Vapor phase diffusion of aluminum with or without boron
Assignee: Hitachi Ltd
•
Filing: 1978-08-07
•
Granted: 1980-03-18
•
Expires: 1998-08-07
Abstract
Abstract A method of fabricating a semiconductor device through selective diffusion of aluminum vapor into a silicon substrate by heating a sealed tube in which the silicon substrate and an aluminum source are disposed. The diffusion is effected with a low concentration of aluminum smaller than about 1017 atoms/cm3, thereby making it possible to use a silicon oxide film as a diffusion mask for the selective diffusion of aluminum at predetermined region of the silicon substrate.
Inventors
- 👤 Yasuhiro Mochizuki
- 👤 Hiroaki Hachino
- 👤 Yasumichi Yasuda
- 👤 Yutaka Misawa
- 👤 Takuzo Ogawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:39
CPC Classifications
H; H10; H10P; H10P32/00; H10P32/10; H10P32/12; H10P32/17; H10P32/171
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
100 words
A method of fabricating a semiconductor device through selective diffusion of aluminum in a vapor phase into a silicon substrate by heating a sealed enclosure in which said silicon substrate and an aluminum diffusion source are disposed, wherein said selective diffusion of aluminum is carried out in a predetermined surface region of said silicon substrate with a low aluminum concentration smaller than a predetermined value and using a silicon oxide film as a diffusion mask, said silicon oxide film having apertures at said predetermined surface region of said silicon substrate, through which aluminum is selectively diffused into the silicon substrate.
Claim 2
Independent Claim
100 words
A method of fabricating a semiconductor device through selective diffusion of aluminum in a vapor phase into a silicon substrate by heating a sealed enclosure in which said silicon substrate and an aluminum diffusion source are disposed, wherein said selective diffusion of aluminum is carried out in a predetermined surface region of said silicon substrate with a low aluminum concentration smaller than a predetermined value and using a silicon oxide film as a diffusion mask, said silicon oxide film having apertures at said predetermined surface region of said silicon substrate, through which aluminum is selectively diffused into the silicon substrate.
Claim 3
Dependent Claim
32 words
A method of fabricating a semiconductor device as set forth in claim 1, wherein said predetermined value of the concentration of aluminum is in the order of 10 17 atoms/cm 3 .
Claim 4
Dependent Claim
45 words
A method of fabricating a semiconductor device as set forth in claim 2, wherein said sealed enclosure is filled with an inert gas so as to have substantially an atmospheric pressure when heated at a diffusion temperature in the range of 1000° to 1250° C.
Claim 5
Dependent Claim
42 words
A method of fabricating a semiconductor device as set forth in claim 2, wherein said diffusion source of aluminum is contained in a diffusion source container made of either silicon or quartz thereby to adjust the surface concentration of the diffused aluminum.
Claim 6
Dependent Claim
66 words
A method of fabricating a semiconductor device as set forth in claim 1, wherein a diffusion source of boron is additionally contained in the sealed enclosure and selective diffusion of boron is carried out in said predetermined surface region of said semiconductor substrate, whereby the depth of diffusion is controlled by aluminum, while the surface impurity concentration of said silicon substrate is controlled by diffused boron.
Claim 7
Dependent Claim
29 words
A method of fabricating a semiconductor device as set forth in claim 5, wherein said diffusion sources of aluminum and boron are constituted by silicon containing aluminum and boron.
Claim 8
Dependent Claim
52 words
A method of fabricating a semiconductor device as set forth in claim 5, wherein selective diffusion of aluminum and boron into a silicon substrate is carried out by using said silicon oxide film as a diffusion mask and then a drive-in diffusion is carried out after said silicon oxide film is removed.
Claim 9
Dependent Claim
26 words
A method of fabricating a semiconductor device as set forth in claim 5, wherein the aluminum and boron are simultaneously selectively diffused into the silicon substrate.
Claim 10
Dependent Claim
39 words
A method of fabricating a semiconductor device as set forth in claim 1, wherein the sealed enclosure is heated at a temperature and for an amount of time such that the silicon oxide film does not form into α-cristobalite.
Claim 11
Dependent Claim
104 words
A method of fabricating a semiconductor device as set forth in claim 9, wherein, after the sealed enclosure has been heated at a temperature and for a time such that α-cristobalite is not formed, whereby aluminum is selectively diffused into the silicon substrate, a silicon oxide film is again formed on the silicon substrate and formed into a diffusion mask, and then said silicon substrate and an aluminum diffusion source are disposed in a sealed enclosure and heated such that a further selective diffusion of aluminum is carried out, whereby a diffusion layer having a greater depth than after the first diffusion is formed.
Claim 12
Dependent Claim
24 words
A method of fabricating a semiconductor device as set forth in claim 1, wherein an Al-Si alloy is used as the aluminum diffusion source.
Claim 13
Dependent Claim
25 words
A method of fabricating a semiconductor device as set forth in claim 1, wherein said silicon oxide film has a thickness of 0.5 to 3.1μm.
References Cited (Backward Citations)
US3562033A
Cited
US3615936A
Cited
US3577287A
Cited
US3615945A
Cited
US3798084A
Cited
US4029528A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-03-18 | 1983-09-17 | 1984-03-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-03-18 | 1987-09-17 | 1988-03-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-03-18 | 1991-09-17 | 1992-03-18 | $7700.00 | Window Closed / Lapsed |