Epitaxially extended polycrystalline structures utilizing a predeposit of amorphous silicon with subsequent annealing
Assignee: International Business Machines Corp
•
Filing: 1980-11-03
•
Granted: 1982-11-09
•
Expires: 2000-11-03
Abstract
Abstract Disclosed is a process for reducing microcracks and microvoids in the formation of polycrystalline (polysilicon) structures from initial layers of amorphous silicon by annealing. In annealing of amorphous silicon to the polycrystalline form, the crystal grains are thickness limited; and thus by maintaining the thickness below 1000 angstroms, the spacing between contrasting material forming the crystal grains can be minimized on anneal. The resultant equiaxial grains are used as seed crystals for epi-like growth of silicon from them into the required or desired layer thickness.
Inventors
- 👤 Ven Y. Doo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 21:03
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/20; H10P14/38; H10P14/3802; H10D; H10D62/00; H10D62/40; H10P14/24; H10P14/32; H10P14/3202; H10P14/3204; H10P14/3211; H10P14/34; H10P14/3402; H10P14/3404; H10P14/3411; H10P14/3451; H10P14/3452; H10P14/3456; H10P95/00; H10P95/90; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H10W20/065; Y; Y10; Y10S; Y10S148/00; Y10S148/003; Y10S148/026; Y10S148/122; Y10S148/123; Y10S148/164
Claims Analysis
Total Claims: 45
Claim 1
Independent Claim
115 words
A method of forming a polycrystalline layer on an insulator coating of a silicon integrated circuit depositing from a silicon forming gaseous phase a discrete amorphous silicon layer in a thickness not exceeding 1000 angstroms on said insulator coating at a temperature in the range of about 550° to 600° C.; heating the resultant structure at a temperature of about 800° C. to convert said amorphous silicon layer to an equiaxial polycrystalline seed layer, and epitaxially extending the crystal grains of said polycrystalline seed layer by heating thereof in a silicon forming ambient at a temperature in the range of about 650° to about 700° C. for a time sufficient to grow the thickness desired.
Claim 2
Independent Claim
115 words
A method of forming a polycrystalline layer on an insulator coating of a silicon integrated circuit depositing from a silicon forming gaseous phase a discrete amorphous silicon layer in a thickness not exceeding 1000 angstroms on said insulator coating at a temperature in the range of about 550° to 600° C.; heating the resultant structure at a temperature of about 800° C. to convert said amorphous silicon layer to an equiaxial polycrystalline seed layer, and epitaxially extending the crystal grains of said polycrystalline seed layer by heating thereof in a silicon forming ambient at a temperature in the range of about 650° to about 700° C. for a time sufficient to grow the thickness desired.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein said insulating layer is thermally grown silicon dioxide.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein said insulating layer is a chemically vapor deposited silicon dioxide.
Claim 5
Dependent Claim
18 words
The method of claim 1 wherein said extended polycrystalline layer is doped with a conductivity type determining impurity.
Claim 6
Independent Claim
140 words
A method for forming polycrystalline layers on an insulator coating of an integrated circuit device, comprising: forming a first polycrystalline silicon layer on said insulator coating, forming a second insulator coating on said polycrystalline silicon layer, depositing from a silicon forming gaseous phase a discrete amorphous silicon layer in a thickness not exceeding 1000 angstroms on said second insulator coating at a temperature in the range of about 550° C. to about 600° C., heating the resultant structure at a temperature of about 800° C. to convert said amorphous layer to a second polycrystalline layer having equiaxial grains, and epitaxially extending the crystal grains of said second polycrystalline layer, by heating thereof in a silicon forming ambient at a temperature in the range of about 650° C. to about 700° C. for a time sufficient to grow the thickness desired.
Claim 7
Independent Claim
140 words
A method for forming polycrystalline layers on an insulator coating of an integrated circuit device, comprising: forming a first polycrystalline silicon layer on said insulator coating, forming a second insulator coating on said polycrystalline silicon layer, depositing from a silicon forming gaseous phase a discrete amorphous silicon layer in a thickness not exceeding 1000 angstroms on said second insulator coating at a temperature in the range of about 550° C. to about 600° C., heating the resultant structure at a temperature of about 800° C. to convert said amorphous layer to a second polycrystalline layer having equiaxial grains, and epitaxially extending the crystal grains of said second polycrystalline layer, by heating thereof in a silicon forming ambient at a temperature in the range of about 650° C. to about 700° C. for a time sufficient to grow the thickness desired.
Claim 8
Dependent Claim
18 words
The method of claim 5 wherein said extended polycrystalline layer is doped with a conductivity type determining impurity.
Claim 9
Dependent Claim
12 words
The method of claim 5 wherein said second polycrystalline layer is doped.
Claim 10
Dependent Claim
41 words
The method of claim 5 including forming a third insulating coating on said second polycrystalline layer, forming a via hole through said third insulating coating, to the second said polycrystalline layer, and forming a conductive metal contact in said via opening.
Claim 11
Dependent Claim
12 words
The method of claim 8 wherein said second polycrystalline layer is doped.
Claim 12
Dependent Claim
17 words
The method of claim 5 wherein the first said insulating coating is a thermally grown silicon dioxide.
Claim 13
Dependent Claim
12 words
The method of claim 10 wherein said second polycrystalline layer is doped.
Claim 14
Dependent Claim
23 words
The method of claim 10 wherein at least one of said second and third insulating coatings comprises a chemically vapor deposited silicon dioxide.
Claim 15
Dependent Claim
12 words
The method of claim 12 wherein said second polycrystalline layer is doped.
Claim 16
Dependent Claim
111 words
The method of claim 5 wherein the first polycrystalline layer is formed by depositing a discrete amorphous silicon layer in a thickness not exceeding about 1000 angstroms on the first said insulating coating at a temperature in the range of about 550 to about 600° C., heating this said amorphous silicon layer at a temperature of about 800° C. to convert it to a polycrystalline seed layer, and epitaxially extending the crystal grains of said polycrystalline layer in a silicon forming ambient at a temperature in the range of about 650° C. to about 700° C. for a time sufficient to grow the desired thickness of the said first polycrystalline layer.
Claim 17
Dependent Claim
18 words
The method of claim 14 wherein said extended polycrystalline layer is doped with a conductivity type determining impurity.
Claim 18
Dependent Claim
41 words
The method of claim 14 including forming a third insulating coating on said second polycrystalline layer, forming a via hole through said third insulating coating, to the second said polycrystalline layer, and forming a conductive metal contact in said via opening.
Claim 19
Dependent Claim
12 words
The method of claim 14 wherein said second polycrystalline layer is doped.
Claim 20
Dependent Claim
17 words
The method of claim 14 wherein the first said insulating coating is a thermally grown silicon dioxide.
Claim 21
Dependent Claim
23 words
The method of claim 18 wherein at least one of said second and third insulating coatings comprises a chemically vapor deposited silicon dioxide.
Claim 22
Dependent Claim
12 words
The method of claim 19 wherein said second polycrystalline layer is doped.
Claim 23
Dependent Claim
12 words
The method of claim 18 wherein said second polycrystalline layer is doped.
Claim 24
Dependent Claim
20 words
The method of claim 1 wherein said polycrystalline seed layer has grain sizes corresponding to the thickness of said layer.
Claim 25
Dependent Claim
14 words
The method of claim 22 wherein said insulating layer is thermally grown silicon dioxide.
Claim 26
Dependent Claim
16 words
The method of claim 22 wherein said insulating layer is a chemically vapor deposited silicon dioxide.
Claim 27
Dependent Claim
18 words
The method of claim 22 wherein said extended polycrystalline layer is doped with a conductivity type determining impurity.
Claim 28
Dependent Claim
19 words
The method of claim 5 wherein said grains of said sizes corresponding to the thickness of said second layer.
Claim 29
Dependent Claim
19 words
The method of claim 26 wherein said extended second polycrystalline layer is doped with a conductivity type determining impurity.
Claim 30
Dependent Claim
12 words
The method of claim 26 wherein said second polycrystalline layer is doped.
Claim 31
Dependent Claim
41 words
The method of claim 26 including forming a third insulating coating on said second polycrystalline layer, forming a via hole through said third insulating coating, to the second said polycrystalline layer, and forming a conductive metal contact in said via opening.
Claim 32
Dependent Claim
12 words
The method of claim 27 wherein said second polycrystalline layer is doped.
Claim 33
Dependent Claim
17 words
The method of claim 26 wherein the first said insulating coating is a thermally grown silicon dioxide.
Claim 34
Dependent Claim
12 words
The method of claim 31 wherein said second polycrystalline layer is doped.
Claim 35
Dependent Claim
23 words
The method of claim 31 wherein at least one of said second and third insulating coatings comprises a chemically vapor deposited silicon dioxide.
Claim 36
Dependent Claim
12 words
The method of claim 33 wherein said second polycrystalline layer is doped.
Claim 37
Dependent Claim
122 words
The method of claim 26 wherein the first polycrystalline layer is formed by depositing from a silicon forming gaseous phase a discrete amorphous silicon layer in a thickness not exceeding about 1000 angstroms on the first said insulating coating at a temperature in the range of about 550 to about 600° C., heating this said amorphous silicon layer at a temperature of about 750° C. to about 800° C. to convert it to an equiaxial polycrystalline seed layer, and epitaxially extending the crystal grains of said polycrystalline layer in a silicon forming ambient at a temperature in the range of about 650° C. to about 700° C. for a time sufficient to grow the desired thickness of the said first polycrystalline layer.
Claim 38
Dependent Claim
19 words
The method of claim 35 wherein said extended first polycrystalline layer is doped with a conductivity type determining impurity.
Claim 39
Dependent Claim
41 words
The method of claim 35 including forming a third insulating coating on said second polycrystalline layer, forming a via hole through said third insulating coating, to the second said polycrystalline layer, and forming a conductive metal contact in said via opening.
Claim 40
Dependent Claim
12 words
The method of claim 35 wherein said second polycrystalline layer is doped.
Claim 41
Dependent Claim
17 words
The method of claim 35 wherein the first said insulating coating is a thermally grown silicon dioxide.
Claim 42
Dependent Claim
23 words
The method of claim 39 wherein at least one of said second and third insulating coatings comprises a chemically vapor deposited silicon dioxide.
Claim 43
Dependent Claim
12 words
The method of claim 40 wherein said second polycrystalline layer is doped.
Claim 44
Dependent Claim
12 words
The method of claim 39 wherein said second polycrystalline layer is doped.
Claim 45
Dependent Claim
22 words
The method of claim 35 wherein the said first layer grains have a size corresponding to the thickness of said first layer.
References Cited (Backward Citations)
US3370980A
Cited
US3479237A
Cited
US3533857A
Cited
US3558374A
Cited
US3519901A
Cited
US3589949A
Cited
US3586542A
Cited
US3736192A
Cited
US3730765A
Cited
US4087571A
Cited
US3811076A
Cited
US3841926A
Cited
US3900345A
Cited
US4123300A
Cited
US4270960A
Cited
US4249968A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-08 | 1986-05-10 | 1986-11-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-08 | 1990-05-10 | 1990-11-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-08 | 1994-05-10 | 1994-11-09 | $7700.00 | Window Closed / Lapsed |