US4525224A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the doping of supporting silicon plates for the manufacture of semiconductors
Assignee: BBC Brown Boveri AG Switzerland
•
Filing: 1984-05-22
•
Granted: 1985-06-25
•
Expires: 2004-05-22
Abstract
Abstract A method for the locally selective doping of a planar substrate, essentially made of silicon, for the production of semiconductors using a diffusion process, in which aluminum as the doping additive is applied by vaporizing in a vacuum at temperatures above 500° C. to the substrate surface areas to be doped and permitted to diffuse into the substrate. A part of the substrate surface is masked in order to prevent the doping of the substrate beneath the mask, by forming a SiO 2 layer on the substrate and abutting a masking plate against the SiO 2 layer.
Inventors
- 👤 Thomas Vlasak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 13:31
CPC Classifications
H; H10; H10P; H10P76/00; H10P76/20; H10P32/00; H10P32/10; H10P32/14; H10P32/1408; H10P32/17; H10P32/171; Y; Y10; Y10S; Y10S438/00; Y10S438/914
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
153 words
A method for selectively diffusing aluminum into at least a first silicon substrate having a first surface, comprising the steps of: defining on said first surface a first surface portion to be masked and a first unmasked surface portion; covering at least said first surface portion to be masked with a first layer of silicon dioxide grown onto said first surface portion to be masked; additionally covering only said first portion to be masked with a masking plate abutting against said first silicon dioxide layer, whereby said first surface portion to be masked is masked by said silicon dioxide layer and said masking plate; subjecting said first silicon substrate with said first silicon dioxide layer and said masking plate to a source of aluminum impurities under vacuum conditions and at temperatures between 800° C. and 1300° C.; and diffusing said aluminum impurities into said first silicon substrate at said first unmasked surface portion.
Claim 2
Independent Claim
153 words
A method for selectively diffusing aluminum into at least a first silicon substrate having a first surface, comprising the steps of: defining on said first surface a first surface portion to be masked and a first unmasked surface portion; covering at least said first surface portion to be masked with a first layer of silicon dioxide grown onto said first surface portion to be masked; additionally covering only said first portion to be masked with a masking plate abutting against said first silicon dioxide layer, whereby said first surface portion to be masked is masked by said silicon dioxide layer and said masking plate; subjecting said first silicon substrate with said first silicon dioxide layer and said masking plate to a source of aluminum impurities under vacuum conditions and at temperatures between 800° C. and 1300° C.; and diffusing said aluminum impurities into said first silicon substrate at said first unmasked surface portion.
Claim 3
Dependent Claim
25 words
The method of claim 1, wherein said vacuum conditions are better than 10 -3 Torr and said temperatures lie between 1000° C. and 1250° C.
Claim 4
Dependent Claim
33 words
The method according to claim 2, wherein said covering step comprises covering said first surface portion to be masked with said first layer of silicon dioxide which is 0.2 to 2.0 μm thick.
Claim 5
Dependent Claim
25 words
The method of claim 1, wherein said masking plate is a silicon plate with a thickness identical to the thickness of said first silicon substrate.
Claim 6
Dependent Claim
140 words
The method of claim 4, wherein said silicon plate is a second silicon substrate identical to said first silicon substrate, said second silicon substrate having a second surface corresponding to said first surface of said first silicon substrate, comprising the further steps of: defining on said second surface a second portion to be masked and a second unmasked portion; covering at least said second surface portion to be masked with a second layer of silicon dioxide grown onto said second surface; and putting said first and second silicon substrate together with said first and second masked surface portions abutting against one another, whereby said second silicon substrate acts as a masking plate and masks said first surface portion to be masked and said first silicon substrate acts as a masking plate and masks said second surface portion to be masked.
Claim 7
Dependent Claim
33 words
The method according to claim 5 wherein said covering step comprises covering said first surface porton to be masked with said first layer of silicon dioxide which is 0.2 to 2.0 μm thick.
Claim 8
Dependent Claim
33 words
The method according to claim 4, wherein said covering step comprises covering said first surface portion to be masked with said first layer of silicon dioxide which is 0.2 to 2.0 μm thick.
Claim 9
Dependent Claim
33 words
The method according to claim 1, wherein said covering step comprises covering said first surface portion to be masked with said first layer of silicon dioxide which is 0.2 to 2.0 μm thick.
References Cited (Backward Citations)
US3143444A
Cited
US3314833A
Cited
US3604694A
Cited
US3644154A
Cited
US3972838A
Cited
US3997379A
Cited
US4193826A
Cited
US4235650A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1988-06-24 | 1988-12-24 | 1989-06-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1992-06-24 | 1992-12-24 | 1993-06-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1996-06-24 | 1996-12-24 | 1997-06-25 | $7700.00 | Window Closed / Lapsed |