Well-drive anneal technique using preplacement of nitride films for enhanced field isolation
Assignee: Micron Technology Inc
•
Filing: 1997-11-18
•
Granted: 2000-05-30
•
Expires: 2017-11-18
Abstract
Abstract A method of forming an isolation structure comprising forming n-type areas and/or p-type areas implanted respectively therein on a first surface of the substrate. A pad oxide film is grown on the substrate first surface covering the p-wells and/or n-wells. A diffusion barrier(s) is deposited on the substrate first surface and a substrate second surface to form an encapsulated structure. The encapsulated structure is annealed to activate the n-type and/or p-type areas. A mask material is applied over the diffusion barrier on the substrate first surface to define active device areas and a dry etch process is used to etch away the unmasked portions of the diffusion barrier. The mask material is stripped and a field oxide is grown on the substrate first surface. A portion of the field oxide and all of the diffusion barrier is removed, resulting in active areas surrounded by a field isolation structure.
Inventors
- 👤 Pai-Hung Pan
- 👤 Nanseng Jeng
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:49
CPC Classifications
H; H10; H10D; H10D84/00; H10D84/01; H10D84/0123; H10D84/0126; H10D84/0165; H10D84/0188; H10D84/02; H10D84/03; H10D84/038; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0125; H10W10/0126; H10W10/0127; H10W10/031; H10W10/10; H10W10/13; H10W10/30
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
136 words
A method of forming elements of isolated electrical devices on a semiconductor substrate comprising: providing a semiconductor substrate having a first surface, a second surface, at least one p-well, and at least one n-well; forming a zero oxide layer over said first surface; creating at least one p-type area within said at least one n-well and at least one n-type area within said at least one p-well after formation of said zero oxide layer; substantially removing said zero oxide layer from said first surface; forming a pad oxide layer over said first surface after substantially removing said zero oxide layer; depositing a diffusion barrier layer over said pad oxide layer; and annealing said substrate to create at least one activated p-type area and at least one activated n-type area after deposition of the diffusion barrier layer.
Claim 2
Independent Claim
136 words
A method of forming elements of isolated electrical devices on a semiconductor substrate comprising: providing a semiconductor substrate having a first surface, a second surface, at least one p-well, and at least one n-well; forming a zero oxide layer over said first surface; creating at least one p-type area within said at least one n-well and at least one n-type area within said at least one p-well after formation of said zero oxide layer; substantially removing said zero oxide layer from said first surface; forming a pad oxide layer over said first surface after substantially removing said zero oxide layer; depositing a diffusion barrier layer over said pad oxide layer; and annealing said substrate to create at least one activated p-type area and at least one activated n-type area after deposition of the diffusion barrier layer.
Claim 3
Dependent Claim
27 words
The method of claim 1, wherein depositing said diffusion barrier layer over said pad oxide layer includes depositing said diffusion barrier layer over said substrate second surface.
Claim 4
Dependent Claim
18 words
The method of claim 1, further comprising depositing a second diffusion barrier layer over said substrate second surface.
Claim 5
Dependent Claim
32 words
The method of claim 1, wherein said step of depositing a diffusion barrier layer over said pad oxide layer comprises depositing a silicon nitride diffusion barrier layer over said pad oxide layer.
Claim 6
Dependent Claim
32 words
The method of claim 1, wherein said step of depositing a diffusion barrier layer over said pad oxide layer comprises depositing a silicon oxynitride diffusion barrier layer over said pad oxide layer.
Claim 7
Dependent Claim
99 words
The method of claim 1, further comprising: applying a mask material over said diffusion barrier layer after annealing said substrate to create said at least one activated p-type area and said at least one activated n-type area; etching said diffusion barrier layer to define at least one active device area comprised of said at least one activated n-type area or said at least one activated p-type area; stripping said mask material; growing a field oxide on said substrate; and removing said diffusion barrier layer and a portion of said field oxide to expose portions of said substrate first surface.
Claim 8
Independent Claim
95 words
A method of forming elements of a MOS structure, comprising: providing a semiconductor substrate having a first surface, a second surface, at least one p-well, and at least one n-well; forming an oxide layer over said first surface; creating at least one doped area within said at least one p-well or within said at least one n-well; depositing a diffusion barrier layer over said oxide layer after said creation of said at least one doped area; and annealing said substrate to create at least one activated doped area after deposition of said diffusion barrier layer.
Claim 9
Independent Claim
95 words
A method of forming elements of a MOS structure, comprising: providing a semiconductor substrate having a first surface, a second surface, at least one p-well, and at least one n-well; forming an oxide layer over said first surface; creating at least one doped area within said at least one p-well or within said at least one n-well; depositing a diffusion barrier layer over said oxide layer after said creation of said at least one doped area; and annealing said substrate to create at least one activated doped area after deposition of said diffusion barrier layer.
Claim 10
Dependent Claim
26 words
The method of claim 7, wherein depositing said diffusion barrier layer over said oxide layer includes depositing said diffusion barrier layer over said substrate second surface.
Claim 11
Dependent Claim
18 words
The method of claim 7, further comprising depositing a second diffusion barrier layer over said substrate second surface.
Claim 12
Dependent Claim
45 words
The method of claim 7, wherein said step of creating at least one doped area within said at least one p-well or within said at least one n-well comprises creating at least one area doped with a p-type impurity within said at least one n-well.
Claim 13
Dependent Claim
45 words
The method of claim 7, wherein said step of creating at least one doped area within said at least one p-well or within said at least one n-well comprises creating at least one area doped with an n-type impurity within said at least one p-well.
Claim 14
Dependent Claim
30 words
The method of claim 7, wherein said step of depositing a diffusion barrier layer over said oxide layer comprises depositing a silicon nitride diffusion barrier layer over said oxide layer.
Claim 15
Dependent Claim
30 words
The method of claim 7, wherein said step of depositing a diffusion barrier layer over said oxide layer comprises depositing a silicon oxynitride diffusion barrier layer over said oxide layer.
Claim 16
Dependent Claim
83 words
The method of claim 9, further comprising: applying a mask material over said diffusion barrier layer after annealing said substrate to create said at least one activated doped area; etching said diffusion barrier layer to define at least one active device area comprised of said at least one activated doped area; stripping said mask material; growing a field oxide on said substrate; and removing said diffusion barrier layer and a portion of said field oxide to expose portions of said substrate first surface.
Claim 17
Dependent Claim
81 words
A well-drive anneal method using preplacement of nitride films for enhanced field isolation comprising: providing a semiconductor substrate having a first surface and a second surface; forming an oxide layer over said first surface; creating at least one doped area on said first surface; depositing a diffusion barrier layer over said oxide layer after creation of said at least one doped area; and annealing said substrate to create at least one activated doped area after deposition of said diffusion barrier layer.
Claim 18
Dependent Claim
81 words
A well-drive anneal method using preplacement of nitride films for enhanced field isolation comprising: providing a semiconductor substrate having a first surface and a second surface; forming an oxide layer over said first surface; creating at least one doped area on said first surface; depositing a diffusion barrier layer over said oxide layer after creation of said at least one doped area; and annealing said substrate to create at least one activated doped area after deposition of said diffusion barrier layer.
Claim 19
Dependent Claim
26 words
The method of claim 15, wherein depositing said diffusion barrier layer over said oxide layer includes depositing said diffusion barrier layer over said substrate second surface.
Claim 20
Dependent Claim
18 words
The method of claim 15, further comprising depositing a second diffusion barrier layer over said substrate second surface.
Claim 21
Dependent Claim
33 words
The method of claim 15, wherein said step of creating at least one doped area on said first surface comprises doping at least one area on said first surface with a p-type impurity.
Claim 22
Dependent Claim
33 words
The method of claim 15, wherein said step of creating at least one doped area on said first surface comprises doping at least one area on said first surface with an n-type impurity.
Claim 23
Dependent Claim
35 words
The method of claim 15, wherein said step of depositing a diffusion barrier layer over said oxide layer after creation of said at least one doped area comprises depositing a silicon nitride diffusion barrier layer.
Claim 24
Dependent Claim
35 words
The method of claim 15, wherein said step of depositing a diffusion barrier layer over said oxide layer after creation of said at least one doped area comprises depositing a silicon oxynitride diffusion barrier layer.
Claim 25
Dependent Claim
83 words
The method of claim 17, further comprising: applying a mask material over said diffusion barrier layer after annealing said substrate to create said at least one activated doped area; etching said diffusion barrier layer to define at least one active device area comprised of said at least one activated doped area; stripping said mask material; growing a field oxide on said substrate; and removing said diffusion barrier layer and a portion of said field oxide to expose portions of said substrate first surface.
References Cited (Backward Citations)
US5043778A
Cited
US5296400A
Cited
US5497021A
Cited
US5677208A
Cited
US5516710A
Cited
US5627099A
Cited
US5837378A
Cited
US5846596A
Cited
US5688710A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2003-05-30 | 2003-11-29 | 2004-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2007-05-30 | 2007-11-29 | 2008-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2011-05-30 | 2011-11-29 | 2012-05-30 | $7700.00 | Window Closed / Lapsed |