Air firable base metal conductors
Assignee: BASF Catalysts LLC
•
Filing: 1975-04-21
•
Granted: 1978-10-24
•
Expires: 1995-04-21
Abstract
Abstract A paste for forming a thick film conductor of a base metal on a non-conductive substrate comprises a base metal powder (particularly nickel) which ordinarily would oxidize when fired in air, boron powder and a vehicle. In one embodiment, the paste may also contain glass frit. By proper selection of the composition, in particular the amounts of boron and glass frit, a base metal conductor can be formed which strongly adheres to the substrate and has excellent conductive properties. Ranges of compositions are disclosed within which the pastes can be fired in air and produce conductive thick films and outside which conductive properties are inferior and/or the bond strength is unsatisfactory.
Inventors
- 👤 Charles Y. Kuo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 06:50
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/14; H01B1/16; H05; H05K; H05K1/00; H05K1/02; H05K1/09; H05K1/092; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/252; Y10T428/256
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
258 words
A method of forming a base metal thick film electrical conductor having a sheet resistance less than about 1 ohm/square on a non-conductive substrate comprising: (a) mixing a paste comprising (i) a base metal powder which oxidizes upon firing in the presence of air and becomes substantially electrically non-conductive and selected from the group consisting of nickel, copper, cobalt and mixtures thereof, said powder having a particle size less than 325 mesh and a concentration between 50 and 80 percent dry weight of base metal and boron, (ii) boron powder in an amount sufficient to prevent oxidation of said base metal powder during firing of said paste in air, said boron powder having a particle size less than 325 mesh and a concentration between 4 and 50 percent by dry weight of base metal and boron, (iii) sufficient vehicle to produce a paste suitable for application on said substrate, and (iv) up to about 20 percent of glass frit by dry weight relative to the total of base metal, boron, and glass frit, said glass frit having a particle size of less than 325 mesh; (b) applying said paste of (a) onto said non-conductive substrate; (c) air-drying the applied paste of (b) at an elevated temperature to remove volatile materials in said vehicle; (d) firing the air-dried paste of (c) in air to bond said powders to said substrate, said boron preventing oxidation of said base metal powder, thereby forming a base metal thick film electrical conductor having a sheet resistance less than 1 ohm/square on said substrate.
Claim 2
Independent Claim
258 words
A method of forming a base metal thick film electrical conductor having a sheet resistance less than about 1 ohm/square on a non-conductive substrate comprising: (a) mixing a paste comprising (i) a base metal powder which oxidizes upon firing in the presence of air and becomes substantially electrically non-conductive and selected from the group consisting of nickel, copper, cobalt and mixtures thereof, said powder having a particle size less than 325 mesh and a concentration between 50 and 80 percent dry weight of base metal and boron, (ii) boron powder in an amount sufficient to prevent oxidation of said base metal powder during firing of said paste in air, said boron powder having a particle size less than 325 mesh and a concentration between 4 and 50 percent by dry weight of base metal and boron, (iii) sufficient vehicle to produce a paste suitable for application on said substrate, and (iv) up to about 20 percent of glass frit by dry weight relative to the total of base metal, boron, and glass frit, said glass frit having a particle size of less than 325 mesh; (b) applying said paste of (a) onto said non-conductive substrate; (c) air-drying the applied paste of (b) at an elevated temperature to remove volatile materials in said vehicle; (d) firing the air-dried paste of (c) in air to bond said powders to said substrate, said boron preventing oxidation of said base metal powder, thereby forming a base metal thick film electrical conductor having a sheet resistance less than 1 ohm/square on said substrate.
Claim 3
Dependent Claim
13 words
The method of claim 1 wherein said paste of (a) further comprises silver.
Claim 4
Dependent Claim
176 words
A paste for forming a thick film electrical conductor on a non-conductive substrate by firing at elevated temperatures in the presence of air comprising: (a) A base metal powder which oxidizes upon firing in the presence of air and becomes substantially electrically non-conductive, selected from the group consisting of nickel, copper, cobalt and mixtures thereof, said powder having a particle size less than 325 mesh and a concentration between 40 and 80 percent by dry weight of base metal and boron; (b) an operable amount of boron powder whereby oxidation of said base metal powder of (a) is prevented during firing of said paste in air and thereby producing an electrically conductive film, said boron powder having a particle size less than 325 mesh and a concentration between 4 and 50 percent by dry weight of base metal and boron; (c) a vehicle; and (d) up to about 20 percent of glass frit by dry weight relative to the total of base metal, boron and glass frit having a particle size of less than 325 mesh.
Claim 5
Dependent Claim
176 words
A paste for forming a thick film electrical conductor on a non-conductive substrate by firing at elevated temperatures in the presence of air comprising: (a) A base metal powder which oxidizes upon firing in the presence of air and becomes substantially electrically non-conductive, selected from the group consisting of nickel, copper, cobalt and mixtures thereof, said powder having a particle size less than 325 mesh and a concentration between 40 and 80 percent by dry weight of base metal and boron; (b) an operable amount of boron powder whereby oxidation of said base metal powder of (a) is prevented during firing of said paste in air and thereby producing an electrically conductive film, said boron powder having a particle size less than 325 mesh and a concentration between 4 and 50 percent by dry weight of base metal and boron; (c) a vehicle; and (d) up to about 20 percent of glass frit by dry weight relative to the total of base metal, boron and glass frit having a particle size of less than 325 mesh.
Claim 6
Dependent Claim
21 words
The paste of claim 3 wherein the vehicle content is within the range of 10 to 40 percent by dry weight.
Claim 7
Dependent Claim
8 words
The paste of claim 3 further comprising silver.
Claim 8
Dependent Claim
166 words
A base metal thick film conductor on a non-conductive substrate characterized by having a sheet resistance less than about 1 ohm/square and formed from: (a) between 40 and 80 percent by dry weight of a base metal powder relative to the total of base metal and boron which oxidizes upon firing in the presence of air and becomes substantially electrically non-conductive and selected from the group consisting of nickel, copper, cobalt and mixtures thereof; (b) between 4 and 50 percent by dry weight of boron powder relative to the total of base metal and boron; and (c) up to about 20 percent by dry weight of glass frit relative to the total of base metal, boron and glass frit; said conductor formed by firing in the presence of air a paste comprising powders having particles less than 325 mesh of said base metal powder, boron and glass frit mixed with a suitable vehicle to produce a conductor having a sheet resistance less than about 1 ohm/square.
Claim 9
Dependent Claim
166 words
A base metal thick film conductor on a non-conductive substrate characterized by having a sheet resistance less than about 1 ohm/square and formed from: (a) between 40 and 80 percent by dry weight of a base metal powder relative to the total of base metal and boron which oxidizes upon firing in the presence of air and becomes substantially electrically non-conductive and selected from the group consisting of nickel, copper, cobalt and mixtures thereof; (b) between 4 and 50 percent by dry weight of boron powder relative to the total of base metal and boron; and (c) up to about 20 percent by dry weight of glass frit relative to the total of base metal, boron and glass frit; said conductor formed by firing in the presence of air a paste comprising powders having particles less than 325 mesh of said base metal powder, boron and glass frit mixed with a suitable vehicle to produce a conductor having a sheet resistance less than about 1 ohm/square.
References Cited (Backward Citations)
US2313410A
Cited
US2221286A
Cited
US2886476A
Cited
US3151386A
Cited
US3627573A
Cited
US3647532A
Cited
US3622523A
Cited
US3948812A
Cited
US3824127A
Cited
US3928242A
Cited
US4079156A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-23 | 1982-04-24 | 1982-10-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-23 | 1986-04-24 | 1986-10-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-23 | 1990-04-24 | 1990-10-24 | $7700.00 | Window Closed / Lapsed |