US6319775B1
Expired / Lapsed
US
⏱️ 0.0 years remaining
Nitridation process for fabricating an ONO floating-gate electrode in a two-bit EEPROM device
Assignee: Monterey Research LLC
•
Filing: 1999-10-25
•
Granted: 2001-11-20
•
Expires: 2019-10-25
Abstract
Abstract A process for fabricating an ONO floating-gate electrode in a two-bit EEPROM device includes the formation of a nitrogenated top oxide layer. The process includes the sequential formation of a silicon nitride layer and a top oxide layer using an in-situ LPCVD or RTCVD deposition process in which the silicon nitride layer is not exposed to ambient atmosphere prior to the formation of the top oxide layer. After forming the top oxide layer, an annealing process is carried out to diffuse nitrogen into the top oxide layer. The formation of a nitrogenated top oxide layer provides an improved two-bit EEPROM memory device by reducing charge leakage in the ONO floating-gate electrode.
Inventors
- 👤 Arvind Halliyal
- 👤 Robert B. Ogle
- 👤 Susan G. Kim
- 👤 Kenneth Au
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:16
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6927; H10B; H10B43/00; H10B43/30; H10D; H10D30/00; H10D30/01; H10D30/021; H10D30/0413; H10D64/00; H10D64/01; H10D64/031; H10D64/037; H10P14/63; H10P14/6326; H10P14/6328; H10P14/6334; H10P14/65; H10P14/6516; H10P14/6518; H10P14/6524; H10P14/6526; H10P14/6529; H10P14/66; H10P14/668; H10P14/6681; H10P14/6682; H10P14/662; H10P14/69215; H10P14/694; H10P14/6943; H10P14/69433
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
114 words
A process for fabricating an ONO floating-gate electrode in a two-bit EEPROM device comprising the steps of: providing a semiconductor substrate; forming a first silicon oxide layer overlying the semiconductor substrate; forming a silicon nitride layer overlying the first silicon oxide layer; forming a second silicon oxide layer overlying the silicon nitride layer by a first rapid thermal chemical vapor deposition process at a temperature from about 700° C. to about 800° C. using nitrous oxide and dichlorosilane; and subjecting the second silicon oxide layer to a second rapid thermal chemical vapor deposition process with exposure to a nitrogen-containing gas to form a nitridated silicon oxide layer, and to form said ONO floating-gate electrode.
Claim 2
Dependent Claim
114 words
A process for fabricating an ONO floating-gate electrode in a two-bit EEPROM device comprising the steps of: providing a semiconductor substrate; forming a first silicon oxide layer overlying the semiconductor substrate; forming a silicon nitride layer overlying the first silicon oxide layer; forming a second silicon oxide layer overlying the silicon nitride layer by a first rapid thermal chemical vapor deposition process at a temperature from about 700° C. to about 800° C. using nitrous oxide and dichlorosilane; and subjecting the second silicon oxide layer to a second rapid thermal chemical vapor deposition process with exposure to a nitrogen-containing gas to form a nitridated silicon oxide layer, and to form said ONO floating-gate electrode.
Claim 3
Dependent Claim
40 words
The process of claim 1 , wherein subjecting the second silicon oxide layer to a second rapid thermal chemical vapor deposition process in a nitrogen-containing gas is carried out at a temperature from about 800° C. to about 1100° C.
Claim 4
Dependent Claim
23 words
The process of claim 1 , wherein the nitrogen-containing gas is selected from the group consisting of ammonia, nitrogen oxide, and nitrous oxide.
Claim 5
Dependent Claim
38 words
The process of claim 1 , further comprising: prior to forming the second silicon oxide layer, transferring the semiconductor structure to an oxide deposition chamber under vacuum conditions to mitigate exposing the silicon nitride layer to ambient air.
Claim 6
Dependent Claim
27 words
The process of claim 1 , wherein nitridating the second silicon oxide layer comprises flowing the nitrogen-containing gas into a rapid thermal chemical vapor deposition process apparatus.
Claim 7
Dependent Claim
37 words
The process of claim 1 , wherein the step of forming a nitrogenated silicon oxide layer comprises forming a nitrogenated silicon oxide layer having a nitrogen concentration of about 0 wt. % to about 10 wt. %.
Claim 8
Dependent Claim
141 words
A process for fabricating a stacked-gate structure including an ONO floating-gate electrode in a two-bit EEPROM device comprising: providing a semiconductor substrate having a first bit-line oxide layer and a second bit-line oxide layer therein separated by a substrate surface region; forming the ONO floating-gate electrode on the substrate surface region comprising: sequentially forming a first silicon oxide layer on the substrate surface region, a silicon nitride layer overlying the first silicon oxide layer, and a second silicon oxide layer overlying the silicon nitride layer; and subjecting the second silicon oxide layer to a rapid thermal chemical vapor deposition process in a nitrogen-containing gas to form a nitridated silicon oxide layer, and to form said ONO floating-gate electrodes; and depositing a control gate electrode layer overlying the ONO floating gate electrode to form a stacked-gate structure on the substrate surface region.
Claim 9
Dependent Claim
141 words
A process for fabricating a stacked-gate structure including an ONO floating-gate electrode in a two-bit EEPROM device comprising: providing a semiconductor substrate having a first bit-line oxide layer and a second bit-line oxide layer therein separated by a substrate surface region; forming the ONO floating-gate electrode on the substrate surface region comprising: sequentially forming a first silicon oxide layer on the substrate surface region, a silicon nitride layer overlying the first silicon oxide layer, and a second silicon oxide layer overlying the silicon nitride layer; and subjecting the second silicon oxide layer to a rapid thermal chemical vapor deposition process in a nitrogen-containing gas to form a nitridated silicon oxide layer, and to form said ONO floating-gate electrodes; and depositing a control gate electrode layer overlying the ONO floating gate electrode to form a stacked-gate structure on the substrate surface region.
Claim 10
Dependent Claim
39 words
The process of claim 7 , wherein subjecting the second silicon oxide layer to a rapid thermal chemical vapor deposition process in a nitrogen-containing gas is carried out at a temperature of about 700° C. to about 1000° C.
Claim 11
Dependent Claim
23 words
The process of claim 7 , wherein the nitrogen-containing gas is selected from the group consisting of ammonia, nitrogen oxide, and nitrous oxide.
Claim 12
Dependent Claim
38 words
The process of claim 7 , further comprising: prior to forming the second silicon oxide layer, transferring the semiconductor structure to an oxide deposition chamber under vacuum conditions to mitigate exposing the silicon nitride layer to ambient air.
Claim 13
Dependent Claim
27 words
The process of claim 7 , wherein nitridating the second silicon oxide layer comprises flowing the nitrogen-containing gas into a rapid thermal chemical vapor deposition process apparatus.
Claim 14
Dependent Claim
37 words
The process of claim 2 , wherein the step of forming a nitrogenated silicon oxide layer comprises forming a nitrogenated silicon oxide layer having a nitrogen concentration of about 0 wt. % to about 10 wt. %.
Claim 15
Dependent Claim
164 words
A process for fabricating an ONO floating-gate electrode in a two-bit device comprising the steps of: providing a semiconductor substrate having a silicon surface region; depositing a bottom silicon oxide layer overlying the surface region; depositing a silicon nitride layer overlying the bottom silicon oxide layer; depositing a top silicon oxide layer overlying the silicon nitride layer by a first rapid thermal chemical vapor deposition process at a temperature from about 700° C. to about 800° C. using nitrous oxide and dichlorosilane; and subjecting the top silicon layer to a second rapid thermal chemical vapor deposition process in a nitrogen-containing gas ambient selected from the group consisting of ammonia, nitrogen oxide, and nitrous oxide to form a nitridated silicon oxide layer having a nitrogen concentration from about 0 wt. % to about 10 wt. % to form said ONO floating-gate electrode, wherein the second rapid thermal chemical vapor deposition process is carried out at a temperature from about 700° C. to about 1000° C.
Claim 16
Dependent Claim
164 words
A process for fabricating an ONO floating-gate electrode in a two-bit device comprising the steps of: providing a semiconductor substrate having a silicon surface region; depositing a bottom silicon oxide layer overlying the surface region; depositing a silicon nitride layer overlying the bottom silicon oxide layer; depositing a top silicon oxide layer overlying the silicon nitride layer by a first rapid thermal chemical vapor deposition process at a temperature from about 700° C. to about 800° C. using nitrous oxide and dichlorosilane; and subjecting the top silicon layer to a second rapid thermal chemical vapor deposition process in a nitrogen-containing gas ambient selected from the group consisting of ammonia, nitrogen oxide, and nitrous oxide to form a nitridated silicon oxide layer having a nitrogen concentration from about 0 wt. % to about 10 wt. % to form said ONO floating-gate electrode, wherein the second rapid thermal chemical vapor deposition process is carried out at a temperature from about 700° C. to about 1000° C.
Claim 17
Dependent Claim
38 words
The process of claim 13 , further comprising: prior to depositing the top silicon oxide layer, transferring the semiconductor structure to an oxide deposition chamber under vacuum conditions to mitigate exposing the silicon nitride layer to ambient air.
References Cited (Backward Citations)
US5304829A
Cited
US5496753A
Cited
US5371028A
Cited
US6069041A
Cited
US5966603A
Cited
US5851881A
Cited
US5888870A
Cited
US6063666A
Cited
US6074917A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2004-11-19 | 2005-05-21 | 2005-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2008-11-19 | 2009-05-21 | 2009-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2012-11-19 | 2013-05-21 | 2013-11-20 | $7700.00 | Window Closed / Lapsed |