Laser curing of spin-on dielectric thin films
Assignee: National University of Singapore
•
Filing: 1998-11-16
•
Granted: 2000-09-19
•
Expires: 2018-11-16
Abstract
Abstract A process for curing low-k spin-on dielectric layers based on alkyl silsesquioxane polymers by laser scanning is described wherein curing is achieved by both photothermal and photochemical mechanisms. The layers are deposited by spin deposition, dried and cured by raster scanning with a pulsed laser at energies between 0.1 and 1 Joules/cm 2 . Because the laser causes heating of the layer, a nitrogen jet is applied in the wake of the scanning laser beam to rapidly cool the layer and to inhibit oxidation and moisture absorption. The laser induced heating also assists in the discharge of moisture and by-products of the polymerization process. The laser operates at wavelengths between 200 and 400 nm. Insulative layers such as silicon oxide are sufficiently transparent at these so that oxide segments overlying the polymer layer do not inhibit the curing process. Implementation of the laser scanning feature is readily incorporated into an existing spin-on deposition and curing tool.
Inventors
- 👤 Chee Tee Chua
- 👤 Yuan-Ping Lee
- 👤 Mei Sheng Zhou
- 👤 Lap Chan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 08:38
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/071; H10W20/093; H10W20/095; H10P; H10P14/00; H10P14/60; H10P14/65; H10P14/6502; H10P14/6506; H10P14/6516; H10P14/6548; H10P14/66; H10P14/665; H10P14/69; H10P14/692; H10P14/6921; H10P14/6922; H10P14/6926; H10P34/00; H10P34/40; H10P34/42; H10P95/00; H10P95/08; H10W20/074; H10W20/077; H10P14/63; H10P14/6326; H10P14/6342
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
78 words
A method for forming a polymer dielectric layer on a substrate comprising: (a) providing a substrate; (b) depositing a polymer layer by spin coating; (c) baking said polymer layer; and (d) curing said polymer layer by raster scanning a laser beam over said polymer layer while cooling said polymer layer after passage of said laser beam by projecting a flow of a cooling gas on the surface of said polymer layer in the wake of said laser beam.
Claim 2
Independent Claim
78 words
A method for forming a polymer dielectric layer on a substrate comprising: (a) providing a substrate; (b) depositing a polymer layer by spin coating; (c) baking said polymer layer; and (d) curing said polymer layer by raster scanning a laser beam over said polymer layer while cooling said polymer layer after passage of said laser beam by projecting a flow of a cooling gas on the surface of said polymer layer in the wake of said laser beam.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said polymer layer is selected from the group consisting of an alkyl silsesquioxane, an aryl silsesquioxane, and a polyimide.
Claim 4
Dependent Claim
12 words
The method of claim 1 wherein said substrate is a silicon wafer.
Claim 5
Dependent Claim
17 words
The method of claim 1 wherein said polymer layer is between about 4,000 and 5,600 Angstroms thick.
Claim 6
Dependent Claim
49 words
The method of claim 1 wherein said laser beam is provided by a pulsed Nd/YAG laser having a pulse frequency of between about 10 Hz and 10 kHz, a wavelength of between about 200 and 400 nm., and an energy of between about 0.1 and 1 Joule/cm 2 .
Claim 7
Dependent Claim
16 words
The method of claim 1 wherein said laser beam is provided by a pulsed excimer laser.
Claim 8
Dependent Claim
20 words
The method of claim 1 wherein said laser beam has a spot size of 100 mm 2 . or thereabout.
Claim 9
Dependent Claim
11 words
The method of claim 1 wherein said cooling gas is nitrogen.
Claim 10
Independent Claim
152 words
A method for forming an inter metal dielectric layer of an integrated circuit having a polymer dielectric between conductive elements comprising: (a) providing a substrate having integrated circuit components and a pattern of conductive elements on a first insulative layer; (b) depositing a conformal second insulative layer on said pattern; (c) depositing a polymer layer on said second insulative layer by spin coating; (d) baking said polymer layer; (e) curing said polymer layer by raster scanning a laser beam over said polymer layer while cooling said polymer layer after passage of said laser beam by projecting a flow of a cooling gas on the surface of said polymer layer in the wake of said laser beam; (f) etching back said polymer layer until portions of said second insulative layer are exposed over said conductive elements; (g) forming a third insulative layer on said polymer layer; and (h) planarizing said third insulative layer.
Claim 11
Independent Claim
152 words
A method for forming an inter metal dielectric layer of an integrated circuit having a polymer dielectric between conductive elements comprising: (a) providing a substrate having integrated circuit components and a pattern of conductive elements on a first insulative layer; (b) depositing a conformal second insulative layer on said pattern; (c) depositing a polymer layer on said second insulative layer by spin coating; (d) baking said polymer layer; (e) curing said polymer layer by raster scanning a laser beam over said polymer layer while cooling said polymer layer after passage of said laser beam by projecting a flow of a cooling gas on the surface of said polymer layer in the wake of said laser beam; (f) etching back said polymer layer until portions of said second insulative layer are exposed over said conductive elements; (g) forming a third insulative layer on said polymer layer; and (h) planarizing said third insulative layer.
Claim 12
Dependent Claim
11 words
The method of claim 9 wherein said conductive elements are aluminum.
Claim 13
Dependent Claim
24 words
The method of claim 9 wherein said second insulative layer is selected from the group consisting of silicon oxide, silicon nitride, and silicon oxynitride.
Claim 14
Dependent Claim
18 words
The method of claim 9 wherein said second insulative layer is between about 3,000 and 6,500 Angstroms thick.
Claim 15
Dependent Claim
25 words
The method of claim 1 wherein said polymer layer is selected from the group consisting of an alkyl silsesquioxane, an aryl silsesquioxane, and a polyimide.
Claim 16
Dependent Claim
17 words
The method of claim 9 wherein said polymer layer is between about 4,000 and 5,600 Angstroms thick.
Claim 17
Dependent Claim
49 words
The method of claim 9 wherein said laser beam is provided by a pulsed Nd/YAG laser having a pulse frequency of between about 10 Hz and 10 kHz, a wavelength of between about 200 and 400 nm., and an energy of between about 0.1 and 1 Joule/cm 2 .
Claim 18
Dependent Claim
16 words
The method of claim 9 wherein said laser beam is provided by a pulsed excimer laser.
Claim 19
Dependent Claim
20 words
The method of claim 9 wherein said laser beam has a spot size of 100 mm 2 . or thereabout.
Claim 20
Dependent Claim
11 words
The method of claim 9 wherein said cooling gas is nitrogen.
Claim 21
Dependent Claim
12 words
The method of claim 9 wherein said planarizing is chemical mechanical planarization.
Claim 22
Dependent Claim
21 words
The method of claim 9 wherein said third insulative layer is between about 6,000 and 9,500 Angstroms thick after said planarizing.
References Cited (Backward Citations)
US4983419A
Cited
US5124238A
Cited
US4983546A
Cited
US5457073A
Cited
US5669979A
Cited
US5604380A
Cited
US5548159A
Cited
US5958268A
Cited
US6013145A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-09-19 | 2004-03-20 | 2004-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-09-19 | 2008-03-20 | 2008-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-09-19 | 2012-03-20 | 2012-09-19 | $7700.00 | Window Closed / Lapsed |