, and allowed to recrystallize to form a substantially single crystal silicon film seeded by said silicon wafer through seed openings formed through the insulator to the silicon wafer, the improvement comprising forming said seed openings in a discontinuous pattern formed of discontinuous sub-patterns of shaped seed openings, said pattern extending in a semicircle closely adjacent the periphery of the wafer.
Claim 2
Dependent Claim
90 words
In a zone melting and recrystallization process in which a polysilicon film formed over an insulator film over a silicon wafer is melted, by translating a heater past the wafer, and allowed to recrystallize to form a substantially single crystal silicon film seeded by said silicon wafer through seed openings formed through the insulator to the silicon wafer, the improvement comprising forming said seed openings in a discontinuous pattern formed of discontinuous sub-patterns of shaped seed openings, said pattern extending in a semicircle closely adjacent the periphery of the wafer.
Claim 3
Dependent Claim
31 words
The process of claim 1 wherein the wafer has a [110] direction flat and the seed openings are oriented at a 45° angle to that direction on a [100] silicon wafer.
Claim 4
Dependent Claim
21 words
The process of claim 1 wherein the seed openings extend at an obtuse angle to the plane of the silicon wafer.
Claim 5
Dependent Claim
16 words
The process of claim 1 wherein the seed openings have a length-to-width ratio greater than unity.
Claim 6
Dependent Claim
21 words
The process of claim 1 wherein the width of the seed openings is less than or equal to about 5 microns.
Claim 7
Dependent Claim
11 words
The process of claim 1 wherein the sub-patterns overlap each other.
Claim 8
Dependent Claim
117 words
In a zone melting and recrystallization process in which a polysilicon film formed over an insulator film over a silicon wafer is melted and allowed to recrystallize to form a substantially single crystal silicon film seeded by said silicon wafer through seed openings formed through the insulator to the silicon wafer, the improvement comprising forming said seed openings in a discontinuous main pattern formed of a discontinuous sub-pattern extending in a semi-circle about the periphery of said wafer with openings less than about 5 microns and melting the polysilicon film by passing a heater by said wafer in a direction commencing with the center of said semicircle and proceeding across said wafer to the other side thereof.
Claim 9
Dependent Claim
117 words
In a zone melting and recrystallization process in which a polysilicon film formed over an insulator film over a silicon wafer is melted and allowed to recrystallize to form a substantially single crystal silicon film seeded by said silicon wafer through seed openings formed through the insulator to the silicon wafer, the improvement comprising forming said seed openings in a discontinuous main pattern formed of a discontinuous sub-pattern extending in a semi-circle about the periphery of said wafer with openings less than about 5 microns and melting the polysilicon film by passing a heater by said wafer in a direction commencing with the center of said semicircle and proceeding across said wafer to the other side thereof.
Claim 10
Dependent Claim
26 words
The process of claim 7 wherein the wafer has a [100] direction flat and the seed openings are oriented at a 45° angle to that direction.
Claim 11
Dependent Claim
21 words
The process of claim 7 wherein the seed openings extend at an obtuse angle to the plane of the silicon wafer.
Claim 12
Dependent Claim
11 words
The process of claim 7 wherein the seed openings are rectangular.
Claim 13
Dependent Claim
106 words
In a zone melting and recrystallization process in which a polysilicon film is formed over an insulator film over a silicon wafer and is melted and allowed to recrystallize to form a substantially single crystal silicon film seeded by said silicon wafer through seeded openings formed through the insulator to the silicon wafer, the improvement comprising forming said seed openings by removing the outer peripheral edge of the insulator film before the polysilicon film is formed, so that when the polysilicon film is formed over the insulator film, the peripheral edge of the polysilicon film is in contact with the peripheral edge of the silicon wafer.
Claim 14
Dependent Claim
106 words
In a zone melting and recrystallization process in which a polysilicon film is formed over an insulator film over a silicon wafer and is melted and allowed to recrystallize to form a substantially single crystal silicon film seeded by said silicon wafer through seeded openings formed through the insulator to the silicon wafer, the improvement comprising forming said seed openings by removing the outer peripheral edge of the insulator film before the polysilicon film is formed, so that when the polysilicon film is formed over the insulator film, the peripheral edge of the polysilicon film is in contact with the peripheral edge of the silicon wafer.
Claim 15
Dependent Claim
118 words
The process of claim 11 wherein the outer peripheral edge of the insulator film is removed by: (a) forming a precursor structure comprising a resist film over the insulator film formed over the silicon wafer; (b) rotating the precursor structure while spraying resist solvent on the peripheral edge of the resist film and dissolving that edge; thus exposing the insulator film around the edge; (c) etching the peripheral edge of the insulator film to expose the peripheral edge of the wafer using the remaining resist film as an etch mask; (d) removing the resist mask; (e) forming the polysilicon film over the insulator film such that polysilicon is in contact with the peripheral edge of the wafer substrate.
Claim 16
Dependent Claim
12 words
The process of claim 12 wherein the insulator is SiO 2 .
References Cited (Backward Citations)
US4727047A
Cited
US4670086A
Cited
US4371421A
Cited
US4670088A
Cited
US4461670A
Cited
US4497683A
Cited
US4496418A
Cited
US4444620A
Cited
US4704186A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1993-07-30 | 1994-01-29 | 1994-07-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1997-07-30 | 1998-01-29 | 1998-07-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2001-07-30 | 2002-01-29 | 2002-07-31 | $7700.00 | Window Closed / Lapsed |