Rippled polysilicon surface capacitor electrode plate for high density DRAM
Assignee: Industrial Technology Research Institute
•
Filing: 1991-10-02
•
Granted: 1993-05-25
•
Expires: 2011-10-02
Abstract
Abstract A new method to produce a microminiturized capacitor having a regular microscopic ripple surface electrode is achieved by depositing a first polysilicon layer over a suitable insulating base. A resist layer is formed over the first polysilicon layer. The resist layer is exposed through a mask having a pattern of regular spaced openings in the areas of the planned capacitor to radiant energy in sufficient quantity to under expose, out of focus expose or a combination of under expose and out of focus expose the resist layer. The mask is shifted a fixed and short distance. The resist layer is exposed through the shifted mask to radiant energy in sufficient quantity to under expose or out of focus expose, or a combination of under expose or out of focus expose the resist layer again and in a different location. The shifting of the mask and exposing resist steps are repeated until a pattern of the regular microscopic ripple has been formed in the resist layer. The resist layer is developed to leave the pattern of regular microscopic ripple in the surface of the resist layer. The resist layer and said first polysilicon layer is uniformly and anisotropically etched to create the pattern of regular microscopic ripple in the surface of the first polysilicon layer. The remaining resist layer is removed. An insulating layer is deposited over the ripple surface. The capacitor structure is completed by depositing a second polysilicon layer over the insulating layer.
Inventors
- 👤 Chih-Yuan Lu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:47
CPC Classifications
H; H10; H10D; H10D1/00; H10D1/60; H10D1/68; H10D1/692; H10D1/711; H10D1/712; H10P; H10P50/00; H10P50/71; H10D1/01; H10D1/041; H10D1/043; H10D1/716; Y; Y10; Y10S; Y10S148/00; Y10S148/104; Y10S438/00; Y10S438/942; Y10S438/948; Y10S438/964
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
321 words
A method for producing a regular microscopic ripple surface capacitor fabricated on a monocrystalline semiconductor substrate comprising: depositing a first polycrystalline silicon layer to form a first capacitor plate on a partially completed device structure over a base insulating layer and a contact opening exposing said substrate; forming a resist layer over said first polycrystalline silicon layer; exposing said resist layer through a mask having a pattern of regular spaced openings in the areas of the planned said capacitor to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; shifting said mask a fixed distance; exposing said resist layer through the said shifted mask to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; repeating said shifting said mask and exposing said resist steps until a pattern of said regular microscopic ripple has been formed in said resist layer; developing said resist layer to leave said pattern of regular microscopic ripple in the surface of the resist layer; uniformly and anisotropically etching the said resist layer and said first polycrystalline silicon layer to create said pattern of regular microscopic ripple in the surface of said first polycrystalline layer; removing the remaining said resist layer; depositing an insulating layer to form a capacitor dielectric layer over the surface of the said first polycrystalline layer; and depositing a second polycrystalline silicon layer over said insulating layer to form the second capacitor plate and complete said regular microscopic surface capacitor.
Claim 2
Independent Claim
321 words
A method for producing a regular microscopic ripple surface capacitor fabricated on a monocrystalline semiconductor substrate comprising: depositing a first polycrystalline silicon layer to form a first capacitor plate on a partially completed device structure over a base insulating layer and a contact opening exposing said substrate; forming a resist layer over said first polycrystalline silicon layer; exposing said resist layer through a mask having a pattern of regular spaced openings in the areas of the planned said capacitor to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; shifting said mask a fixed distance; exposing said resist layer through the said shifted mask to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; repeating said shifting said mask and exposing said resist steps until a pattern of said regular microscopic ripple has been formed in said resist layer; developing said resist layer to leave said pattern of regular microscopic ripple in the surface of the resist layer; uniformly and anisotropically etching the said resist layer and said first polycrystalline silicon layer to create said pattern of regular microscopic ripple in the surface of said first polycrystalline layer; removing the remaining said resist layer; depositing an insulating layer to form a capacitor dielectric layer over the surface of the said first polycrystalline layer; and depositing a second polycrystalline silicon layer over said insulating layer to form the second capacitor plate and complete said regular microscopic surface capacitor.
Claim 3
Dependent Claim
51 words
The method of claim 1 wherein said pattern of regular openings is uniform in both the X and Y directions and the opening size is less than about 2.5 micrometers and the spacing between said openings is uniformly less than about 2.5 micrometers and a 5× reduction projection stepper is used.
Claim 4
Dependent Claim
36 words
The method of claim 1 wherein phase-shifting technique is used to improve the resolution of the mask and said shifting said mask is less than about 3 repetitions to produce the desired said regular microscopic ripple.
Claim 5
Dependent Claim
36 words
The method of claim 2 wherein said shifting said mask distance is between about 0.5 to 0.1 micrometers and said shifting said mask is less than about 10 repetitions to produce desired said regular microscopic ripple.
Claim 6
Dependent Claim
50 words
The method of claim 1 wherein the thickness of said resist layer is between about 2000 to 5000 Angstroms and said etching of said resist layer and first polycrystalline silicon layer is accomplished by exposure to an ambient of CF 4 +Cl 2 +O 2 in a ratio of 25:25:2.
Claim 7
Dependent Claim
39 words
The method of claim 1 wherein said pattern of regular microscopic ripple has a ripple width of less than about 0.1 micrometers and a spacing between ripples of less than about 0.1 micrometers in said first polycrystalline silicon layer.
Claim 8
Dependent Claim
16 words
The method of claim 6 wherein said ripple depth is between about 0.05 to 0.2 micrometers.
Claim 9
Dependent Claim
40 words
The method of claim 1 wherein said contact opening exposing said substrate allows the electrical contact of said first polycrystalline silicon layer to a source/drain region in said substrate and the partially completed structure is a dynamic random access memory.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein the thickness of said capacitor dielectric layer is between about 30 to 250 Angstroms.
Claim 11
Dependent Claim
22 words
The method of claim 9 wherein said capacitor dielectric layer is a composite layer of silicon oxide, silicon nitride and silicon oxide.
Claim 12
Dependent Claim
15 words
The method of claim 9 wherein said capacitor dielectric layer at least includes tantalum oxide.
Claim 13
Dependent Claim
21 words
The method of claim 9 wherein the thickness of said second polycrystalline silicon layer is between about 500 to 5000 Angstroms.
Claim 14
Dependent Claim
32 words
The method of claim 1 wherein said ripple surface capacitor is made in combination with a field effect transistor and is adapted for use in a high density dynamic random access memory.
Claim 15
Dependent Claim
27 words
The method of claim 1 wherein following said removal of said resist layer, the said first polycrystalline silicon layer is patterned as an electrode of said capacitor.
Claim 16
Independent Claim
361 words
A method for producing a regular microscopic ripple surface capacitor fabricated on a monocrystalline semiconductor substrate comprising: depositing a first polycrystalline silicon layer to form a first capacitor plate on a partially completed device structure over a base insulating layer and a contact opening exposing said substrate; forming a layer that can be a selective etching mask for polycrystalline silicon over said first polycrystalline silicon layer; forming a resist layer over said layer over said fist layer; exposing said resist layer through a mask having a pattern of regular spaced openings in the areas of the planned said capacitor to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; shifting said mask a fixed distance; exposing said resist layer through the said shifted mask to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; repeating said shifting said mask and exposing said resist steps until a pattern of said regular microscopic ripple has been formed in said resist layer; developing said resist layer to leave said pattern of regular microscopic ripple in the surface of the resist layer; uniformly and anisotropically etching the said resist layer and said layer over said first layer to create said pattern of regular microscopic ripple mask; removing the remaining said resist layer; uniformly and anisotropically etching the said regular microscopic ripple into the surface of said first polycrystalline layer; removing the remaining said layer over said first layer; depositing an insulating layer to form a capacitor dielectric layer over the surface of the said first polycrystalline layer; and depositing a second polycrystalline silicon layer over said insulating layer to form the second capacitor plate and complete said regular microscopic surface capacitor.
Claim 17
Independent Claim
361 words
A method for producing a regular microscopic ripple surface capacitor fabricated on a monocrystalline semiconductor substrate comprising: depositing a first polycrystalline silicon layer to form a first capacitor plate on a partially completed device structure over a base insulating layer and a contact opening exposing said substrate; forming a layer that can be a selective etching mask for polycrystalline silicon over said first polycrystalline silicon layer; forming a resist layer over said layer over said fist layer; exposing said resist layer through a mask having a pattern of regular spaced openings in the areas of the planned said capacitor to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; shifting said mask a fixed distance; exposing said resist layer through the said shifted mask to radiant energy in sufficient quantity through a lens system to under-expose, de-focus an image on said resist layer or a combination of under-expose and de-focus an image on said resist layer to create in said resist layer a ripple image wherein said image does not reach said first polycrystalline silicon layer; repeating said shifting said mask and exposing said resist steps until a pattern of said regular microscopic ripple has been formed in said resist layer; developing said resist layer to leave said pattern of regular microscopic ripple in the surface of the resist layer; uniformly and anisotropically etching the said resist layer and said layer over said first layer to create said pattern of regular microscopic ripple mask; removing the remaining said resist layer; uniformly and anisotropically etching the said regular microscopic ripple into the surface of said first polycrystalline layer; removing the remaining said layer over said first layer; depositing an insulating layer to form a capacitor dielectric layer over the surface of the said first polycrystalline layer; and depositing a second polycrystalline silicon layer over said insulating layer to form the second capacitor plate and complete said regular microscopic surface capacitor.
Claim 18
Dependent Claim
44 words
The method of claim 15 wherein the said layer over said first layer is silicon oxide, the thickness of said resist layer is between about 500 to 1000 Angstroms and the thickness of said silicon oxide layer is between about 200 to 1000 Angstroms.
Claim 19
Dependent Claim
55 words
The method of claim 15 wherein said pattern of regular openings is uniform in both the X and Y directions and the opening size is less than about 2.5 micrometers and the spacing between said openings is uniformly less than about 2.5 micrometers and a 5× reduction projection stepper is used in the exposing steps.
Claim 20
Dependent Claim
36 words
The method of claim 17 wherein phase-shifting technique is used to improve the resolution of the mask and said shifting said mask is less than about 3 repetitions to produce the desired said regular microscopic ripple.
Claim 21
Dependent Claim
37 words
The method of claim 17 wherein said shifting said mask distance is between about 0.5 to 0.1 micrometers and said shifting said mask is less than about 10 repetitions to produce the desired said regular microscopic ripple.
Claim 22
Dependent Claim
39 words
The method of claim 15 wherein said pattern of regular microscopic ripple has a ripple width of less than about 0.1 micrometers and a spacing between ripples of less than about 0.1 micrometers in said first polycrystalline silicon layer.
Claim 23
Dependent Claim
16 words
The method of claim 20 wherein said ripple depth is between about 0.05 to 0.2 micrometers.
Claim 24
Dependent Claim
40 words
The method of claim 15 wherein said contact opening exposing said substrate allows the electrical contact of said first polycrystalline silicon layer to a source/drain region in said substrate and the partially completed structure is a dynamic random access memory.
Claim 25
Dependent Claim
20 words
The method of claim 15 wherein the thickness of said capacitor dielectric layer is between about 30 to 250 Angstroms.
Claim 26
Dependent Claim
22 words
The method of claim 23 wherein said capacitor dielectric layer is a composite layer of silicon oxide, silicon nitride and silicon oxide.
Claim 27
Dependent Claim
15 words
The method of claim 23 wherein said capacitor dielectric layer at least includes tantalum oxide.
References Cited (Backward Citations)
US5149676A
Cited
US5112773A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1996-05-24 | 1996-11-23 | 1997-05-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2000-05-24 | 2000-11-23 | 2001-05-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2004-05-24 | 2004-11-23 | 2005-05-25 | $7700.00 | Window Closed / Lapsed |