Continuous process for forming improved titanium nitride barrier layers
Assignee: Applied Materials Inc
•
Filing: 1995-06-07
•
Granted: 1999-10-26
•
Expires: 2015-06-07
Abstract
Abstract A continuous process for the deposition of robust titanium-containing barrier layers comprises sputtering in a single substrate sputtering chamber a first layer of titanium, sputtering a layer of titanium nitride thereover, treating the titanium nitride layer with a plasma containing oxygen while continuing to sputter the titanium target to deposit a thin layer of TiON, and finally sputtering a layer of titanium over the titanium nitride. The latter step removes impurities from the titanium target, preventing poisoning of the target. Thus subsequent substrates can be continuously processed in said chamber without degrading the barrier properties or poisoning the titanium target.
Inventors
- 👤 Murali K. Narasimhan
- 👤 Kenny King-Tai Ngan
- 👤 Nitin Khurana
- 👤 Bradley O. Stimson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:59
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/032; H10W20/033; C; C23; C23C; C23C14/00; C23C14/06; C23C14/0641; C23C14/0676; C23C14/14; C23C14/16; C23C14/165
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
177 words
A continuous method for forming improved titanium-containing barrier layers in a single substrate sputtering chamber including a target, a DC source connected to the target, a substrate support, an RF power supply connected to the substrate support and a gas inlet comprising the following steps in sequence: a) transferring a substrate into said chamber and sputter depositing in argon atmosphere a first layer of titanium onto said substrate; b) sputter depositing a second layer of titanium nitride in an atmosphere of argon and nitrogen onto said substrate; c) turning on the RF power supply and forming a plasma adjacent to the substrate from a mixture of argon and oxygen while continuing to sputter the titanium target by applying DC power to the target to form an oxygen-treated titanium nitride layer; d) turning off the oxygen and sputter depositing a second layer of titanium over the oxygen-treated nitride layer for at least about three seconds; and e) transferring said substrate out of said chamber; and f) transferring another substrate into said chamber, and repeating steps a) to e).
Claim 2
Dependent Claim
177 words
A continuous method for forming improved titanium-containing barrier layers in a single substrate sputtering chamber including a target, a DC source connected to the target, a substrate support, an RF power supply connected to the substrate support and a gas inlet comprising the following steps in sequence: a) transferring a substrate into said chamber and sputter depositing in argon atmosphere a first layer of titanium onto said substrate; b) sputter depositing a second layer of titanium nitride in an atmosphere of argon and nitrogen onto said substrate; c) turning on the RF power supply and forming a plasma adjacent to the substrate from a mixture of argon and oxygen while continuing to sputter the titanium target by applying DC power to the target to form an oxygen-treated titanium nitride layer; d) turning off the oxygen and sputter depositing a second layer of titanium over the oxygen-treated nitride layer for at least about three seconds; and e) transferring said substrate out of said chamber; and f) transferring another substrate into said chamber, and repeating steps a) to e).
Claim 3
Dependent Claim
24 words
A method according to claim 1 wherein the combined thickness of the first titanium layer and the titanium nitride layer is about 1000 Å.
Claim 4
Dependent Claim
26 words
A method according to claim 1 wherein said titanium nitride layer is treated in the oxygen plasma for about 30 seconds to form a TiON layer.
Claim 5
Dependent Claim
17 words
A method according to claim 3 wherein a layer of TiON about 20-100 Å thick is deposited.
Claim 6
Dependent Claim
16 words
A method according to claim 1 wherein said second titanium layer is about 80-200 Å thick.
Claim 7
Dependent Claim
27 words
A method according to claim 1 wherein after transferring the substrate out of the chamber, a layer of aluminum is deposited thereover in a second vacuum chamber.
References Cited (Backward Citations)
US5232871A
Cited
EP0545602A1
Cited
US5439574A
Cited
US5240880A
Cited
EP0598422A1
Cited
US5378660A
Cited
EP0680077A1
Cited
JPH08130302A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 2002-10-25 | 2003-04-26 | 2003-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 2006-10-25 | 2007-04-26 | 2007-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 2010-10-25 | 2011-04-26 | 2011-10-26 | $7700.00 | Window Closed / Lapsed |