Method for forming a high density shallow trench contactless nonvolatile memory
Assignee: Taiwan Semiconductor Manufacturing Co TSMC Ltd
•
Filing: 1998-03-25
•
Granted: 1999-12-28
•
Expires: 2018-03-25
Abstract
Abstract The present invention proposes a method for fabricating a high-density shallow trench contactless nonvolatile memory. First, a stacked pad oxide/silicon nitride layer is deposited on the substrate and the buried bit line region is defined by a photoresist. An anisotropic etching follows to etch the silicon layer and then the n+ impurity ions are implanted to form the source and drain. After stripping the photoresist, a high temperature steam oxidation process is used to grow a thick field oxide, and the doped ions are active and driven in to form the buried bit lines simultaneously. The silicon nitride layer and the pad oxide layer are then removed, and the silicon substrate is recessed by using the field oxide as an etching mask. After rounding the trench corners by using thermal oxidation and etching back processes, a thin silicon oxy-nitride film is regrown. An in-situ doped polysilicon film is deposited to refill the trench region and then etch back by using a CMP process to form the floating gates. Next, the interpoly dielectric such as ultra-thin ONO film, and, the control gate formed of n+ doped polysilicon film, are sequentially built. After the word lines are defined, the nonvolatile memory is thus finished.
Inventors
- 👤 Shye-Lin Wu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 22:32
CPC Classifications
H; H10; H10B; H10B41/00; H10B41/30
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
259 words
A method for forming nonvolatile memories with trench gates, said method comprises: forming a pad oxide layer on a semiconductor substrate; forming a silicon nitride layer on said pad oxide layer; patterning a photoresist on said silicon nitride layer to define the buried bit line region; etching said silicon nitride layer to expose a portion of said pad oxide which defines said buried bit line region of said semiconductor substrate, said etching uses said patterned photoresist as an etching mask; implanting ions into said semiconductor substrate to form source and drain using said patterned photoresist as an implantation mask; removing said patterned photoresist; performing a thermal oxidation to oxidize a potion of said semiconductor substrate exposed by said silicon nitride layer, thereby generating field oxides on said semiconductor substrate and simultaneously driving said ions into said semiconductor substrate; removing said silicon nitride layer; removing said pad oxide layer; recessing said semiconductor substrate to form trenches in said semiconductor substrate using said field oxides as a mask; forming a silicon oxy-nitride layer on said semiconductor substrate; forming a first polysilicon layer on said semiconductor substrate and refilling into said trenches; removing a portion of said first polysilicon layer which exceeds said trenches, whereby the residual portion of said first polysilicon layer forms the recessed floating gates isolated by said field oxide and said silicon oxy-nitride layer; forming a dielectric layer on said semiconductor substrate; forming a second polysilicon layer on said dielectric layer to serve as a control gate; and patterning said second polysilicon layer to form the word lines.
Claim 2
Independent Claim
259 words
A method for forming nonvolatile memories with trench gates, said method comprises: forming a pad oxide layer on a semiconductor substrate; forming a silicon nitride layer on said pad oxide layer; patterning a photoresist on said silicon nitride layer to define the buried bit line region; etching said silicon nitride layer to expose a portion of said pad oxide which defines said buried bit line region of said semiconductor substrate, said etching uses said patterned photoresist as an etching mask; implanting ions into said semiconductor substrate to form source and drain using said patterned photoresist as an implantation mask; removing said patterned photoresist; performing a thermal oxidation to oxidize a potion of said semiconductor substrate exposed by said silicon nitride layer, thereby generating field oxides on said semiconductor substrate and simultaneously driving said ions into said semiconductor substrate; removing said silicon nitride layer; removing said pad oxide layer; recessing said semiconductor substrate to form trenches in said semiconductor substrate using said field oxides as a mask; forming a silicon oxy-nitride layer on said semiconductor substrate; forming a first polysilicon layer on said semiconductor substrate and refilling into said trenches; removing a portion of said first polysilicon layer which exceeds said trenches, whereby the residual portion of said first polysilicon layer forms the recessed floating gates isolated by said field oxide and said silicon oxy-nitride layer; forming a dielectric layer on said semiconductor substrate; forming a second polysilicon layer on said dielectric layer to serve as a control gate; and patterning said second polysilicon layer to form the word lines.
Claim 3
Dependent Claim
14 words
The method according to claim 1, wherein said semiconductor substrate is a p-type substrate.
Claim 4
Dependent Claim
18 words
The method according to claim 1, wherein said pad oxide layer has a thickness of about 50-350 angstroms.
Claim 5
Dependent Claim
46 words
The method according to claim 1, wherein said implanted ions are n-type ions selected from the group consisting of phosphorus ions, arsenic ions and antimony ions, and said ions are implanted at about 0.5-150 keV with dosage of about 5×10 14 -5×10 16 atoms/cm 2 .
Claim 6
Dependent Claim
24 words
The method according to claim 1 further comprises a process for rounding the corners of said trenches before said silicon oxy-nitride layer is formed.
Claim 7
Dependent Claim
35 words
The method according to claim 5, wherein said trench corners is rounded by following method: performing a thermal oxidation to grow a silicon oxide film on said semiconductor substrate; and removing said silicon oxide film.
Claim 8
Dependent Claim
18 words
The method according to claim 1, wherein said silicon oxy-nitride layer has a thickness of about 30-250 angstroms.
Claim 9
Dependent Claim
18 words
The method according to claim 1, wherein said first polysilicon layer is formed of in-situ n-type doped polysilicon.
Claim 10
Dependent Claim
32 words
The method according to claim 1, wherein said exceeding portion of said first polysilicon layer is removed by a chemical mechanical polish process using said silicon oxy-nitride layer as a stopping layer.
Claim 11
Dependent Claim
51 words
The method according to claim 1, wherein said dielectric layer is formed of the material selected from the group consisting of tantalum pentoxide (Ta 2 O 5 ), BST, a double film of silicon nitride and silicon oxide, and a triple film of silicon oxide, silicon nitride and silicon oxide (ONO).
Claim 12
Dependent Claim
21 words
The method according to claim 1, wherein said second polysilicon layer is formed of n-type doped or in-situ n-type doped polysilicon.
Claim 13
Independent Claim
265 words
A method for forming nonvolatile memories with trench gates, said method comprises: forming a pad oxide layer on a semiconductor substrate; forming a silicon nitride layer on said pad oxide layer; patterning a photoresist on said silicon nitride layer to define the buried bit line region; etching said silicon nitride layer to expose a portion of said pad oxide which defines said buried bit line region of said semiconductor substrate, said etching uses said patterned photoresist as an etching mask; implanting ions into said semiconductor substrate to form source and drain using said patterned photoresist as an implantation mask; removing said patterned photoresist; performing a thermal oxidation to oxidize a potion of said semiconductor substrate exposed by said silicon nitride layer, thereby generating field oxides on said semiconductor substrate and simultaneously driving said ions into said semiconductor substrate; removing said silicon nitride layer; removing said pad oxide layer; recessing said semiconductor substrate to form trenches in said semiconductor substrate using said field oxides as a mask; rounding the corners of said trenches; forming a silicon oxy-nitride layer on said semiconductor substrate; forming a first polysilicon layer on said semiconductor substrate and refilling into said trenches; removing a portion of said first polysilicon layer which exceeds said trenches, whereby the residual portion of said first polysilicon layer forms the recessed floating gates isolated by said field oxide and said silicon oxy-nitride layer; forming a dielectric layer on said semiconductor substrate; forming a second polysilicon layer on said dielectric layer to serve as a control gate; and patterning said second polysilicon layer to form the word lines.
Claim 14
Independent Claim
265 words
A method for forming nonvolatile memories with trench gates, said method comprises: forming a pad oxide layer on a semiconductor substrate; forming a silicon nitride layer on said pad oxide layer; patterning a photoresist on said silicon nitride layer to define the buried bit line region; etching said silicon nitride layer to expose a portion of said pad oxide which defines said buried bit line region of said semiconductor substrate, said etching uses said patterned photoresist as an etching mask; implanting ions into said semiconductor substrate to form source and drain using said patterned photoresist as an implantation mask; removing said patterned photoresist; performing a thermal oxidation to oxidize a potion of said semiconductor substrate exposed by said silicon nitride layer, thereby generating field oxides on said semiconductor substrate and simultaneously driving said ions into said semiconductor substrate; removing said silicon nitride layer; removing said pad oxide layer; recessing said semiconductor substrate to form trenches in said semiconductor substrate using said field oxides as a mask; rounding the corners of said trenches; forming a silicon oxy-nitride layer on said semiconductor substrate; forming a first polysilicon layer on said semiconductor substrate and refilling into said trenches; removing a portion of said first polysilicon layer which exceeds said trenches, whereby the residual portion of said first polysilicon layer forms the recessed floating gates isolated by said field oxide and said silicon oxy-nitride layer; forming a dielectric layer on said semiconductor substrate; forming a second polysilicon layer on said dielectric layer to serve as a control gate; and patterning said second polysilicon layer to form the word lines.
Claim 15
Dependent Claim
14 words
The method according to claim 12, wherein said semiconductor substrate is a p-type substrate.
Claim 16
Dependent Claim
18 words
The method according to claim 13, wherein said pad oxide layer has a thickness of about 50-350 angstroms.
Claim 17
Dependent Claim
46 words
The method according to claim 12, wherein said implanted ions are n-type ions selected from the group consisting of phosphorus ions, arsenic ions and antimony ions, and said ions are implanted at about 0.5-150 keV with dosage of about 5×10 14 -5×10 16 atoms/cm 2 .
Claim 18
Dependent Claim
35 words
The method according to claim 12, wherein said trench corners is rounded by following method: performing a thermal oxidation to grow a silicon oxide film on said semiconductor substrate; and removing said silicon oxide film.
Claim 19
Dependent Claim
18 words
The method according to claim 12, wherein said silicon oxy-nitride layer has a thickness of about 30-250 angstroms.
Claim 20
Dependent Claim
18 words
The method according to claim 12, wherein said first polysilicon layer is formed of in-situ n-type doped polysilicon.
Claim 21
Dependent Claim
32 words
The method according to claim 12, wherein said exceeding portion of said first polysilicon layer is removed by a chemical mechanical polish process using said silicon oxy-nitride layer as a stopping layer.
Claim 22
Dependent Claim
51 words
The method according to claim 12, wherein said dielectric layer is formed of the material selected from the group consisting of tantalum pentoxide (Ta 2 O 5 ), BST, a double film of silicon nitride and silicon oxide, and a triple film of silicon oxide, silicon nitride and silicon oxide (ONO).
Claim 23
Dependent Claim
21 words
The method according to claim 12, wherein said second polysilicon layer is formed of n-type doped or in-situ n-type doped polysilicon.
References Cited (Backward Citations)
US5423973A
Cited
US5480819A
Cited
US5554568A
Cited
US5744847A
Cited
US5521110A
Cited
US5661055A
Cited
US5680345A
Cited
US5923977A
Cited
US5763310A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-12-27 | 2003-06-28 | 2003-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-12-27 | 2007-06-28 | 2007-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-12-27 | 2011-06-28 | 2011-12-28 | $7700.00 | Window Closed / Lapsed |