Dielectric isolation method using shallow oxide and polycrystalline silicon utilizing a preliminary etching step
Assignee: Massachusetts Institute of Technology
•
Filing: 1979-07-27
•
Granted: 1980-11-04
•
Expires: 1999-07-27
Abstract
Abstract A process is described which combines polycrystalline isolation of collectors and shallow oxide isolation of bases. This approach is capable of providing deep dielectric isolation, surface planarity and the high density of walled emitter geometries, a combination heretofore unobtainable by any other means. This isolation scheme has been used to fabricate ECL gate chains. The transistors were located in 2.5 micron thick n epi islands surrounded by 5x105 ohm-cm polysilicon selectively oxidized with silicon nitride masking to a thickness of one micron. The oxide "bump" at the nitride mask was typically 3000 A and the epi-poly step height was as small as 2600 A. The circuits have polysilicon resistors and were fabricated using both thermal diffusion and ion implantation. The power-delay product of these circuits was approximately one-half that of junction isolated circuits.
Inventors
- 👤 Jack I. Raffel
- 👤 Stephen E. Bernacki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:34
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/40; H10D1/47; H10D62/00; H10D62/10; H10D62/113; H10D62/115; H10W; H10W10/00; H10W10/01; H10W10/041; H10W10/40
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
193 words
A method for achieving isolation of the silicon islands of integrated circuits comprising: isotropically etching to a predetermined depth those portions of a silicon substrate surface which correspond to the area surrounding the bottom of silicon islands to be subsequently grown, oxidizing the preceding etched silicon surface, simultaneously growing a polycrystalline layer of silicon on said oxidized surface and an epitaxial layer on the remaining portions of said silicon substrate to form said silicon islands, masking the surface of said silicon islands leaving the portions of said islands contiguous to said polysilicon surface unmasked and also any regions of said island surface for oxide isolation between impurity junctions, oxidizing the exposed silicons, the depth of such silicon etching and the thickness of said oxide being such that the top of said oxide is substantially co-planar with the top surface of the masked silicon islands and the bottom of the oxide extends below the junction depth of junctions to be subsequently formed in said epitaxial silicon islands, removing said mask on the surface of the silicon islands to provide a surface into which impurities may be provided to form junction devices in said islands.
Claim 2
Independent Claim
193 words
A method for achieving isolation of the silicon islands of integrated circuits comprising: isotropically etching to a predetermined depth those portions of a silicon substrate surface which correspond to the area surrounding the bottom of silicon islands to be subsequently grown, oxidizing the preceding etched silicon surface, simultaneously growing a polycrystalline layer of silicon on said oxidized surface and an epitaxial layer on the remaining portions of said silicon substrate to form said silicon islands, masking the surface of said silicon islands leaving the portions of said islands contiguous to said polysilicon surface unmasked and also any regions of said island surface for oxide isolation between impurity junctions, oxidizing the exposed silicons, the depth of such silicon etching and the thickness of said oxide being such that the top of said oxide is substantially co-planar with the top surface of the masked silicon islands and the bottom of the oxide extends below the junction depth of junctions to be subsequently formed in said epitaxial silicon islands, removing said mask on the surface of the silicon islands to provide a surface into which impurities may be provided to form junction devices in said islands.
Claim 3
Dependent Claim
116 words
The method of claim 1 wherein said silicon etching step comprises: depositing 500 A of silicon dioxide on said silicon substrate, depositing a nitride layer on said silicon dioxide surface, masking and etching said nitride and oxide layer to remove all the nitride and oxide and expose the surface of the substrate except where buried collectors are to be subsequently formed in said substrate, the said isotropic etching of the silicon surface is to a depth which results in the surface of the subsequently grown oxide on the surface of the polycrystalline silicon and the surface of the epitaxial silicon to be co-planar, said nitride and oxide mask being stripped away prior to said silicon growth.
Claim 4
Dependent Claim
55 words
The method of claim 1 wherein said silicon substrate is prepared for the initial growth of oxide by implanting or diffusing a p-type dopant into the surface of the substrate prior to the growth of the first oxide layer to increase the impurity concentration of the surface relative to the bulk doping of the substrate.
References Cited (Backward Citations)
US3386865A
Cited
US3791882A
Cited
US3871007A
Cited
US4009484A
Cited
US3736193A
Cited
US3947299A
Cited
US4016596A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1983-11-04 | 1984-05-05 | 1984-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1987-11-04 | 1988-05-05 | 1988-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1991-11-04 | 1992-05-05 | 1992-11-04 | $7700.00 | Window Closed / Lapsed |