Method for forming a capacitor with a multiple pillar structure
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-07-24
•
Granted: 2000-06-06
•
Expires: 2018-07-24
Abstract
Abstract The present invention provides a method for fabricating a multiple pillar shaped capacitor which has pillars of a smaller dimension than the resolution of the photolithography tool. The invention has two embodiments for forming the pillars and third embodiment for patterning a conductive layer into discrete bottom electrodes. The method begins by forming a conductive layer on a first planarization layer. For the first embodiment, the pillars are formed using a photolithography mask with a pattern of spaced transparent areas. The dimensions of the spaced transparent areas and distances between the spaced transparent areas are smaller that the resolution of the lithographic tool. Spaced oxide islands are formed with the mask and are used as an etch mask to form spaced pillars from the conductive layer. The second embodiment for forming the pillars involves using small titanium silicide islands as an etch mask to define the pillars. The third embodiment uses two resist layers and a photo mask shifting (offset) technique to form small spaces between the electrodes. Lastly, a capacitor dielectric layer and a top electrode are formed over the bottom electrodes thereby completing the capacitor with a pillar structure.
Inventors
- 👤 Jan Mye Sung
- 👤 Howard C. Kirsch
- 👤 Chih-Yuan Lu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:14
CPC Classifications
H; H10; H10B; H10B12/00; H10B12/01; H10B12/02; H10B12/03; H10B12/033; H10B12/30; H10B12/31; H10B12/318; H10D; H10D1/00; H10D1/01; H10D1/041; H10D1/043; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/716; H10D1/712; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/947; Y10S438/968
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
208 words
A method of fabricating multiple pillar-shaped capacitors for use in DRAM cells; said capacitors are formed over cell areas in a substrate, the method comprising the steps of: forming a first planarization layer having a contact hole on said substrate; forming a conductive layer on said first planarization layer and in said contact hole; forming sequentially an oxide layer and a first photoresist layer over said conductive layer; exposing said first photoresist layer using a lithographic tool with an optical mask having a pattern of spaced transparent areas forming a partially defined pattern, and etching said partially defined pattern to form a first photoresist pattern of spaced photoresist islands; the dimensions of spaced transparent areas and the distances between said spaced transparent areas are less than the resolution of said lithographic tool; etching said oxide layer using said first photoresist pattern of spaced photoresist islands as a mask to form spaced oxide islands; anisotropically etching said conductive layer using said spaced oxide islands as an etch mask to form spaced pillars; removing said spaced oxide islands; patterning said conductive layer to form bottom electrodes over said cell areas; forming a capacitor dielectric layer over said bottom electrodes; and forming a top electrode layer over said capacitor dielectric layer.
Claim 2
Independent Claim
208 words
A method of fabricating multiple pillar-shaped capacitors for use in DRAM cells; said capacitors are formed over cell areas in a substrate, the method comprising the steps of: forming a first planarization layer having a contact hole on said substrate; forming a conductive layer on said first planarization layer and in said contact hole; forming sequentially an oxide layer and a first photoresist layer over said conductive layer; exposing said first photoresist layer using a lithographic tool with an optical mask having a pattern of spaced transparent areas forming a partially defined pattern, and etching said partially defined pattern to form a first photoresist pattern of spaced photoresist islands; the dimensions of spaced transparent areas and the distances between said spaced transparent areas are less than the resolution of said lithographic tool; etching said oxide layer using said first photoresist pattern of spaced photoresist islands as a mask to form spaced oxide islands; anisotropically etching said conductive layer using said spaced oxide islands as an etch mask to form spaced pillars; removing said spaced oxide islands; patterning said conductive layer to form bottom electrodes over said cell areas; forming a capacitor dielectric layer over said bottom electrodes; and forming a top electrode layer over said capacitor dielectric layer.
Claim 3
Dependent Claim
96 words
The method of claim 1 wherein said conductive layer comprises a first and a second conductive layer; said first conductive layer is composed of doped polysilicon, said first conductive layer having a thickness in the range between 1000 and 3000 Å; said first conductive layer having an impurity concentration in the range between 1E19 and 1E21 atoms/cm 3 ; and said second conductive layer is composed of a material selected from the group consisting of: tungsten silicide and titanium nitride; and said second conductive layer having a thickness in the range between 3000 and 40,000 Å.
Claim 4
Dependent Claim
20 words
The method of claim 1 wherein said oxide layer has a thickness in the range between 1000 and 3000 Å.
Claim 5
Dependent Claim
43 words
The method of claim 1 wherein said pattern of spaced transparent areas in said optical mask have said dimensions in the range between 0.2 and 0.5 μm and said distances between said transparent areas are in the range between 0.7 and 1.2 μm.
Claim 6
Dependent Claim
35 words
The method of claim 1 wherein said spaced pillars have a diameter in the range between 0.2 and 0.5 μm and a spacing between the adjacent pillars in the range between 0.7 and 1.2 μm.
Claim 7
Dependent Claim
45 words
The method of claim 1 wherein said capacitor dielectric layer is composed of a material selected from the group consisting of ONO, silicon nitride, Ta 2 O 5 , and silicon oxide; and has a thickness in the range between about 40 and 60 Å.
Claim 8
Dependent Claim
125 words
The method of claim 1 wherein said patterning of said conductive layer comprises: (a) forming a first resist layer having patterns of blocks over said cell areas and a first space between said blocks; said first space having a first width; (b) forming a second resist layer having said pattern of blocks over said first resist layer and over said first spaces; said pattern of blocks of second resist layer offset a distance in the x and y directions in relation to said pattern of said first resist layer; the distance offset being less than said first width of said first space; (c) etching said pillars and said conducive layer using said first and second resist layers as a mask to define said bottom electrodes.
Claim 9
Dependent Claim
32 words
The method of claim 7 wherein said second resist layer is offset in relation to said first resist layer a distance in the range between 25% to 50% of said first width.
Claim 10
Dependent Claim
41 words
The method of claim 1 wherein said top electrode is formed of doped polysilicon having a thickness in the range between about 2000 and 4000 Å and an impurity concentration in the range between about 1E19 and 1E21 atoms/cm 3 .
Claim 11
Dependent Claim
39 words
The method of claim 1 which further includes forming a top insulation layer over said top electrode; said top insulation layer is formed of a material selected from the group consisting of: silicon nitride, borophosphosilicate glass and tetraethylorthosilicate (TEOS).
Claim 12
Independent Claim
315 words
A method of fabricating multiple pillar-shaped capacitors for use in DRAM cells; said capacitors are formed over cell areas in a substrate, the method comprising the steps of: forming a first planarization layer having a contact hole on said substrate; forming a conductive layer on said first planarization layer and in said contact hole; forming sequentially an oxide layer and a first photoresist layer over said conductive layer; exposing said first photoresist layer using a lithographic tool with an optical mask having a pattern of spaced transparent areas forming a first photoresist pattern of spaced photoresist islands; the dimensions of spaced transparent areas and the distance between said spaced transparent areas are less than the resolution of said lithographic tool; etching said oxide layer using said first photoresist pattern of spaced photoresist islands as a mask to form spaced oxide islands; anisotropically etching said conductive layer using said spaced oxide islands as an etch mask to form spaced pillars; removing said spaced oxide islands; patterning said conductive layer to form bottom electrodes over said cell areas; said patterning of said conductive layer comprises: (a) forming a first resist layer having patterns of blocks over said cell areas and a first space between said blocks; said first space having a first width; (b) forming a second resist layer having said pattern of blocks over said first resist layer and over said first spaces; said pattern of blocks of second resist layer offset a distance in the x and y directions in relation to said pattern of said first resist layer; the distance offset being less than said first width of said first space; (c) etching said pillars and said conducive layer using said first and second resist layers as a mask to define said bottom electrodes; forming a capacitor dielectric layer over said bottom electrodes; and forming a top electrode layer over said capacitor dielectric layer.
Claim 13
Independent Claim
315 words
A method of fabricating multiple pillar-shaped capacitors for use in DRAM cells; said capacitors are formed over cell areas in a substrate, the method comprising the steps of: forming a first planarization layer having a contact hole on said substrate; forming a conductive layer on said first planarization layer and in said contact hole; forming sequentially an oxide layer and a first photoresist layer over said conductive layer; exposing said first photoresist layer using a lithographic tool with an optical mask having a pattern of spaced transparent areas forming a first photoresist pattern of spaced photoresist islands; the dimensions of spaced transparent areas and the distance between said spaced transparent areas are less than the resolution of said lithographic tool; etching said oxide layer using said first photoresist pattern of spaced photoresist islands as a mask to form spaced oxide islands; anisotropically etching said conductive layer using said spaced oxide islands as an etch mask to form spaced pillars; removing said spaced oxide islands; patterning said conductive layer to form bottom electrodes over said cell areas; said patterning of said conductive layer comprises: (a) forming a first resist layer having patterns of blocks over said cell areas and a first space between said blocks; said first space having a first width; (b) forming a second resist layer having said pattern of blocks over said first resist layer and over said first spaces; said pattern of blocks of second resist layer offset a distance in the x and y directions in relation to said pattern of said first resist layer; the distance offset being less than said first width of said first space; (c) etching said pillars and said conducive layer using said first and second resist layers as a mask to define said bottom electrodes; forming a capacitor dielectric layer over said bottom electrodes; and forming a top electrode layer over said capacitor dielectric layer.
Claim 14
Dependent Claim
96 words
The method of claim 11 wherein said conductive layer comprises a first and a second conductive layer; said first conductive layer is composed of doped polysilicon, said first conductive layer having a thickness in the range between 1000 and 3000 Å, said first conductive layer having an impurity concentration in the range between 1E19 and 1E21 atoms/cm 3 ; and said second conductive layer is composed of a material selected from the group consisting of: tungsten silicide and titanium nitride; and said second conductive layer having a thickness in the range between 3000 and 40,000 Å.
Claim 15
Dependent Claim
20 words
The method of claim 11 wherein said oxide layer has a thickness in the range between 1000 and 3000 Å.
Claim 16
Dependent Claim
43 words
The method of claim 11 wherein said pattern of spaced transparent areas in said optical mask have said dimensions in the range between 0.2 and 0.5 μm and said distances between said transparent areas are in the range between 0.7 and 1.2 μm.
Claim 17
Dependent Claim
35 words
The method of claim 11 wherein said spaced pillars have a diameter in the range between 0.2 and 0.5 μm and a spacing between the adjacent pillars in the range between 0.7 and 1.2 μm.
Claim 18
Dependent Claim
45 words
The method of claim 11 wherein said capacitor dielectric layer is composed of a material selected from the group consisting of: ONO, silicon nitride, Ta 2 O 5 , and silicon oxide; and has a thickness in the range between about 40 and 60 Å.
Claim 19
Dependent Claim
32 words
The method of claim 11 wherein said second resist layer is offset in relation to said first resist layer a distance in the range between 25% to 50% of said first width.
Claim 20
Dependent Claim
41 words
The method of claim 11 wherein said top electrode is formed of doped polysilicon having a thickness in the range between about 2000 and 4000 Å and an impurity concentration in the range between about 1E19 and 1E21 atoms/cm 3 .
References Cited (Backward Citations)
US5213992A
Cited
US5336630A
Cited
US5302540A
Cited
US5427974A
Cited
US5466627A
Cited
US5492848A
Cited
US5459095A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-06-06 | 2003-12-06 | 2004-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-06-06 | 2007-12-06 | 2008-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-06-06 | 2011-12-06 | 2012-06-06 | $7700.00 | Window Closed / Lapsed |