Halogen-free flameproofed thermoplastic molding material
Assignee: BASF SE
•
Filing: 1985-01-18
•
Granted: 1986-12-30
•
Expires: 2005-01-18
Abstract
Abstract A halogen-free flameproofed thermoplastic molding material consists of a halogen-free thermoplastic resin (A) and one or more further halogen-free components. The thermoplastic resin (A) is present in an amount of from 30 to 90% by weight, based on the molding material. The latter contains, as further components, from 1 to 50% by weight of a phenol/aldehyde resin (B), from 1 to 50% by weight of a nitrogen-containing organic compound (C) and from 3 to 50% by weight of a phosphorus-containing organic compound (D), the percentages in each case being based on the molding material. The molding material is used for the production of flameproofed moldings.
Inventors
- 👤 Volker Muench
- 👤 Juergen Hambrecht
- 👤 Adolf Echte
- 👤 Karl H. Illers
- 👤 Johann Swoboda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:03
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/0008; C08K5/0066; C08L; C08L101/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
174 words
A halogen-free flameproofed thermoplastic molding material, comprising one or more halogen-free thermoplastic resins of homopolymers of styrene or copolymers of styrene and acrylonitrile in which some of the styrene component can be replaced by alkylated styrene (A) and one or more further halogen-free components wherein the thermoplastic resin (A) is present in an amount of from 30 to 90% by weight, and the said molding material contains, as further components, (B) from 1 to 50% by weight of one or more phenol/aldehyde resins, (C) from 1 to 50% by weight of one or more nitrogen-containing organic compounds selected from the group consisting of the triazines, triazolidines, ureas, guanidines, guanamines, aminoacids, peptides their derivatives and salts thereof, and (D) from 3 to 50% by weight of one or more phosphorus-containing organic compounds selected from the group consisting of the phosphines, phosphine oxides, phosphinous acids, phosphinic acids, phosphates, hypophosphires, hypodiphosphates and amides of phosphinic acid, of phosphonic acid and of phosphoric acid, the percentages in each case being based on the molding material consisting of A+B+C+D.
Claim 2
Dependent Claim
174 words
A halogen-free flameproofed thermoplastic molding material, comprising one or more halogen-free thermoplastic resins of homopolymers of styrene or copolymers of styrene and acrylonitrile in which some of the styrene component can be replaced by alkylated styrene (A) and one or more further halogen-free components wherein the thermoplastic resin (A) is present in an amount of from 30 to 90% by weight, and the said molding material contains, as further components, (B) from 1 to 50% by weight of one or more phenol/aldehyde resins, (C) from 1 to 50% by weight of one or more nitrogen-containing organic compounds selected from the group consisting of the triazines, triazolidines, ureas, guanidines, guanamines, aminoacids, peptides their derivatives and salts thereof, and (D) from 3 to 50% by weight of one or more phosphorus-containing organic compounds selected from the group consisting of the phosphines, phosphine oxides, phosphinous acids, phosphinic acids, phosphates, hypophosphires, hypodiphosphates and amides of phosphinic acid, of phosphonic acid and of phosphoric acid, the percentages in each case being based on the molding material consisting of A+B+C+D.
Claim 3
Dependent Claim
91 words
A thermoplastic molding material as claimed in claim 1, wherein the thermoplastic resin (A) is present in an amount of from 30 to 90% by weight, and the said molding material contains, as further components, (B) from 5 to 25% by weight of one or more phenol/aldehyde resins, (C) from 5 to 35% by weight of one or more nitrogen-containing organic compounds and (D) from 5 to 35% by weight of one or more phosphorus-containing organic compounds, the percentages in each case being based on the molding material consisting of A+B+C+D.
Claim 4
Dependent Claim
38 words
A thermoplastic molding material as claimed in claim 1, wherein the thermoplastic resin (A) employed is a styrene homopolymer or copolymer which may or may not furthermore contain an elastomer component having a glass transition temperature Tg<0° C.
Claim 5
Dependent Claim
51 words
A molding material as claimed in claim 3, wherein the thermoplastic resin used is a styrene copolymer consisting of from 50 to 99% by weight of styrene, or of styrene which is alkylated in the nucleus, or of a mixture of these, and from 1 to 50% by weight of acrylonitrile.
Claim 6
Dependent Claim
53 words
A thermoplastic molding material as claimed in claim 1, wherein the thermoplastic resin (A) used is a styrene homopolymer or copolymer which contains an elastomer component having a glass transition temperature Tg <0° C, this elastomer component being employed in the form of a graft copolymer of the monomers constituting the component A.
Claim 7
Dependent Claim
92 words
A molding material as claimed in claim 4, wherein the styrene copolymer contains, as copolymerized units, from 50 to 95% by weight of styrene or of a styrene which is alkylated in the nucleus, or of a mixture of these, and from 1 to 50% by weight of acrylonitrile, and furthermore consists of from 5 to 50% by weight, based on the component A, of a graft copolymer consisting of from 10 to 50% by weight of a grafted shell and from 50 to 90 by weight of an elastomeric grafting base.
Claim 8
Dependent Claim
254 words
A thermoplastic molding material as claimed in claim 1, wherein component (B) employed is a phenol/aldehyde resin which consists of (b 1 ) one or more aldehydes of the formula (I) R.sup.1 -CHO (I) where R 1 is H, C 1 -C 10 -alkyl, cycloalkyl, C 6 -C 12 -aryl or -aryl-C 1 -C 3 -alkyl, and (b 2 ) one or more phenols of the formula (II) ##STR3## where R 2 and R 6 are each hydrogen, and R 3 , R 4 and R 5 can each alternatively be hydrogen, C 1 -C 20 -alkyl, cycloalkyl, C 6 -C 10 -aryl, C 1 -C 6 -alkoxy, cycloalkoxy, C 6 -C 10 -phenoxy, hydroxyl, carbonyl, carboxyl, cyano, a C 1 -C 6 -alkyl ester radical, a C 6 -C 10 -aryl ester radical, sulfo, sulfonamido, a sulfonic acid C 1 -C 6 -alkyl ester radical, a sulfonic acid C 6 -C 10 -aryl ester radical, a C 1 -C 6 -alkyl- or C 6 -C 10 -arylphosphonic acid radical or its C 1 -C 6 -alkyl or C 6 -C 10 -aryl ester radical, a phosphonic acid radical or its mono- or di-C 1 -C 6 -alkyl or C 6 -C 10 -aryl ester, an 0-phosphoric acid radical or its mono- or di-C 1 -C 6 -alkyl or C 6 -C 10 -aryl ester, or -aryl-C 1 -C 6 -alkyl, or R 2 and R 4 are each hydrogen, and R 3 , R 5 and R 6 can have the above meanings.
Claim 9
Dependent Claim
52 words
A thermoplastic molding material as claimed in claim 4, wherein the phenol/aldehyde resin (B) used consists of formaldehyde and phenol or a monosubstituted or polysubstituted alkylphenol where alkyl is of 2 to 8 carbon atoms, or a mixture of these, and has a number average molecular weight of from 500 to 2,000.
Claim 10
Dependent Claim
14 words
A molding material as claimed in claim 6, wherein a triazine derivative is employed.
Claim 11
Dependent Claim
26 words
A thermoplastic molding material as claimed in claim 8, wherein a cyclic or dicyclic phosphite, a phosphonate, a phosphate, a hypophosphite or a hypodiphosphate is used.
References Cited (Backward Citations)
US3124551A
Cited
US2473319A
Cited
US2635976A
Cited
US3061900A
Cited
US3098057A
Cited
US3313651A
Cited
US3554934A
Cited
US3816562A
Cited
GB1433781A
Cited
US3931101A
Cited
US3883613A
Cited
US4094834A
Cited
US3930104A
Cited
US4107103A
Cited
US4105825A
Cited
US4332714A
Cited
US4170508A
Cited
US4198492A
Cited
US4385140A
Cited
US4268633A
Cited
US4465807A
Cited
GB2054610A
Cited
US4542186A
Cited
US4338412A
Cited
US4328139A
Cited
US4367295A
Cited
US4380593A
Cited
US4397974A
Cited
US4468495A
Cited
US4504613A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |