Method of fabricating a transparent metal oxide electrode structure on a solid-state electrooptical device
Assignee: Eastman Kodak Co
•
Filing: 1980-12-22
•
Granted: 1982-06-22
•
Expires: 2000-12-22
Abstract
Abstract A method of fabricating an electrode structure of transparent metal oxide on a solid-state electrooptical device is disclosed. A layer of conductive transparent metal oxide is deposited on the surface of the device. Thereafter, the transparent conductive layer is covered with a layer of pattern metal that forms a good electrical contact with the transparent metal oxide and is etchable independently of the transparent metal oxide. Portions of the pattern metal are etched away to define the desired electrode pattern using a photolithographic technique and an etchant that attacks the pattern metal but does not substantially attack the transparent metal oxide layer. Portions of the transparent metal oxide layer not covered by the pattern metal are removed using an etchant that attacks the transparent metal oxide but does not substantially attack the pattern metal. Portions of the remaining pattern metal are removed from imaging areas of the device, leaving pattern metal in the peripheral areas where electrical connections to the electrodes are to be located, using photolithographic techniques and the etchant that attacks the pattern metal but not the transparent metal oxide. In the preferred embodiment, the pattern metal comprises chromium, and to complete the circiut and form bonding pads, a final metallization layer (e.g. gold) is deposited over the structure, and the structure is baked to adhere the final metal to the remaining portions of the chromium. Finally, portions of the final layer of metal are removed leaving the conductor pattern and the bonding pads.
Inventors
- 👤 Frank T. J. Smith
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 20:28
CPC Classifications
H; H10; H10D; H10D44/00; H10D44/01; H10D44/041; H10F; H10F30/00; H10F30/20; H10F30/21; H10F30/28; H10F30/2823; H10F77/00; H10F77/20; H10F77/206; H10F77/244; Y; Y10; Y10S; Y10S428/00; Y10S428/901; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
243 words
A method of fabricating an electrode structure of transparent metal oxide on a solid-state electrooptic device of the type having transparent gate electrodes through which light passes to expose the device, comprising the steps of: depositing a layer of conductive transparent metal oxide on the device; depositing a layer of pattern metal comprising a transition metal capable of forming a good electrical contact with the transparent metal oxide, and capable of being etched independently of the transparent metal oxide; removing by etching, portions of the pattern metal to define a desired electrode pattern employing photolithographic techniques using an etchant that attacks the pattern metal, but does not substantially attack the metal oxide layer; removing by etching, the portions of the metal oxide layer not covered by the pattern metal, using an etchant that attacks the transparent metal oxide but does not substantially attack the pattern metal; further removing by etching, portions of the pattern metal from optically active areas of the device, but leaving pattern metal in the peripheral areas of the electrode structure where electrical contacts are to be made, using photolithographic techniques and an etchant that attacks the pattern metal but not the transparent metal oxide; depositing a final layer of metal over the structure; baking the structure at a temperature sufficient to promote adhesion of the final metal layer to the pattern metal; and etching away portions of the final metal layer to define electrical conductive paths and bonding pads.
Claim 2
Independent Claim
243 words
A method of fabricating an electrode structure of transparent metal oxide on a solid-state electrooptic device of the type having transparent gate electrodes through which light passes to expose the device, comprising the steps of: depositing a layer of conductive transparent metal oxide on the device; depositing a layer of pattern metal comprising a transition metal capable of forming a good electrical contact with the transparent metal oxide, and capable of being etched independently of the transparent metal oxide; removing by etching, portions of the pattern metal to define a desired electrode pattern employing photolithographic techniques using an etchant that attacks the pattern metal, but does not substantially attack the metal oxide layer; removing by etching, the portions of the metal oxide layer not covered by the pattern metal, using an etchant that attacks the transparent metal oxide but does not substantially attack the pattern metal; further removing by etching, portions of the pattern metal from optically active areas of the device, but leaving pattern metal in the peripheral areas of the electrode structure where electrical contacts are to be made, using photolithographic techniques and an etchant that attacks the pattern metal but not the transparent metal oxide; depositing a final layer of metal over the structure; baking the structure at a temperature sufficient to promote adhesion of the final metal layer to the pattern metal; and etching away portions of the final metal layer to define electrical conductive paths and bonding pads.
Claim 3
Dependent Claim
50 words
The invention claimed in claim 1, wherein the transparent metal oxide layer is a material selected from the group consisting of SnO 2 , In 2 O 3 , CdO, Sb 2 O 3 , and mixtures of these and the transparent metal oxide etchant is hydrochloric or hydroiodic acid.
Claim 4
Dependent Claim
27 words
The invention claimed in claim 2 wherein the pattern metal is chromium, and the chromium etchant is a mixture of nitric acid, water and ceric ammonium nitrate.
Claim 5
Dependent Claim
19 words
The invention claimed in claim 2, wherein the pattern metal is gold, and the gold etchant is potassium polyiodide.
Claim 6
Dependent Claim
13 words
The invention claimed in claim 1 wherein the final metal layer is gold.
Claim 7
Dependent Claim
17 words
The invention claimed in claim 5 wherein the final metal etchant is a solution of potassium polyiodide.
Claim 8
Dependent Claim
12 words
The invention claimed in claim 1 wherein the final metal is aluminum.
Claim 9
Dependent Claim
16 words
The invention claimed in claim 7 wherein the final metal etchant is a halide containing plasma.
Claim 10
Dependent Claim
15 words
The invention claimed in claim 8 wherein the halide-containing plasma is produced from carbon tetrachloride.
Claim 11
Dependent Claim
253 words
A solid-state electrooptic device of the type having a patterned electrode structure of transparent metal oxide through which light passes to expose the device, with peripheral areas covered by a metal, for electrical contact to the metal oxide electrode structure, formed by the process of: depositing a layer of conductive transparent metal oxide on the device; depositing a layer of pattern metal comprising a transition metal capable of forming a good electrical contact with the transparent metal oxide, and capable of being etched independently of the transparent metal oxide; removing by etching, portions of the pattern metal to define a desired electrode pattern employing photolithographic techniques using an etchant that attacks the pattern metal, but does not substantially attack the metal oxide layer; removing by etching, the portions of the metal oxide layer not covered by the pattern metal, using an etchant that attacks the transparent metal oxide but does not substantially attack the pattern metal; further removing by etching, portions of the pattern metal from optically active areas of the device, but leaving pattern metal in the peripheral areas of the electrode structure where electrical contacts are to be made, using photolithographic techniques and an etchant that attacks the pattern metal but not the transparent metal oxide; depositing a final layer of metal over the structure; baking the structure at a temperature sufficient to promote adhesion of the final metal layer to the pattern metal; and etching away portions of the final metal layer to define electrical conductive paths and bonding pads.
Claim 12
Dependent Claim
253 words
A solid-state electrooptic device of the type having a patterned electrode structure of transparent metal oxide through which light passes to expose the device, with peripheral areas covered by a metal, for electrical contact to the metal oxide electrode structure, formed by the process of: depositing a layer of conductive transparent metal oxide on the device; depositing a layer of pattern metal comprising a transition metal capable of forming a good electrical contact with the transparent metal oxide, and capable of being etched independently of the transparent metal oxide; removing by etching, portions of the pattern metal to define a desired electrode pattern employing photolithographic techniques using an etchant that attacks the pattern metal, but does not substantially attack the metal oxide layer; removing by etching, the portions of the metal oxide layer not covered by the pattern metal, using an etchant that attacks the transparent metal oxide but does not substantially attack the pattern metal; further removing by etching, portions of the pattern metal from optically active areas of the device, but leaving pattern metal in the peripheral areas of the electrode structure where electrical contacts are to be made, using photolithographic techniques and an etchant that attacks the pattern metal but not the transparent metal oxide; depositing a final layer of metal over the structure; baking the structure at a temperature sufficient to promote adhesion of the final metal layer to the pattern metal; and etching away portions of the final metal layer to define electrical conductive paths and bonding pads.
References Cited (Backward Citations)
US3740280A
Cited
US3928658A
Cited
US3904453A
Cited
US3941630A
Cited
US4012767A
Cited
US4139443A
Cited
US4182647A
Cited
US4178403A
Cited
US4172004A
Cited
US4184909A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-21 | 1985-12-21 | 1986-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-21 | 1989-12-21 | 1990-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-21 | 1993-12-21 | 1994-06-22 | $7700.00 | Window Closed / Lapsed |