Process for air firing oxidizable conductors
Assignee: CTS Corp
•
Filing: 1981-11-18
•
Granted: 1983-10-11
•
Expires: 2001-11-18
Abstract
Abstract A thick film is formed initially as a paste and made up of such oxidizable conductor ingredients as copper which is then mixed with glass frit and next printed on a non-conductive inert substrate by silk screening. The silk screen printed thick film with vehicle is then dried, and a coating of boron in suitable paste or paint form having been mixed with a thixotropic organic vehicle is covered over the entirety of the substrate and silk screen printed thick film. The resulting product after a second air drying is then fired to bond the glass frit-copper as a thick film onto the substrate, with the copper particles being sintered throughout into a thick film. Superposed boron, where contiguous with the copper printing, is fused as a protective layer over the copper allowing the sintering of the copper and bonding with the substrate to occur without oxidation of the copper. Oxidized boron that covers portions of the substrate not occupied by the thick film and not superposing the copper layer is then washed away and the boron bonded to the copper remains as a protective coating.
Inventors
- 👤 Charles Y. Kuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:04
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/28; H05K1/00; H05K1/02; H05K1/09; H05K1/092; H05K3/24; H05K3/245; H05K3/247; H05K3/248; H05K1/03; H05K1/0306; H05K2201/00; H05K2201/01; H05K2201/0137; H05K2201/017; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24851; Y10T428/24893; Y10T428/24909; Y10T428/24926; Y10T428/25; Y10T428/252
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
124 words
A method of forming a thick film electrical conductor on a non-conductive substrate wherein the resistance is less than one ohm per square, comprising the steps of intimately mixing a copper powder, glass frit and vehicle to form a printable mixture, printing the mixture on a non-conductive substrate and thereafter drying the mixture, preparing a combination of boron powder and vehicle which are intimately mixed together and applying the boron powder-vehicle mixture over the entire surface of the previously printed and dried mixture, drying the boron powder-vehicle mixture, firing the boron on top of the printed copper powder and glass frit mixture, and finally washing with water to remove the boron and boron oxide from the surface of the substrate and overlying printed surface.
Claim 2
Independent Claim
124 words
A method of forming a thick film electrical conductor on a non-conductive substrate wherein the resistance is less than one ohm per square, comprising the steps of intimately mixing a copper powder, glass frit and vehicle to form a printable mixture, printing the mixture on a non-conductive substrate and thereafter drying the mixture, preparing a combination of boron powder and vehicle which are intimately mixed together and applying the boron powder-vehicle mixture over the entire surface of the previously printed and dried mixture, drying the boron powder-vehicle mixture, firing the boron on top of the printed copper powder and glass frit mixture, and finally washing with water to remove the boron and boron oxide from the surface of the substrate and overlying printed surface.
Claim 3
Dependent Claim
24 words
The process in accordance with claim 1 in which the substrate material is selected from the group consisting of glass, alumina, and enamel materials.
Claim 4
Dependent Claim
25 words
The process in accordance with claim 1 in which the substrate consists of a material which is non-reactive with the printed surface and electrically non-conductive.
Claim 5
Dependent Claim
21 words
The process in accordance with claim 1 including the step of firing at a temperature between 550° C. to 800° C.
Claim 6
Dependent Claim
53 words
The process in accordance with claim 1 including the step of roll milling the copper powder, glass frit, and vehicle together to form a viscous copper paint which is adapted for printing onto the surface of the substrate and applying a pattern of such paint to the substrate by a silk screen procedure.
Claim 7
Dependent Claim
39 words
The process in accordance with claim 1 including the step of roll milling together the boron powder and vehicle, the boron powder consisting of an amorphous boron powder of submicron size and a purity of at least 90-97 percent.
Claim 8
Dependent Claim
25 words
The process in accordance with claim 1 in which said glass frit consists of lead borosilicate frit of a particle size less than 325 mesh.
Claim 9
Dependent Claim
38 words
The process in accordance with claim 1 in which the boron powder is mixed with a thixotropic organic in the form of ethyl cellulose dissolved in a material selected from a group consisting of pine oil and terpineol.
Claim 10
Dependent Claim
35 words
The process in accordance with claim 1 in which the solderability of said materials is modifiable by the inclusion of a metal selected from the group consisting of silver, palladium, platinum, gold, nickel, and lead.
Claim 11
Dependent Claim
58 words
The process in accordance with claim 1 in which the copper powder and glass frit are mixed together in the ranges of 10 to 35 percent by weight frit together with 90-65 percent by weight copper powder and wherein said glass frit forms the bonding between the copper powder particles and the copper powder particles to the substrate.
Claim 12
Dependent Claim
30 words
The process in accordance with claim 1 in which the printable mixture has a ratio of solid to vehicle in the range of 90-60 percent solid to 10-40 percent vehicle.
Claim 13
Dependent Claim
35 words
The process in accordance with claim 1 in which the printable mixture is printed onto the substrate through a screen, said substrate consisting of a material selected from the group consisting of glass and alumina.
Claim 14
Dependent Claim
41 words
The process in accordance with claim 1 in which the drying of the printable mixture on the substrate is at approximately 100° C. for 15 minutes, and the surface of the substrate is then covered with the boron powder vehicle mixture.
Claim 15
Dependent Claim
48 words
The process in accordance with claim 13 in which the boron powder-vehicle mixture covering the printed copper powder-glass frit mixture is dried, and thereafter fired at a range of 550° C. to 800° C. and for a time period ranging from approximately three minutes to approximately 15 minutes.
Claim 16
Dependent Claim
30 words
The process in accordance with claim 1 in which the step of washing is carried out with warm soapy water to dissolve the boron oxide and remove the excess boron.
References Cited (Backward Citations)
US3016037A
Cited
US2993815A
Cited
US3948812A
Cited
US3929674A
Cited
US4067736A
Cited
US3948813A
Cited
US4068022A
Cited
US4122232A
Cited
US4072771A
Cited
US4070517A
Cited
US4172919A
Cited
US4248921A
Cited
US4140817A
Cited
US4169171A
Cited
US4316920A
Cited
US4316942A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-10-10 | 1987-04-11 | 1987-10-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-10-10 | 1991-04-11 | 1991-10-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-10-10 | 1995-04-11 | 1995-10-11 | $7700.00 | Window Closed / Lapsed |