Low fired conductive compositions
Assignee: WALTER E HELLER WESTERN Inc
•
Filing: 1976-07-08
•
Granted: 1978-01-24
•
Expires: 1996-07-08
Abstract
Abstract Disclosed herein are powder compositions useful for making conductors, e.g., microcircuit conductors, end terminations for capacitors, electrodes for gas discharge display devices, etc. The compositions comprise inorganic powders dispersed in an inert vehicle and are printed and fired in the conventional manner on dielectric substrates. The inorganic powders comprise a mixture of nickel and/or aluminum or copper and boron. Glass powder and/or silicon powder may also be present.
Inventors
- 👤 Casimir W. Kazmierowicz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:17
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/04; C03C3/062; C03C3/07; C03C3/072; C03C8/00; C03C8/14; C03C8/18; H; H01; H01B; H01B1/00; H01B1/02; H01B1/14; H01B1/16; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/24942; Y10T428/2495; Y10T428/24967
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
30 words
A composition comprising about 79 weight percent nickel, about 11 weight percent glass, about 4 weight percent lead oxide, about 3 weight percent boron, and about 3 weight percent silicon.
Claim 2
Dependent Claim
30 words
A composition comprising about 79 weight percent nickel, about 11 weight percent glass, about 4 weight percent lead oxide, about 3 weight percent boron, and about 3 weight percent silicon.
Claim 3
Dependent Claim
40 words
A composition comprising from about 0.2 to about 6 weight percent silicon, from about 0.2 to about 2 weight percent boron, from about 75 to about 90 weight percent aluminum, and from about 2 to about 24 weight percent glass.
Claim 4
Dependent Claim
40 words
A composition comprising from about 0.2 to about 6 weight percent silicon, from about 0.2 to about 2 weight percent boron, from about 75 to about 90 weight percent aluminum, and from about 2 to about 24 weight percent glass.
Claim 5
Dependent Claim
27 words
The composition of claim 2 comprising about 0.5 weight percent silicon, about 0.5 weight percent boron, about 80 weight percent aluminum, and about 19 weight percent glass.
Claim 6
Dependent Claim
49 words
A composition comprising from about 5 to about 20 weight percent nickel, from about 0.2 to about 4 weight percent silicon, from about 0.2 to about 4 weight percent boron, from about 50 to about 85 weight percent aluminum, and from about 9 to about 40 weight percent glass.
Claim 7
Dependent Claim
49 words
A composition comprising from about 5 to about 20 weight percent nickel, from about 0.2 to about 4 weight percent silicon, from about 0.2 to about 4 weight percent boron, from about 50 to about 85 weight percent aluminum, and from about 9 to about 40 weight percent glass.
Claim 8
Dependent Claim
31 words
The composition of claim 4 comprising about 10 weight percent nickel, about 1.5 weight percent silicon, about 0.5 weight percent boron, about 63 percent aluminum, and about 25 weight percent glass.
Claim 9
Dependent Claim
62 words
The composition of claim 4 comprising from about 50 to about 85 weight percent aluminum, from about 9 to about 40 weight percent glass, from about 5 to about 20 weight percent nickel, from about 0 to about 2 weight percent lead oxide, from about 0.2 to about 4 weight percent silicon, and from about 0.2 to about 4 weight percent boron.
Claim 10
Dependent Claim
38 words
The composition of claim 6 comprising about 65 weight percent aluminum, about 26 weight percent glass, about 8 weight percent nickel, about 0.4 weight percent lead oxide, about 0.3 weight percent silicon, and about 0.3 weight percent boron.
Claim 11
Dependent Claim
23 words
A composition comprising from about 98 to about 99.5 weight percent nickel oxide and from about 0.5 to about 2 weight percent boron.
Claim 12
Dependent Claim
23 words
A composition comprising from about 98 to about 99.5 weight percent nickel oxide and from about 0.5 to about 2 weight percent boron.
Claim 13
Dependent Claim
70 words
A conductor comprising successively a nonconducting substrate; a thick film pattern comprising from about 0.2 to about 6 weight percent silicon, from about 0.2 to about 2 weight percent boron, from about 75 to about 90 weight percent aluminum, and from about 2 to about 24 weight percent glass; and a layer of nickel over said thick film pattern having a thickness of from about 0.05 to about 0.5 mil.
Claim 14
Dependent Claim
70 words
A conductor comprising successively a nonconducting substrate; a thick film pattern comprising from about 0.2 to about 6 weight percent silicon, from about 0.2 to about 2 weight percent boron, from about 75 to about 90 weight percent aluminum, and from about 2 to about 24 weight percent glass; and a layer of nickel over said thick film pattern having a thickness of from about 0.05 to about 0.5 mil.
Claim 15
Dependent Claim
79 words
A conductor comprising successively a nonconducting substrate; a thick film pattern comprising from about 5 to about 20 weight percent nickel, from about 0.2 to about 4 weight percent silicon, from about 0.2 to about 4 weight percent boron, from about 50 to about 85 weight percent aluminum, and from about 9 to about 40 weight percent glass; and a layer of nickel over said thick film pattern having a thickness of from about 0.05 to about 0.5 mil.
Claim 16
Dependent Claim
79 words
A conductor comprising successively a nonconducting substrate; a thick film pattern comprising from about 5 to about 20 weight percent nickel, from about 0.2 to about 4 weight percent silicon, from about 0.2 to about 4 weight percent boron, from about 50 to about 85 weight percent aluminum, and from about 9 to about 40 weight percent glass; and a layer of nickel over said thick film pattern having a thickness of from about 0.05 to about 0.5 mil.
Claim 17
Dependent Claim
89 words
A conductor comprising successively a nonconducting substrate; a thick film pattern comprising from about 50 to about 85 weight percent aluminum, from about 9 to about 40 weight percent glass, from about 5 to about 20 weight percent nickel, from about 0 to about 2 weight percent lead oxide, from about 0.2 to about 4 weight percent silicon, and from about 0.2 to about 4 weight percent boron; and a layer of nickel over said thick film pattern having a thickness of from about 0.05 to about 0.5 mil.
Claim 18
Dependent Claim
89 words
A conductor comprising successively a nonconducting substrate; a thick film pattern comprising from about 50 to about 85 weight percent aluminum, from about 9 to about 40 weight percent glass, from about 5 to about 20 weight percent nickel, from about 0 to about 2 weight percent lead oxide, from about 0.2 to about 4 weight percent silicon, and from about 0.2 to about 4 weight percent boron; and a layer of nickel over said thick film pattern having a thickness of from about 0.05 to about 0.5 mil.
References Cited (Backward Citations)
US3484284A
Cited
US3948812A
Cited
US3794518A
Cited
US3904461A
Cited
US3854957A
Cited
US3929674A
Cited
US3943168A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-01-23 | 1981-07-25 | 1982-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-01-23 | 1985-07-25 | 1986-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-01-23 | 1989-07-25 | 1990-01-24 | $7700.00 | Window Closed / Lapsed |