Shallow trench isolation formation with simplified reverse planarization mask
Assignee: Advanced Micro Devices Inc
•
Filing: 1997-12-18
•
Granted: 2000-07-18
•
Expires: 2017-12-18
Abstract
Abstract An insulated trench isolation structure with large and small trenches of differing widths is formed in a semiconductor substrate using a simplified reverse source/drain planarization mask. Embodiments include forming trenches and refilling them with an insulating material which also covers the substrate surface, polishing to remove an upper portion of the insulating material and to planarize the insulating material above the small trenches, depositing a second, thin layer of insulating material filling seams in the insulating material above the small trenches, masking the insulating material above the large trenches, isotropically etching, and polishing to planarize the insulating material. Since the insulating material is partially planarized and the seams over the small trenches are filled, etching can be carried out after the formation of a relatively simple planarization mask over only the large trenches, and not the small trenches. The use of a planarization mask having relatively few features with relatively large geometry avoids the necessity of creating and implementing a complex, critical mask, thereby reducing manufacturing costs and increasing production throughput.
Inventors
- 👤 Olov Karlsson
- 👤 Christopher F. Lyons
- 👤 Basab Bandyophadhyay
- 👤 Nick Kepler
- 👤 Larry Wang
- 👤 Effiong Ibok
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 08:08
CPC Classifications
H; H10; H10P; H10P95/00; H10P95/06; H10P95/062; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/014; H10W10/0143; H10W10/10; H10W10/17; H10P95/064
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
232 words
A method of manufacturing a semiconductor device having a plurality of trenches formed in a semiconductor substrate or in an epitaxial layer on the semiconductor substrate, which method comprises, sequentially: forming a pad oxide layer on a main surface of the substrate or epitaxial layer; forming a polish stop layer having an upper surface on the pad oxide layer; forming a large trench and a small trench, the large trench having a width at the main surface greater than a width at the main surface of the substrate of the small trench; depositing a first layer of an insulating material to fill the trenches and cover the polish stop layer, whereby the first insulating layer has a seam above the small trench; performing a first polish to substantially planarize a portion of the first layer of the insulating material above the small trench; depositing a second layer of the insulating material filling the seam; masking the large trench with a planarization mask having an opening above the small trench; etching to remove a portion of each of the first and second layers of the insulating material above the small trench; removing the planarization mask; and performing a second polish to planarize such that the upper surface of the first layer of the insulating material in the large and small trenches is substantially flush with the upper surface of the polish stop layer.
Claim 2
Independent Claim
232 words
A method of manufacturing a semiconductor device having a plurality of trenches formed in a semiconductor substrate or in an epitaxial layer on the semiconductor substrate, which method comprises, sequentially: forming a pad oxide layer on a main surface of the substrate or epitaxial layer; forming a polish stop layer having an upper surface on the pad oxide layer; forming a large trench and a small trench, the large trench having a width at the main surface greater than a width at the main surface of the substrate of the small trench; depositing a first layer of an insulating material to fill the trenches and cover the polish stop layer, whereby the first insulating layer has a seam above the small trench; performing a first polish to substantially planarize a portion of the first layer of the insulating material above the small trench; depositing a second layer of the insulating material filling the seam; masking the large trench with a planarization mask having an opening above the small trench; etching to remove a portion of each of the first and second layers of the insulating material above the small trench; removing the planarization mask; and performing a second polish to planarize such that the upper surface of the first layer of the insulating material in the large and small trenches is substantially flush with the upper surface of the polish stop layer.
Claim 3
Dependent Claim
54 words
The method according to claim 1, comprising: providing a source/drain mask on the polish stop layer, the source/drain mask containing a pattern having a plurality of openings; etching to remove portions of the underlying polish stop and pad oxide layers and to form the trenches; and thermally growing an oxide layer lining each trench.
Claim 4
Dependent Claim
22 words
The method according to claim 2, wherein the pad oxide layer comprises silicon oxide and the polish stop layer comprises silicon nitride.
Claim 5
Dependent Claim
19 words
The method according to claim 2, wherein the source/drain mask and the planarization mask each comprises a photoresist mask.
Claim 6
Dependent Claim
32 words
The method according to claim 3, wherein each opening in the source/drain mask has a width substantially equal to the width of one of the plurality of trenches at the main surface.
Claim 7
Dependent Claim
23 words
The method according to claim 5, wherein the plurality of trenches are each etched to a depth of up to about 4000 Å.
Claim 8
Dependent Claim
25 words
The method according to claim 6, wherein the plurality of trenches are each etched to a depth of about 2500 Å to about 3000 Å.
Claim 9
Dependent Claim
24 words
The method according to claim 3, comprising heating at a temperature of at least about 1000° C. to thermally grow a silicon oxide liner.
Claim 10
Dependent Claim
38 words
The method according to claim 3, wherein the insulating material comprises silicon dioxide derived from tetraethyl orthosilicate (TEOS) by low pressure chemical vapor deposition (LPCVD), silicon dioxide derived from silane by LPCVD, or a high density plasma oxide.
Claim 11
Dependent Claim
20 words
The method according to claim 9, comprising polishing the first and second layers of the insulating material by chemical-mechanical polishing.
Claim 12
Dependent Claim
18 words
The method according to claim 9, comprising isotropically etching the first and second layers of the insulating material.
Claim 13
Dependent Claim
18 words
The method according to claim 1, wherein the first insulating layer has a step above the large trench.
Claim 14
Dependent Claim
13 words
The method according to claim 12, comprising masking the step prior to etching.
Claim 15
Independent Claim
373 words
A method of manufacturing an integrated circuit, comprising sequentially: forming a silicon oxide pad layer on a main surface of the substrate or an epitaxial layer formed on the substrate; forming a silicon nitride polish stop layer having an upper surface on the silicon oxide pad layer; providing a photoresist source/drain mask on the silicon nitride polish stop layer, the source/drain mask containing a pattern having a plurality of openings; etching to remove portions of the underlying nitride polish stop and pad oxide layers and to form a large trench and a small trench, the large trench having a width at the main surface greater than a width at the main surface of the small trench; thermally growing a thin silicon oxide layer lining each trench; depositing a first layer of an insulating material to fill the trenches and cover the silicon nitride polish stop layer, the first layer of the insulating material comprising silicon dioxide derived from tetraethyl orthosilicate (TEOS) by low pressure chemical vapor deposition (LPCVD), silicon dioxide derived from silane by LPCVD, or a high density plasma oxide, whereby the first layer of the insulating material has a seam above the small trench; performing a first polish by chemical-mechanical polishing (CMP) to substantially planarize a portion of the first layer of the insulating material above the small trench; depositing a second layer of the insulating material to fill the seam and to cover the upper surface of the first layer of the insulating material, the second layer of the insulating material comprising silicon dioxide derived from tetraethyl orthosilicate (TEOS) by low pressure chemical vapor deposition (LPCVD), silicon dioxide derived from silane by LPCVD, or a high density plasma oxide; masking the large trench with a photoresist planarization mask having an opening above the small trench; isotropically etching to remove a portion of each of the first and second layers of the insulating material above the silicon nitride polish stop layer and the small trench; removing the planarization mask; and performing a second polish by CMP to planarize such that the upper surface of the first layer of the insulating material in the large and small trenches is substantially flush with the upper surface of the silicon nitride polish stop layer.
Claim 16
Independent Claim
373 words
A method of manufacturing an integrated circuit, comprising sequentially: forming a silicon oxide pad layer on a main surface of the substrate or an epitaxial layer formed on the substrate; forming a silicon nitride polish stop layer having an upper surface on the silicon oxide pad layer; providing a photoresist source/drain mask on the silicon nitride polish stop layer, the source/drain mask containing a pattern having a plurality of openings; etching to remove portions of the underlying nitride polish stop and pad oxide layers and to form a large trench and a small trench, the large trench having a width at the main surface greater than a width at the main surface of the small trench; thermally growing a thin silicon oxide layer lining each trench; depositing a first layer of an insulating material to fill the trenches and cover the silicon nitride polish stop layer, the first layer of the insulating material comprising silicon dioxide derived from tetraethyl orthosilicate (TEOS) by low pressure chemical vapor deposition (LPCVD), silicon dioxide derived from silane by LPCVD, or a high density plasma oxide, whereby the first layer of the insulating material has a seam above the small trench; performing a first polish by chemical-mechanical polishing (CMP) to substantially planarize a portion of the first layer of the insulating material above the small trench; depositing a second layer of the insulating material to fill the seam and to cover the upper surface of the first layer of the insulating material, the second layer of the insulating material comprising silicon dioxide derived from tetraethyl orthosilicate (TEOS) by low pressure chemical vapor deposition (LPCVD), silicon dioxide derived from silane by LPCVD, or a high density plasma oxide; masking the large trench with a photoresist planarization mask having an opening above the small trench; isotropically etching to remove a portion of each of the first and second layers of the insulating material above the silicon nitride polish stop layer and the small trench; removing the planarization mask; and performing a second polish by CMP to planarize such that the upper surface of the first layer of the insulating material in the large and small trenches is substantially flush with the upper surface of the silicon nitride polish stop layer.
References Cited (Backward Citations)
US5298110A
Cited
US5362669A
Cited
US5494857A
Cited
US5492858A
Cited
US5459096A
Cited
US5792707A
Cited
US5930645A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-07-18 | 2004-01-17 | 2004-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-07-18 | 2008-01-17 | 2008-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-07-18 | 2012-01-17 | 2012-07-18 | $7700.00 | Window Closed / Lapsed |