Abstract
Abstract Disclosed is a method and resulting product whereby thick film conductors which require a reducing firing atmosphere may be included in circuits with thick film resistors requiring an oxidizing firing atmosphere. In accordance with one embodiment, a fritless paste including copper is deposited onto a substrate in a desired conductor pattern and fired to establish adhesion. The copper oxide in the pattern is then reduced to copper metal at a high temperature. This is followed by oxidation of the copper to produce a copper oxide of lower density than the oxide formed after the initial firing. The resistor material is then deposited and fired in an oxidizing atmosphere. The low density copper oxide may then be reduced at a low temperature so that resistor properties are not adversely affected.
Inventors
- 👤 John F. Brown
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 04:22
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H01; H01C; H01C17/00; H01C17/28; H01C17/281; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49099
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
159 words
A method of fabricating a thick film circuit on a substrate comprising the steps of: depositing a fritless paste comprising a material selected from the group consisting of a metal and a metal oxide onto the substrate in a desired conductor pattern; heating the resulting structure in an oxidizing atmosphere at a temperature sufficient to establish adhesion between the paste and substrate; heating the structure at a high temperature in a reducing atmosphere to convert the resulting metal oxide to the metal; heating the structure in an oxidizing atmosphere to convert the metal to a lower density metal oxide; forming a resistor material on said substrate and portions of said conductor pattern; heating the resulting structure in an oxidizing atmosphere to establish a desired resistivity of the resistor material; and heating the structure at a low temperature in a reducing atmosphere to convert the lower density metal oxide to metal and establish a desired resistivity for the conductor pattern.
Claim 2
Independent Claim
159 words
A method of fabricating a thick film circuit on a substrate comprising the steps of: depositing a fritless paste comprising a material selected from the group consisting of a metal and a metal oxide onto the substrate in a desired conductor pattern; heating the resulting structure in an oxidizing atmosphere at a temperature sufficient to establish adhesion between the paste and substrate; heating the structure at a high temperature in a reducing atmosphere to convert the resulting metal oxide to the metal; heating the structure in an oxidizing atmosphere to convert the metal to a lower density metal oxide; forming a resistor material on said substrate and portions of said conductor pattern; heating the resulting structure in an oxidizing atmosphere to establish a desired resistivity of the resistor material; and heating the structure at a low temperature in a reducing atmosphere to convert the lower density metal oxide to metal and establish a desired resistivity for the conductor pattern.
Claim 3
Dependent Claim
24 words
The method according to claim 1 wherein the metal is selected from the group consisting of copper, nickel, cobalt, titanium, chromium, cadmium and vanadium.
Claim 4
Dependent Claim
11 words
The method according to claim 1 wherein the metal is copper.
Claim 5
Dependent Claim
13 words
The method according to claim 1 wherein the resistor material comprises ruthenium oxide.
Claim 6
Dependent Claim
28 words
The method according to claim 1 wherein the heating at a high temperature in a reducing atmosphere is done at a temperature of at least 700 degrees C.
Claim 7
Dependent Claim
97 words
The method according to claim 1 wherein the structure is heated in air at a temperature of 1100-1220 degrees C. for 10 minutes-1 hour, then heated at a temperature of 700-1100 degrees C. for 10-60 minutes in an atmosphere of at least 2% hydrogen followed by heating in air at a temperature of 250-950 degrees C. for 5 minutes to 1 hour, and subsequent to formation of the resistors, the structure is heated in an atmosphere of at least 2% hydrogen at a temperature in the range of 250-450 degrees C. for 5 minutes to 1 hour.
Claim 8
Dependent Claim
20 words
The method according to claim 1 wherein the desired resistivity of the conductor pattern is no greater than 0.1 ohms/square.
Claim 9
Dependent Claim
11 words
The method according to claim 1 wherein the substrate comprises alumina.
Claim 10
Independent Claim
192 words
A method of fabricating a thick film circuit on an alumina substrate comprising the steps of: screen printing a fritless paste comprising copper and an organic binder onto the substrate in a desired conductor pattern; heating the resulting structure in an oxidizing atmosphere at a temperature sufficient to establish adhesion between the copper and substrate; heating the structure at a temperature of 700 degrees-1100 degrees C. in a reducing atmosphere for 10-60 minutes to convert the resulting copper oxide to copper; heating the structure in an oxidizing atmosphere at a temperature of 250-950 degrees C. for 5 minutes to 1 hour to convert the resulting copper to a lower density copper oxide; forming a ruthenium-based resistor material on said substrate and portions of said conductor pattern; heating the resulting structure in an oxidizing atmosphere for a time and temperature sufficient to establish a desired resistivity of the resistor material, and heating the structure in a reducing atmosphere at a temperature of 250-450 degrees C. for 5 minutes to 1 hour to convert the lower density copper oxide to copper and establish a resistivity of the conductor pattern no greater than 0.1 ohms/square.
Claim 11
Independent Claim
192 words
A method of fabricating a thick film circuit on an alumina substrate comprising the steps of: screen printing a fritless paste comprising copper and an organic binder onto the substrate in a desired conductor pattern; heating the resulting structure in an oxidizing atmosphere at a temperature sufficient to establish adhesion between the copper and substrate; heating the structure at a temperature of 700 degrees-1100 degrees C. in a reducing atmosphere for 10-60 minutes to convert the resulting copper oxide to copper; heating the structure in an oxidizing atmosphere at a temperature of 250-950 degrees C. for 5 minutes to 1 hour to convert the resulting copper to a lower density copper oxide; forming a ruthenium-based resistor material on said substrate and portions of said conductor pattern; heating the resulting structure in an oxidizing atmosphere for a time and temperature sufficient to establish a desired resistivity of the resistor material, and heating the structure in a reducing atmosphere at a temperature of 250-450 degrees C. for 5 minutes to 1 hour to convert the lower density copper oxide to copper and establish a resistivity of the conductor pattern no greater than 0.1 ohms/square.
References Cited (Backward Citations)
US3998980A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-02-19 | 1982-08-21 | 1983-02-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-02-19 | 1986-08-21 | 1987-02-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-02-19 | 1990-08-21 | 1991-02-20 | $7700.00 | Window Closed / Lapsed |